A composite material and high-elasticity technology, applied in the field of composite materials, can solve the problems of poor flexibility and rebound performance, poor softness and elasticity, and unsatisfactory wear resistance, so as to improve the rebound performance and flexibility , Improve compatibility and bonding, improve strength and wear resistance

Inactive Publication Date: 2012-07-04
JINJIANG CHENGCHANG SHOES
View PDF2 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) is light in weight and easy to shape, but the softness and elasticity of the material are not good, and even if the softness partia

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0019] A kind of highly elastic and wear-resistant rubber-plastic composite material adopts 20kg of talcum powder,

[0020] The coupling agent adopts 0.1kg of silane coupling agent, the metal oxide adopts 0.6kg of ZnO as foaming aid and active agent, and the lubricant adopts 0.2kg of stearic acid and 0.3kg of zinc stearate; foaming agent 4kg of AC azo foaming agent is used; 1kg of dicumyl peroxide is used as a bridging agent; the raw material of rubber particles is 100kg, and the ratio of raw materials of rubber particles is: 90kg of EVA (ethylene vinyl acetate), 5kg of POE (polyolefin elastomer), 4kg of EPDM rubber, 1kg of oil-extended (mineral oil) styrene-ethylene / butylene-styrene copolymer.

[0021] The production process of a high elastic wear-resistant rubber-plastic composite material is as follows: First, 90kg of EVA (ethylene vinyl acetate), 5kg of POE (polyolefin elastomer), 4kg of EPDM rubber, 1 kg of oil-extended (mineral oil) styrene-ethylene / butylene-styrene cop...

specific Embodiment 2

[0023] A kind of high elastic wear-resistant rubber-plastic composite material, adopts 2kg calcium carbonate as filler, coupling agent adopts 7kg titanate coupling agent, metal oxide adopts 2kg ZnO as foaming aid and activator, lubricating agent Agent adopts the stearic acid of 1kg and the zinc stearate of 1kg, foaming agent adopts the AC azo foaming agent of 0.5kg, bridging agent adopts the colloidal raw material of 0.4kg dicumyl peroxide, 100kg, its The ratio is: 60kg of EVA (ethylene vinyl acetate), 20kg of POE (polyolefin elastomer), 15kg of EPDM rubber, 5kg of oil-extended (mineral oil) styrene-ethylene / butylene-benzene Ethylene copolymer.

[0024] The production process of a high elastic wear-resistant rubber-plastic composite material is as follows: First, 60kg of EVA (ethylene vinyl acetate), 20kg of POE (polyolefin elastomer), 15kg of EPDM 5kg of oil-extended (mineral oil) styrene-ethylene / butylene-styrene copolymer with 2kg of talc, 2kg of ZnO, 1kg of stearic acid a...

specific Embodiment 3

[0026] A kind of high elasticity wear-resistant rubber-plastic composite material, adopts 15kg of talcum powder or calcium carbonate as the filler, 3kg of silane coupling agent or titanate coupling agent as the coupling agent, and 1kg of ZnO as the metal oxide. 0.7kg of stearic acid and 0.8kg of zinc stearate are used as foam aids and active agents, lubricants are used, 2kg of AC azo foaming agents are used as foaming agents, and 0.6kg of diisoperoxide is used as bridging agent Propylbenzene, 100kg of rubber particle raw materials, the ratio of rubber particle raw materials is: 50kg of EVA (ethylene vinyl acetate), 20kg of POE (polyolefin elastomer), 23kg of EPDM rubber, 7kg of oil-extended (mineral oil) styrene-ethylene / butylene-styrene copolymer.

[0027] The production process of a high elastic and wear-resistant rubber-plastic composite material is as follows: first, 50kg of EVA (ethylene vinyl acetate), 20kg of POE (polyolefin elastomer), 23kg of EPDM rubber, 7 kg of oil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite material, in particular to a rubber plastic composite material for shoes, sports goods and leather components. The composite material is prepared by mixing rubber particle raw material, a filler, a coupling agent, metal oxide, a lubricant, a foaming agent and a cross linking agent with a certain proportion. The rubber particle raw material is obtained by mixing EVA (ethylene vinyl acetate), POE (polyolefin elastomer), modified ethylene propylene diene monomer, and oil-extended (mineral oil) styrene-ethylene/butylene-styrene copolymer. By introducing the modified ethylene propylene diene monomer and oil-extended (mineral oil) styrene-ethylene/butylene-styrene copolymer to the formula, the resilience and toughness of the composite material are greatly improved, at the same time, by introducing the coupling agent to the formula, the compatibility and consistency of components in the composite material are improved, and the strength and wear resistance of the composite material are increased.

Description

technical field [0001] The invention relates to a composite material, especially a composite material specially used for shoe materials, sporting goods, leather and other components. Background technique [0002] Most of the existing EVA adopts the production method of POE modified materials. The modified materials are suitable for injection molding and compression molding. They can be widely used in shoe outsoles, sporting goods and other light industrial products. The ingredients are composed of 50-95% EVA, 5 -40% POE (polyolefin elastomer), 5-20% talcum powder or CaCO3, metal oxide 1-2%, lubricant 0.1-1%, peroxide (bridging agent) 0.4-1%, even Nitrogen foaming agent 1-4% and appropriate amount of pigment are mixed by internal mixer, auxiliary mixing by open mixer, pelletizing, injection molding or compression molding. The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) is light in weight and easy to shape, but the softness and elasticity of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L23/16C08L53/02C08K13/02C08K3/34C08K3/26C08K3/22C08J9/10
Inventor 庄辉煌李灿升
Owner JINJIANG CHENGCHANG SHOES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap