Method for extracting rhenium from rhenium-rich concentrates
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of concentrated ore and oxygen-enriched air, which is applied in the direction of improving process efficiency, can solve the problems of unreported treatment, easy crystallization of calcium ions, unfavorable separation and purification, etc., to achieve industrial application, high recovery rate of rhenium, and good effect thorough effect
Active Publication Date: 2012-08-08
YANGGU XIANGGUANG COPPER
View PDF3 Cites 21 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The quicklime roasting + water leaching process adopts the method of mixing roasting molybdenum concentrate roasting soot and calcium oxide under air conditions to generate calcium molybdate (insoluble matter) and calcium rhenate (easily soluble matter), and water leaching to separate molybdenum and rhenium. The concentration of c
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0055] Example 1:
[0056] (1) Oxygen-enriched roasting
[0057] Take 1 kg of rhenium-rich concentrate, the main components of the rhenium-rich concentrate: Re 3.5%, As 8%, Cu 13%, S 65%. The rhenium-rich concentrate and quicklime are mixed and ground to 100 mesh. The added amount of quicklime is 0.5 times the mass of the concentrate, that is, 0.5 kg. The mixture is added to the electric furnace, oxygen-enriched air is passed, the gas oxygen content volume ratio is 50%, the pressure is 0.3Mpa, and the gas consumption is 0.7Nm 3 , Calcination temperature 550℃, calcination time 6h.
[0058] (2) Water leaching
[0059] The roasted material is directly added to the reaction vessel, and leached with water slurry, the liquid-solid ratio is 5, the leaching temperature is 60°C, and the leaching time is 5h. After the leaching is completed, filter, solid-liquid separation, the solid residue with higher arsenic content is combined with the copper-arsenic filter cake for unified treatment. The...
Example Embodiment
[0064] Example 2:
[0065] (1) Oxygen-enriched roasting
[0066] Take 1 kg of rich rhenium concentrate, the main components of rich rhenium concentrate: Re5.4%, As 10%, Cu 15%, S 59.7%. Mix and grind the rich rhenium concentrate with quicklime to 100 meshes. The added amount of quicklime is twice the mass of the concentrate, that is, 1 kg. The mixture is added to the electric furnace, oxygen-enriched air is passed, the gas oxygen content volume ratio is 70%, the pressure is 0.4Mpa, and the gas consumption is 0.6Nm 3 , Calcination temperature 700℃, calcination time 4h.
[0067] (2) Water leaching
[0068] The roasted materials are directly added to the reaction vessel, and leached with water slurry, the liquid-to-solid ratio is 5, the leaching temperature is 80°C, and the leaching time is 3h. After the leaching is completed, filter, solid-liquid separation, the solid residue with higher arsenic content is combined with the copper-arsenic filter cake for unified treatment. The main c...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a method for extracting rhenium from rhenium-rich concentrates. The method comprises the following steps of: mixing the rhenium-rich concentrates with quick lime, grinding a mixture, feeding oxygen-enriched air into the mixture, and roasting the mixture at a temperature of 400-900 DEG C; sizing and immersing the roasted mixture by using water, and filtering after the immersion is finished; adding an impurity removing agent into the filtered liquid so as to remove calcium and trace heavy metal ions; filtering after removing impurities; and carrying out ion exchange process on the filtered liquid, which is subjected to impurity removal and filtering, through anion exchange resin, obtaining ammonium rhenate solution after desorption, and obtaining ammonium perrhenate through reconcentration and crystallization. According to the method provided by the invention, quick lime oxygen-enriched roasting and water immersion are used, so that the operations of decoppering, arsenic removal and desulfuration are carried out, therefore rhenium, arsenic and sulfur are oxidized sufficiently under the oxygen enrichment condition; the rhenium, arsenic and sulfur are combined with calcium oxide, so that insoluble substances are generated; the effects of removing copper, arsenic and sulfur are more thorough in the water immersion condition, and the disadvantage that the calcium content is high in the quick lime roasting and water immersion technology is solved through using the impurity removing agent to remove impurities; and the recovery rate of rhenium is high, so that the method provided by the invention is favorable to industrialized application.
Description
technical field [0001] The invention relates to the field of metal extraction, in particular to a method for extracting rhenium from rhenium-rich concentrate. Background technique [0002] Rhenium and rhenium alloys are mainly used in petrochemical, national defense and aerospace, electronics, metallurgy and other fields due to their excellent characteristics. As a rare element, rhenium is mainly associated with molybdenite, and a small amount is associated with copper ore. At present, the rhenium-containing solid materials at home and abroad are mainly derived from molybdenum concentrate roasting soot. The main form of rhenium in roasting soot of molybdenum concentrate is ReO 2 、ReO 3 、Re 2 S, ReS 2 . [0003] For molybdenum concentrate roasting soot treatment methods are divided into two modes: full wet treatment and pyro-wet combined treatment. Among them, there are two types of full wet treatment, one is oxygen pressure leaching, and the other is oxidant leaching....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more