Desulfuration adsorbent containing phosphorus and preparation method and application thereof

An adsorbent, content technology, applied in chemical instruments and methods, refined hydrocarbon oil, other chemical processes, etc., can solve the problems of low activity and broken structure of adsorbents

Active Publication Date: 2010-07-07
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the chemical reaction of zinc oxide in the adsorption desulfurization process,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0063] Example 1

[0064] Take 0.80 kg of expanded perlite (World Mining Company, M27, containing 0.79 kg on dry basis, 72wt% of silicon oxide, 19wt% of alumina, and the rest being K 2 O, MgO, Fe 2 O 3 Etc.), 0.71 kg of kaolin (Suzhou Kaolin Factory, S1, containing 0.59 kg of dry basis, alumina content 44wt.%, silica content 50wt.%, the rest is CaO, Fe 2 O 3 , TiO 2 Etc.), 1.15 kilograms of hydrated alumina (pseudo-boehmite, produced by Shandong Aluminum Factory, containing 0.78 kilograms on a dry basis) and 9.0 kilograms of neutral water (pH 6-8), after mixing well under stirring, add 200 grams 30% nitric acid (chemically pure, produced by Beijing Chemical Plant) was stirred and heated to 80°C for aging for 2 hours. When the temperature dropped below 40°C, 115 g of phosphoric acid was added, stirred for 1 hour, then 3.5 kg of zinc oxide (containing 3.43 kg of pure zinc oxide) powder was added, mixed and stirred for 1 hour to obtain a carrier slurry. The carrier slurry adopts Nir...

Example Embodiment

[0067] Example 2

[0068] Add 3.9 kg of zinc oxide powder (produced by Beijing Chemical Plant) into 5.2 kg of deionized water and stir for 30 minutes to obtain a zinc oxide slurry.

[0069] Take 0.78 kg of expanded perlite (World Mining Company, M27, containing 0.77 kg of dry basis), 0.57 kg of kaolin (Suzhou Kaolin Factory, S1, containing 0.48 kg of dry basis), and 1.15 kg of hydrated alumina (pseudo-boehmite, Shandong Produced by the aluminum factory, containing 0.78 kg on dry basis) and 3.8 kg of neutral water (pH 6-8). After mixing uniformly under stirring, add 200 grams of 30% nitric acid (chemically pure, produced by Beijing Chemical Plant) and then heat to After acidification at 80°C for 2 hours, the temperature was lowered, 250 g of ammonium dihydrogen phosphate was added and stirred for 1 hour. Then, pour the above-mentioned zinc oxide slurry and stir for 1 hour to obtain a carrier slurry. The carrier slurry adopts Niro Bowen Nozzle Tower TM The spray dryer of the model...

Example Embodiment

[0071] Example 3

[0072] Take 1.07 kilograms of diatomaceous earth (Beijing Chemical Reagent Factory, containing 0.87 kilograms of dry basis, 86.7% by weight of silicon oxide, 7.5% by weight of alumina, and the rest are CaO, Fe 2 O 3 And other impurities), 0.97 kg of kaolin (Suzhou Kaolin Factory, S1, containing 0.81 kg of dry basis), 1.30 kg of hydrated alumina (produced by Shandong Aluminum Factory, containing 0.88 kg of dry basis) and 9.0 kg of neutral water (pH 6 8) After mixing uniformly under stirring, add 135 grams of 30% hydrochloric acid (chemically pure, produced by Beijing Chemical Plant) for 2 hours, stir and acidify, then add 125 grams of diethyl phosphine, and heat to 80° C. for aging for 2 hours. When the temperature drops below 40°C, 3.1 kg of zinc oxide powder is added and mixed and stirred for 1 hour to obtain a carrier slurry. The carrier slurry adopts Niro Bowen Nozzle Tower TM The spray dryer of the model performs spray drying, the spray drying pressure is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a phosphorus-containing adsorbent for removing sulfur from cracked gasoline and diesel fuel, which has good wear resistant strength and desulfuration activity. On the basis of the total weight of the adsorbent, the desulfuration adsorbent comprises the following components: 1) 5-35wt% of alumina, 2) 3-30wt% of monox, 3)10-80wt% of at least one metal oxide which is selected from IIB, VB and VIB group, 4) 3-30wt% of at least one accelerator metal which is selected from VIIB and VIII group and 5) 0.3-5wt% of phosphorus oxide calculated on the basis of phosphorus.

Description

technical field [0001] The invention relates to an adsorbent composition suitable for desulfurization in cracked gasoline and diesel fuel and a preparation method thereof. Background technique [0002] The sulfur oxides produced by the combustion of sulfur in vehicle fuels will inhibit the activity of noble metal catalysts in vehicle exhaust converters and cause irreversible poisoning. As a result, the vehicle exhaust contains unburned non-methane hydrocarbons, nitrogen oxides and carbon monoxide, and these exhaust gases are easily catalyzed by sunlight to form photochemical smog and cause acid rain. At the same time, sulfur oxides in the atmosphere are also the main cause of acid rain. one. As people pay more and more attention to environmental protection, environmental regulations are becoming stricter, and reducing the sulfur content of gasoline and diesel is considered to be one of the most important measures to improve air quality. [0003] Most of the sulfur in gasol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/10B01J20/30C10G25/06
Inventor 林伟田辉平朱玉霞王振波张万虹李峥
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap