Micro-emulsified cutting fluid production additive package and preparation method and application thereof

A technology of additive package and cutting fluid, which is applied in the petroleum industry, lubricating compositions, etc., can solve the problems of microemulsion cutting fluid transparency decrease, affect the operation flexibility, and the defoaming effect is not durable, so as to reduce the risk of technology loss, Reduce the risk of loss of confidentiality, the effect of more foaming

Active Publication Date: 2012-12-05
JINAN COOLANT TECH CO LTD
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such as: reduce the transparency of the microemulsion cutting fluid or cause turbidity, reduce storage stability; condense into a viscous substance in the dilu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Micro-emulsified cutting fluid production additive package and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] An additive package (Type A) for producing microemulsified cutting fluid, the weight ratio of which is composed of: 19 parts of higher fatty acid, 28 parts of alcohol amine, 11 parts of sodium petroleum sulfonate, 7 parts of sorbitan monooleate, 5 parts of fatty alcohol polyoxyethylene ether, 10 parts of coconut oil diethanolamide, 10 parts of butyl carbitol, 4 parts of polyether, 0.2 part of benzotriazole, 2 parts of antiseptic and fungicide, 3.8 parts of water. Vegetable oleic acid or tall oleic acid or a half-and-half mixture is used for higher fatty acids; monoethanolamine and triethanolamine are used for alcohol amines, and the weight percentage of the two is: monoethanolamine 40%, triethanolamine 60%.

[0044] The obtained additive package is a uniform and transparent liquid, which does not become turbid or stratified after standing at 70°C for 4 hours, and freezes at -12°C for 4 hours and returns to room temperature without crystallization or precipitation, and ca...

Embodiment 2

[0048] An additive package (Type A) for producing microemulsified cutting fluid, the weight ratio of which is composed of: 15 parts of higher fatty acid, 25 parts of alcohol amine, 10 parts of sodium petroleum sulfonate, 11 parts of sorbitan monooleate, 8 parts of fatty alcohol polyoxyethylene ether, 8 parts of coconut oil diethanolamide, 8 parts of butyl carbitol, 3 parts of polyether, 0.4 part of benzotriazole, 3 parts of antiseptic and bactericide, and 8.6 parts of water. Vegetable oleic acid or tall oleic acid or a half-and-half mixture is used for higher fatty acids; monoethanolamine and triethanolamine are used for alcohol amines, and the weight percentage of the two is: monoethanolamine 40%, triethanolamine 60%.

[0049] The obtained additive package is a uniform and transparent liquid, which does not become turbid or stratified after standing at 70°C for 4 hours, and freezes at -12°C for 4 hours and returns to room temperature without crystallization or precipitation, a...

Embodiment 3

[0053] A (Type B) additive package for producing microemulsified cutting fluid, the weight ratio of which is composed of: 19 parts of higher fatty acid, 28 parts of alcohol amine, 11 parts of sodium petroleum sulfonate, 7 parts of sorbitan monooleate, 5 parts of fatty alcohol polyoxyethylene ether, 10 parts of coconut oil diethanolamide, 10 parts of butyl carbitol, 4 parts of polyether, 0.2 part of benzotriazole, 2 parts of antiseptic and fungicide, 3.8 parts of water. Higher fatty acid uses ricinoleic acid or coconut oleic acid or the mixture of both; Alcohol amine uses monoethanolamine and triethanolamine, the weight percentage of both is: monoethanolamine 40%, triethanolamine 60%.

[0054] The obtained additive package is a uniform and transparent liquid, which does not become turbid or stratified after standing at 70°C for 4 hours, and freezes at -12°C for 4 hours and returns to room temperature without crystallization or precipitation, and can return to its original shape....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a micro-emulsified cutting fluid production additive package and a preparation method and the application thereof. The additive package is composed of, by weight, 5-25 parts of higher fatty acid, 10-35 parts of alkylol amine, 3-15 parts of sodium alkane sulfonate, 5-20 parts of sorbitan monooleate, 2-15 parts of fatty alcohol-polyoxyethylene ether, 3-15 parts of coconutt diethanol amide, 3-15 parts of butyl carbitol, 1-5 parts of polyether, 0.1-0.6 part of benzotriazole, 1-5 parts of antiseptic bactericide and 3-10 parts of water. The additive package is high in emulsifying ability, high in emulsifying efficiency, and fine in hard water resistance and bubble inhibition performance in preparation of cutting fluid, and micro-emulsified cutting fluid is high in water solubility and free of coagulation, caking and precipitation.

Description

technical field [0001] The present invention relates to an additive composition for producing microemulsion cutting fluid (hereinafter referred to as additive package, Additive package) and its preparation method and application. Background technique [0002] Microemulsion cutting fluid is mainly used in metal processing as a process medium. In the national standard GB / T 7631.5-1989 "Classification of Lubricants and Related Products (Class L) Part 5: Group M (Metal Processing)", the two symbols MAE and MAF correspond to microemulsion cutting fluids. The description of the product type and (or) end-use requirements in this standard is: MAE is a concentrate mixed with water, which has antirust translucent emulsion (microemulsion), and MAF has antifriction and (or) extremely Compressive MAE type concentrate; general application is metal processing; special purpose is for metal removal processes such as cutting, abrasive processing, for stamping, deep drawing, calendering, powe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/00C10N30/12C10N40/22C10N40/20C10N30/04
Inventor 刘镇昌刘煜
Owner JINAN COOLANT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap