Ultra-thick film solvent-free thermal spraying quick-drying heavy-duty anti-corrosive paint and preparation thereof

An anti-corrosion coating, solvent-free technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as unsatisfactory coating efficiency, achieve good film airtightness, improve coating quality, and shorten the coating time. The effect of the installation interval

Inactive Publication Date: 2009-07-15
洛阳双瑞防腐工程技术有限公司
View PDF3 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the single-coat film is only 400 μm, and the surface dry time is 4 hours, so the coating efficiency is also not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-thick film solvent-free thermal spraying quick-drying heavy-duty anti-corrosive paint and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] A: E-51 epoxy resin 23.5

[0080] n-Butyl glycidyl ether 3.0

[0081] Dibutyl phthalate 2.5

[0082] Deqian 6800 defoamer 1.0

[0083] Organic bentonite 1.5

[0084] BYK-220s wetting and dispersing agent 0.5

[0085] Mica iron oxide red 30.0

[0086] Mica powder 10.0

[0087] Talc 10.0

[0088] Homemade Thixotropic Paste 18.0

[0089] Homemade thixotropic paste:

[0090] E-54 epoxy resin 60.0

[0091] n-Butyl glycidyl ether 10.0

[0092] Dibutyl phthalate 15.0

[0093] Fumed silica 15.0

[0094] B: Cardolite NX-2003 30

[0095] Huntsman 3226 15.0

[0096] DMP-30 2.0

[0097] Organic bentonite 3.0

[0098] 600 mesh quartz powder 50.0

[0099] A:B=2.3:1.0

example 2

[0101] A: E-51 epoxy resin 20.0

[0102] E-44 epoxy resin 15.0

[0103] Phenyl glycidyl ether 5.0

[0104] Polysulfide 4.0

[0105] BYK066N defoamer 0.5

[0106] Polyethylene Wax 3.0

[0107] BYK-405 wetting and dispersing additive 1.0

[0108] Mica iron oxide gray 20.0

[0109] Mica powder 10.0

[0110] Asbestos powder 14.5

[0111] Homemade Thixotropic Paste 7.0

[0112] Homemade thixotropic paste:

[0113] E-44 epoxy resin 60.0

[0114] Phenyl glycidyl ether 10.0

[0115] Polysulfide rubber 15.0

[0116] Fumed silica 15.0

[0117] B: Cardolite NX-2003 40.0

[0118] T31 10.0

[0119] DMP-30 2.2

[0120] Organic bentonite 2.0

[0121] 325 mesh gold steel grit 45.8

[0122] A:B=2.5:1.0

example 3

[0124]A: E-44 epoxy resin 20.0

[0125] Allyl Glycidyl Ether 4.0

[0126] Dioctyl phthalate 5.0

[0127] BYK-A530 defoamer 1.5

[0128] Polyethylene Wax 2.0

[0129] AT-203 wetting and dispersing agent 2.0

[0130] Ferrophosphorus powder 25.0

[0131] Mica powder 20.0

[0132] Asbestos powder 10.0

[0133] Homemade thixotropic paste 10.5

[0134] Homemade thixotropic paste:

[0135] E-54 epoxy resin 60.0

[0136] Allyl glycidyl ether 10.0

[0137] Dioctyl phthalate 15.0

[0138] Organic bentonite 15.0

[0139] B: Araldite 830 35.0

[0140] Araldite 850 12.0

[0141] DMP-30 2.5

[0142] Polyethylene wax 2.2

[0143] 325 mesh gold steel grit 48.3

[0144] A:B=2.5:1.0

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of anti-corrosive paint, provides a super thick film solvent-free hot spray fast dried heavy-duty coating and a preparation method thereof. The component A of the heavy-duty coating comprises 20.0-35.0 of epoxide resin, 3.0-5.0 of reactive diluent, 2.0-5.0 of plasticizer, 0.5-1.5 of foam killer, 1.5-3.0 of thixotropic agent, 0.5-2.0 of wetting dispersant, 20.0-30.0 of inhibitive pigment, 20.0-30.0 of cracking prevention stuffing, and 7.0-18.0 of homemade thixotropy slurry; the component B thereof comprises 40.0-55.0 of firming agent I, 2.0-2.5 of curing accelerator, 2.0-3.0 of thixotropic agent, and 40.0-50.0 of wear resistance pigment. The paint film of the heavy-duty coating has good stopping property, excellent performances of adhesive attraction, high hardness, good wearing resistance, fast surface drying, short hardening time and the like. The heavy-duty coating is suitable for being coated in multiple conditions, can be coated in a streamlined way in the special production line, also can be applicable to minor works, small amount coating; the thickness of the first film forming can reach 1000 mum.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion coatings, and in particular relates to an ultra-thick film solvent-free thermal spraying quick-drying heavy-duty anti-corrosion coating and a preparation method thereof. Background technique [0002] At present, there are many epoxy heavy-duty anti-corrosion coatings in the known technology, which are widely used in heavy-duty anti-corrosion fields such as industrial pipelines and ports and wharfs, and have excellent performance. In addition, the industry continues to introduce new ones, and the new technology level develops rapidly. [0003] The Chinese patent application whose patent application number is 200710054013.7 discloses a heavy-duty anti-corrosion coating for marine steel structures. The coating is widely used in heavy anti-corrosion fields such as seaports and wharfs due to its excellent anti-corrosion performance. However, due to its high viscosity, it can only be applied by s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/08B05D7/24
Inventor 刘翰锋张光张东亚
Owner 洛阳双瑞防腐工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap