Lost foam casting paint

A technology of lost foam casting and coating, which is applied to casting molding equipment, coatings, casting molds, etc. It can solve the problems of casting cavity collapse, low high temperature strength, and shape deformation, etc., and achieve high room temperature strength and high temperature strength, high temperature breathability The effect of good performance and comprehensive performance improvement

Active Publication Date: 2012-04-11
ZHANGJIAGANG JIANGNAN POWDER COATING
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the lost foam casting process has developed rapidly since its inception, the coating technology has been plagued by the fact that it is difficult to greatly improve the casting yield. The main reason is that the quality of the coating cannot meet the requirements of the lost foam casting process.
One is that the strength at room temperature does not meet the requirements, and the shape is deformed and the coating is damaged during molding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example one

[0017] A lost foam casting coating, the coating is composed of the following components in parts by weight: 20 parts of zircon powder, 20 parts of kaolin, 10 parts of corundum powder, 3 parts of polyvinyl acetate emulsion, 1 part of aluminum sulfate, 1 part of attapulgite Parts, 0.2 parts of disodium hydrogen phosphate, 7 parts of sodium bentonite, 0.4 parts of sodium benzoate, 0.5 parts of iron oxide, 0.05 parts of n-octanol, 1.2 parts of carboxymethyl cellulose, 0.05 parts of ethyl acetate, nonylphenol polyoxygen 0.06 parts of vinyl ether and 15 parts of water, wherein the particle size of the zircon powder and high territories is 180-320 mesh, and the particle size of the corundum powder is 250-350 mesh.

Example Embodiment

[0018] Example two

[0019] A lost foam casting coating, the coating is composed of the following components in parts by weight: 30 parts of zircon powder, 15 parts of kaolin, 15 parts of corundum powder, 2 parts of polyvinyl acetate emulsion, 2 parts of aluminum sulfate, and 0.5 parts of attapulgite Parts, 0.3 part of disodium hydrogen phosphate, 5 parts of sodium bentonite, 0.6 part of sodium benzoate, 0.3 part of iron oxide, 0.1 part of n-octanol, 0.6 part of carboxymethyl cellulose, 0.08 part of ethyl acetate, nonylphenol polyoxygen 0.04 parts of vinyl ether and 25 parts of water, wherein the particle size of the zircon powder and high territories is 180-320 mesh, and the particle size of the corundum powder is 250-350 mesh.

Example Embodiment

[0020] Example three

[0021] A lost foam casting coating, the coating is composed of the following components in parts by weight: 22 parts of zircon powder, 18 parts of kaolin, 12 parts of corundum powder, 2.2 parts of polyvinyl acetate emulsion, 1.2 parts of aluminum sulfate, and 0.8 parts of attapulgite Parts, 0.22 parts of disodium hydrogen phosphate, 6.5 parts of sodium bentonite, 0.45 parts of sodium benzoate, 0.45 parts of iron oxide, 0.06 parts of n-octanol, 1.0 part of carboxymethyl cellulose, 0.06 parts of ethyl acetate, nonylphenol polyoxygen 0.055 parts of vinyl ether and 18 parts of water, wherein the particle size of the zircon powder and high territory is 180-320 mesh, and the particle size of the corundum powder is 250-350 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a lost foam casting paint. The paint comprises the following components in parts by weight: 20-30 parts of zircon powder, 15-20 parts of kaolin, 10-15 parts of alundum powder, 2-3 parts of polyvinyl acetate emulsion, 1-2 parts of aluminum sulfate, 0.5-1 part of attapulgite, 0.2-0.3 part of disodium hydrogen phosphate, 5-7 parts of sodium bentonite, 0.4-0.6 part of sodium benzoate, 0.3-0.5 part of ferric oxide, 0.05-0.1 part of n-octanol, 0.6-1.2 parts of carboxymethyl cellulose, 0.05-0.08 part of ethyl acetate, 0.04-0.06 part of nonylphenol polyoxyethylene ether and 15-25 parts of water, wherein the particle sizes of zircon powder and kaolin are both 180-320 meshes and the particle size of alundum powder is 250-350 meshes.

Description

technical field [0001] The invention relates to the field of casting, in particular to the technical field of lost foam casting. Background technique [0002] Lost foam casting is to combine the plastic foam model with the same size and shape as the casting and the riser system made of the same material to form a model cluster, brush the lost foam paint and dry it, and bury it in the dry sand of the special sand box Vibrating and compacting the molding, using vacuum equipment to connect a special sand box to evacuate, pouring high-temperature metal liquid under the condition of maintaining a certain negative pressure in the mold to melt and gasify the mold, and the decomposition products escape through the coating / mould interface, and the liquid state A casting method in which metal occupies the position of the model, solidifies and cools to form a casting. Lost foam casting has outstanding advantages such as high dimensional accuracy of castings, less pollution, and low co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C3/02B22C9/04
Inventor 朱小英
Owner ZHANGJIAGANG JIANGNAN POWDER COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap