Laser information coating for gold stamping

A coating and coating technology, applied in the field of laser information coating coatings for hot stamping, can solve the problems of unsatisfactory solvent resistance, difficult production of acrylic, low temperature resistance of the layer, etc., and achieve low cost, high brightness, and materials. The effect of environmental protection

Inactive Publication Date: 2010-05-12
DONGGUAN K LASER TECH
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the thermoplastic acrylic series of laser information coating coatings for bronzing are commonly used in the market. Although the acrylic layer has the advantages of high brightness, good toughness, unbreakable, and strong repairability, the layer has low temperature resistance. The problem of poor solvent resistance has great limitations in the selection of hot stamping substrates and the improvement of hot stamping speed
At the same time, due to the difficulty and high cost of acrylic production, the cost of coating is too high
[0004] Chinese patent application number: 200810029355.8 discloses a laser transfer coating and its preparation method, mainly composed of methyl methacrylate, butyl methacrylate, acrylic acid, vinyl acetate, ethyl acetate, propylene glycol monomethyl ether, n-butyl acetate Ester, benzoyl peroxide and nitrocellulose are heated to prepare a laser transfer coating, but the coating still has the problems of low temperature resistance and poor solvent resistance after coating
[0005] Chinese patent application number: 200510031854.7 discloses an environment-friendly laser transfer composite aluminum foil paper and its preparation process, the coating is made of water-soluble amino resin or water-soluble polyurethane resin or water-soluble alkyd resin or water-soluble acrylic resin or cellulose resin , plus additives, pigments, co-solvents, water, or any combination thereof, the water-based laser transfer coating is prepared by synthesis, wetting and dispersing, but the performance of high temperature resistance and solvent resistance is still not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The first step: first 10 parts of methyl ethyl ketone (100 parts in total of all components, each 100 grams, the same below), 5 parts of n-butanol, 4 parts of xylene and 4.5 parts of ethylene glycol monobutyl ether acetate in sequence Add it into the mixing tank, and stir evenly at a constant temperature of 26°C for 8 minutes;

[0047] Step 2: Pour 50 parts of maleic acid and 25 parts of melamine resin into the mixing tank in sequence according to the formula ratio, and stir continuously for about 10 minutes;

[0048] Step 3: Add 1.5 parts of p-toluenesulfonic acid into the mixing tank, add while stirring, and continue stirring for about 12 minutes after adding, to obtain a liquid coating for laser information coating for bronzing.

[0049] In order to verify the effect of the present invention, the liquid coating of the laser information coating for bronzing prepared by the above method is coated on the PET electroplated aluminum film, and the temperature resistance of...

Embodiment 2

[0051] The first step: first 10 parts of methyl ethyl ketone (100 parts in total of all components, each 100 grams, the same below), 5 parts of n-butanol, 4.8 parts of xylene and 4.05 parts of ethylene glycol monobutyl ether acetate Add it into the mixing tank, and stir evenly at a constant temperature of 28°C for 10 minutes;

[0052] Step 2: Pour 45 parts of maleic acid and 30 parts of melamine resin into the mixing tank in sequence according to the formula ratio, and stir continuously for about 10 minutes;

[0053] Step 3: Add 1.15 parts of p-toluenesulfonic acid into the mixing tank, add while stirring, and continue stirring for about 15 minutes after adding, to obtain a liquid coating for laser information coating for bronzing.

[0054] In order to verify the effect of the present invention, the liquid paint of the laser information coating for bronzing prepared by the above method, after being coated on the PET electroplated aluminum film, can detect that the temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a laser information coating for gold stamping, which comprises the following raw material components in percentage by weight: 40 to 50 percent of maleic acid, 20 to 30 percent of malamine resin, 5 to 15 percent of butanone, 1 to 5 percent of normal butanol, 1 to 5 percent of dimethylbenzene, 1 to 5 percent of ethylene glycol monobutyl ether acetate and 1 to 2 percent of paratoluenesulfonic acid. The laser information coating for gold stamping solves the problems that thermoplastic acryl series general gold stamping laser information coatings generally used on the market at present have lower temperature resistance and poor solvent resistance, and greatly reduces the loss caused by the shortages of temperature resistance and solvent resistance during the use of customers; and the product has the advantages of high brightness, good toughness, difficult breakage, strong repairability, environment-friendly materials, low cost, simple process and the like, and is suitable for large-scale popularization and application.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a laser information coating coating for bronzing. Background technique [0002] In the packaging and printing industry, bronzing laser printing has become a trend in commodity packaging printing, which can bring luxury, noble and exquisite feelings to commodities, so the application of bronzing can be seen on many high-end commodities and printed materials, such as cosmetic packaging , Wine boxes, wine labels, cigarette packs, catalogues, calendars, advanced pens, stationery, etc. [0003] The effect of bronzing laser printing depends to a certain extent on the quality of the laser information coating. At present, the thermoplastic acrylic series of laser information coating coatings for bronzing are commonly used in the market. Although the acrylic layer has the advantages of high brightness, good toughness, unbreakable, and strong repairability, the layer has low temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/28C09D7/12B41M5/382
Inventor 三德·沙达西文吴俊德
Owner DONGGUAN K LASER TECH