Organic silicon-acrylic ester copolymer emulsion and preparation and application thereof

A technology of acrylate and butyl acrylate, which is applied in the field of polymers, can solve the problems of insufficient paint adhesion, weather resistance, water resistance and stain resistance, poor stain resistance, water resistance and adhesion, and achieve simple construction methods Ease of operation, improved anti-sticking performance, and the effect of overcoming high energy consumption

Inactive Publication Date: 2012-08-22
NORTHWEST NORMAL UNIVERSITY
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since there are few reports on the preparation of humidity-conditioning paints with silicone acrylate emulsions, and in the reported moisture-conditioning paints, most of the emulsions are pure acrylic and styrene-acrylic emulsions, although the humidity-conditioning paints prepared with these emulsions Better wet performance, but poor stain resistance, water resistance and adhesion
[0006] Chinese patents CN200810187001.6, CN200810017742.X,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic silicon-acrylic ester copolymer emulsion and preparation and application thereof
  • Organic silicon-acrylic ester copolymer emulsion and preparation and application thereof
  • Organic silicon-acrylic ester copolymer emulsion and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0052] Example 1

[0053] (1) Preparation of silicone-acrylate copolymer emulsion

[0054] Raw material ratio: in parts by weight

[0055] Silicone 1 part 3-glycidylpropyltrimethoxysilane, 1 part methyl methacrylate, 1 part butyl acrylate, 1 part methacrylic acid, 1 part β-hydroxypropyl methacrylate, hydrogen carbonate 1 part of sodium, 1 part of potassium persulfate, 1 part of complex emulsifier (0.5 part of non-ionic emulsifier Tween-20, 0.5 part of ionic emulsifier sodium lauryl sulfate), 1 part of deionized water.

[0056] Process: add deionized water, compound emulsifier and 0.2 parts of silicone, 0.2 parts of methyl methacrylate, 0.2 parts of butyl acrylate, 0.2 parts of methacrylic acid and 0.2 parts of methacrylic acid-β-hydroxypropyl ester were pre-emulsified with stirring at 20°C for 100min; the temperature was raised to 60°C, then the remaining mixed monomers and potassium persulfate were added dropwise to the flask, stirred Under the polymerization reaction fo...

Example Embodiment

[0063] Example 2

[0064] (1) Silicone-acrylate copolymer emulsion is prepared from the following raw materials and processes:

[0065] Raw material ratio: in parts by weight

[0066] Silicone 10 parts methacrylate propyl trimethoxysilane, 20 parts methyl methacrylate, 30 parts butyl acrylate, 10 parts acrylic acid, 20 parts β-hydroxypropyl methacrylate, 5 parts sodium bicarbonate , 5 parts of ammonium persulfate, 5 parts of compound emulsifier (1 part of non-ionic emulsifier Tween-20, 4 parts of ionic sodium lauryl sulfate), 30 parts of deionized water.

[0067] Process: Add deionized water, compound emulsifier, 0.5 parts of silicone, 1 part of methyl methacrylate, 1.5 parts of butyl acrylate to a four-necked flask equipped with an electric stirrer, a thermometer, a condenser and a dropping funnel , 0.5 part of acrylic acid, 1 part of methacrylic acid-β-hydroxypropyl ester, stirred and pre-emulsified at 70 ° C for 20 min; heated to 85 ° C, then the remaining mixed monomer...

Example Embodiment

[0074] Example 3

[0075] (1) Silicone-acrylate copolymer emulsion is prepared from the following raw materials and processes:

[0076] Raw material ratio: in parts by weight

[0077] 30 parts of silicone aminopropyl triethoxysilane, 50 parts of methyl methacrylate, 20 parts of butyl acrylate, 30 parts of fumaric acid, 20 parts of β-hydroxypropyl methacrylate, 8 parts of sodium bicarbonate , 8 parts of potassium persulfate, 8 parts of compound emulsifier (1 part of non-ionic emulsifier Tween-20, 7 parts of ionic sodium lauryl sulfate), 40 parts of deionized water.

[0078] Process: Add deionized water, compound emulsifier, 3 parts of silicone, 5 parts of methyl methacrylate, 2 parts of butyl acrylate to a four-necked flask equipped with an electric stirrer, a thermometer, a condenser and a dropping funnel , 3 parts of fumaric acid, 2 parts of β-hydroxypropyl methacrylate, stirred and pre-emulsified at 60°C for 40min; heated to 80°C, then the remaining mixed monomers and po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides organic silicon-acrylic ester copolymer emulsion, which utilizes organic silicon, methyl methacrylate, butyl acrylate, unsaturated alkyl acid and methacrylic acid-beta-hydroxypropyl ester as comonomers, utilizes deionized water as solvent, utilizes potassium peroxydisulfate or ammonium persulfate as an initiator and utilizes sodium bicarbonate as a neutralizer, and is prepared by polymerization in the presence of an emulsifying agent. The emulsion introduces the organic silicon into polyacrylate, the rigidness of a copolymer is improved to a certain extent, and cohesion of the copolymer emulsion is improved due to the introduction of a polar group. Interior wall humidity-conditioning paint prepared by the copolymer emulsion serving as a film former integrates multiple functions of decoration, humidity conditioning performance, permeability, insulation and anti-condensation performance, water resistance, alkali resistance, alkali-resistant performance and antibiosis, the paint film is durable and long in service life, and the organic silicon-acrylic ester copolymer emulsion serving as the interior wall humidity-conditioning paint has application prospects.

Description

technical field [0001] The invention belongs to the technical field of macromolecules, and relates to a silicone-acrylate copolymer emulsion and its preparation; the invention also relates to the use of the silicone-acrylate copolymer emulsion as a film-forming material in the preparation of indoor humidity-conditioning coatings application. Background technique [0002] Air humidity is an important environmental parameter closely related to human health and work and life. If it is too high or too low, it will affect people's normal life. "Heating Ventilation and Air Conditioning Design Specifications" GB50019-2003 stipulates that the standard value of indoor relative humidity is 40% to 60% for air-conditioned rooms in summer and 30% to 60% for heated rooms in winter, taking into account microbial growth, human disease, and item deterioration As well as various factors such as comfort, it is recognized that the best relative humidity range is 40% to 60%. Controlling indoor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/18C08F220/14C08F220/28C08F230/08C08F220/06C08F2/30C08F2/26C09D133/08C09D133/12C09D133/02C09D133/14C09D143/04
Inventor 王荣民王晓雯何玉凤王俊峰贺睦
Owner NORTHWEST NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products