Plastic wood profile with abrasion resistance, scratch resistance, fouling resistance and weather resistance and preparation method thereof
A profile and wood-plastic technology, applied in the material field of plastic-wood profiles, can solve the problems of wear, pollution and aging, metal sheet or metal foil falling off, high cost of plastic-wood profiles, and achieve high pollution resistance and long service life , high weather resistance effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] Such as figure 1 As shown, the plastic wood profile in this embodiment is a chamfered rectangle, including a core material 1, and the upper, lower, left, and right walls of the core material 1 are coated with wear-resistant, scratch-resistant, anti-fouling and high-weather resistance in a co-extruded manner. protective layer 2.
[0039] The material of the protective layer consists of the following components by weight percentage:
[0040] 10% HDPE (low pressure polyethylene),
[0041] 50% PP (polypropylene),
[0042] 10% EAA (ethylene-acrylic acid copolymer),
[0043] 10% nano ZnO,
[0044] 16.7% talcum powder,
[0045] 0.5% antioxidant 1010,
[0046] 0.5% anti-ultraviolet agent - 2,2,6,6-tetramethyl-4-piperidinol stearate.
[0047] 1.3% toner - iron oxide yellow,
[0048] 1.0% zinc borate.
[0049] The preparation method of the plastic wood profile of this embodiment is:
[0050] (1) Prepare the covering fabric and the core material separately:
[0051] The...
Embodiment 2
[0058] The structure of the wood-plastic profiles in this embodiment is the same as in Embodiment 1.
[0059]The material of the protective layer of this embodiment consists of the following components by weight percentage:
[0060] 40% HDPE (low pressure polyethylene),
[0061] 10% PP (polypropylene),
[0062] 20% EAA (ethylene-acrylic acid copolymer),
[0063] 20% nano ZnO,
[0064] 8.3% filler calcium carbonate,
[0065] 0.3% mixture of Antioxidant 1010 and Antioxidant 168,
[0066] 0.3% anti-UV agent 2-(2'-hydroxy-5'-methylphenyl)benzotriazole,
[0067] 0.5% carbon black,
[0068] 0.6% antifungal agent chlorothalonil.
[0069] The preparation method of the plastic wood profile of this embodiment is:
[0070] (1) Prepare the covering fabric and the core material separately:
[0071] The preparation method of the covering fabric as the protective layer is: after surface activation treatment of nano-zinc oxide powder and inorganic powder filler, mixed with low-pressu...
Embodiment 3
[0078] The structure of the wood-plastic profiles in this embodiment is the same as that in Embodiment 1.
[0079] The material of the protective layer of this embodiment consists of the following components by weight percentage:
[0080] 20% HDPE (low pressure polyethylene),
[0081] 20% PP (polypropylene),
[0082] 40% EAA (ethylene-acrylic acid copolymer),
[0083] 2% nano ZnO,
[0084] 16.7% filler kaolin,
[0085] 0.2% antioxidant 1010,
[0086] 0.2% anti-ultraviolet agent UV531,
[0087] 0.4% iron oxide yellow,
[0088] 0.5% folpet.
[0089] The preparation method of this example is the same as that of Example 1, and will not be repeated here.
[0090] The wood-plastic profiles prepared in this embodiment have been tested and have the following excellent properties:
[0091] Binding force: ASTM D7032 freeze-thaw test 40 cycles without peeling, peeling. Wear-resistant: ASTM D4060 standard test 1000 rpm wear-resistant 30mg; aging resistance: SO4892-2: 2006 standa...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com