Preparation method of nano-grade calcium carbonate
A nano-calcium carbonate, slurry technology, applied in the direction of calcium carbonate/strontium/barium, nanotechnology, etc., can solve the problems of poor dispersibility, poor reinforcement, insufficient gloss, etc., and achieve high reinforcement and high dispersion. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example one
[0023] The lime calcined in the lime kiln is digested with hot water at 40°C, and the weight ratio of water to lime is 10:1. After sieving, the slurry is aged for 12 hours. During the aging process, a crystal form control agent and crystal form are added. The type of control agent is EDTA, and the addition amount is 0.4% of the solid content of lime. The aged lime slurry to 15m 3 The high-speed shearing special carbonization kettle is used for carbonization, the carbonization temperature is controlled at 30℃, the stirring speed is 110r / min, and the carbonized slurry is added with a dispersant. The dispersant is sodium hydrogen phosphate and acrylic acid-2-acrylamide-2 -Methylpropanesulfonic acid copolymer, the addition amount of the two dispersants is 0.2% of the calcium carbonate dry basis, first add sodium hydrogen phosphate, stir for 5min, then add acrylic acid-2-acrylamide-2-methylpropanesulfonic acid The copolymer is stirred for another 10 minutes and t...
Example Embodiment
[0025] Example two
[0026] The lime calcined in the lime kiln is digested with hot water at 50°C, and the weight ratio of water to lime is 8:1. Then the slurry is sieved and aged for 16 hours. A crystal form control agent is added during the aging process to control the crystal form. The type of agent is EDTA-Na 2 , The addition amount is 0.8% of the solid content of lime. The aged lime slurry to 15m 3 The high-speed shearing special carbonization kettle is used for carbonization. The carbonization temperature is controlled at 26°C and the stirring speed is 120r / min. Add dispersant to the carbonized slurry. The dispersant is potassium hydrogen phosphate and acrylic acid-hydroxypropyl acrylate copolymer. , The addition amount of the two dispersants is 0.4% on the dry basis of calcium carbonate, first add potassium hydrogen phosphate, stir for 10 minutes, add acrylic acid-2-acrylamide-2-methylpropanesulfonic acid copolymer, and stir for 15 minutes. Sieve, to the coating kettle, t...
Example Embodiment
[0028] Example three
[0029] The lime calcined in the lime kiln is digested with hot water at 70°C, and the weight ratio of water to lime is 6:1. Then the slurry is sieved and aged for 18 hours. A crystal form control agent is added during the aging process to control the crystal form. The type of agent is soft white sugar, and the addition amount is 0.6% of the solid content of lime. The aged lime slurry to 15m 3 The high-speed shearing special carbonization kettle is used for carbonization. The carbonization temperature is controlled at 24°C and the stirring speed is 130r / min. Add dispersant to the carbonized slurry. The dispersant is sodium pyrophosphate and maleic acid-acrylic acid copolymer. The addition amount of the two dispersants is 0.6% of the calcium carbonate dry basis. First add sodium pyrophosphate, stir for 10 minutes, then add the maleic acid-acrylic acid copolymer, stir for 15 minutes, then sieving, to the coating kettle, coating agent Ceric acid C 22 H 44 O 2 ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap