Method for synthesizing soluble titanium dioxide nano crystal in low temperature

A titanium dioxide and nanocrystal technology, which is applied in the directions of titanium dioxide, titanium oxide/hydroxide, etc., can solve the problems of difficulty in obtaining titanium dioxide nanocrystals, increased difficulty in separation and purification, and various types of reaction materials, and achieves excellent water solubility and non-volatility. , the composition is simple, the effect of improving the yield

Inactive Publication Date: 2006-11-22
RESEARCH INSTITUTE OF TSINGHUA UNIVERSITY IN SHENZHEN
View PDF15 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] (2) A large amount of resources such as alkali, acid solution and water are consumed, and a large amount of waste water is produced at the same time, which is not conducive to environmental governance
[0007] (3) There are many types of reaction materials, and the product purity is not high
At the same time, it also makes the separation and purification of the product more difficult, and it is difficult to obtain titanium dioxide nanocrystals with higher purity.
[0008] (4) The yield per unit reaction volume is low, and the yield is generally only about 10-25g / l

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for synthesizing soluble titanium dioxide nano crystal in low temperature
  • Method for synthesizing soluble titanium dioxide nano crystal in low temperature
  • Method for synthesizing soluble titanium dioxide nano crystal in low temperature

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The volume ratio of each component is V 含钛盐酸溶液 :V 过氧化氢水溶液 :V 碱液 :V 水=1.0: 0.3: 3.0: 1.7, wherein the titanium-containing hydrochloric acid solution is a mixed hydrochloric acid solution of titanium tetrachloride and titanium trichloride (titanium in the tetravalent state 4+ Ions and trivalent Ti 3+ ion-to-matter ratio n Ti 4 + : n Ti 3 + = 3.9 , The total substance concentration of the titanium element is 3.8mol / l); Hydrogen peroxide is a chemically pure hydrogen peroxide aqueous solution, and the mass percentage concentration is 30.0%; The lye is a sodium hydroxide solution of 2.0mol / l; Water for deionized water. first according to n Ti 4 + ...

Embodiment 2

[0038] The volume ratio of each component is V 含钛盐酸溶液 :V 过氧化氢水溶液 :V 碱液 :V 水 =1.0: 0.1: 2.8: 2.1, wherein the titanium-containing hydrochloric acid solution is a mixed hydrochloric acid solution of titanium tetrachloride and titanium trichloride ( n Ti 4 + : n Ti 3 + = 1.6 The total substance concentration of the titanium element is 2.5mol / l); Hydrogen peroxide is a chemically pure hydrogen peroxide aqueous solution, and the mass percentage concentration is 30.0%; The lye is a sodium hydroxide solution of 2.2mol / l; Water for deionized water. The preparation operation of the precursor is the same as that of Example 1. Transfer it to a reflux device in an open system, hydrolyze and crystallize at 155°C for 4.5 hours, cool, centrifuge, recover t...

Embodiment 3

[0040] The volume ratio of each component is V 含钛盐酸溶液 :V 过氧化氢水溶液 :V 碱液 :V 水 =1.0: 0.2: 3.2: 1.5, wherein the titanium-containing hydrochloric acid solution is a mixed hydrochloric acid solution of titanium tetrachloride and titanium trichloride ( n Ti 4 + : n Ti 3 + = 2.4 , The total substance concentration of titanium element is 3.0mol / l); Hydrogen peroxide is a chemically pure hydrogen peroxide aqueous solution, and the mass percent concentration is 30.0%; The lye is a sodium hydroxide solution of 1.8mol / l; Water for deionized water. The preparation operation of the precursor solution is the same as that in Example 1. Transfer it to a reflux device in an open system, hydrolyze and crystallize at 145°C for 7.0 hours, cool, centrif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention provides a chemical method for synthesizing soluble titanium dioxide nanocrystal at low temperature, characterizing in that: using titanium tetrachloride and titanium trichloride mixed hydrochloric acid solution as titanium source, with hydrogen dioxide and alkaline solution as adjuvant material, applying open system reflux reaction apparatus or closed system low-temperature heat reaction apparatus, leave the reaction for 1-12 h between 100 and 180Deg C. The yield of the titanium dioxide nanocrystal synthesized by this method is 30-70g / l. The obtained titanium dioxide nano particle has an anatase phase structure and a high degree of crystallization. The particle size is homogeneous and the particle diameter is distributed between 3 and 20nm, which is easily dispersed. The titanium dioxide nanocrystal has superior photocatalysis, deodorizing, antibacterial and mildew-resistant properties. This method is characterized of combining hydrolysis, crystallization and dispersion in one step, low reaction temperature, strong apparatus universality, easy-obtained and low cost raw material, and high yield.

Description

【Technical field】 [0001] The invention provides a method for synthesizing titanium dioxide nanocrystals, in particular a method for low-temperature synthesis of titanium dioxide nanocrystals with an anatase phase structure that is easily dispersed, and belongs to the field of nanomaterial preparation. 【Background technique】 [0002] In recent years, with the development of science and technology, it has been found that nanoscale titanium dioxide crystals have excellent photocatalytic properties, that is, they have strong oxidation / reduction properties under ultraviolet (UV) irradiation, and can achieve biorefractory organic pollution. It has the functions of thorough mineralization at room temperature, antibacterial and mildew proof, and ultraviolet shielding. Therefore, the application and synthesis method of titanium dioxide nanocrystals has become a major topic, and scientists from various countries have carried out research from different angles. [0003] At present, mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G23/053
Inventor 杨发达李荣先杨建
Owner RESEARCH INSTITUTE OF TSINGHUA UNIVERSITY IN SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com