Macromolecular flame-retardant elastomer environment-friendly material and preparation method thereof
A technology of environmentally friendly materials and elastomers, applied in the field of polymer materials, can solve the problems of low flame retardant efficiency of metal hydroxide materials, failure to meet softness requirements, and difficulties in market promotion and use, and achieve high elongation and excellent High processability and high tensile strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0032] Example one:
[0033] According to the mass parts ratio, weigh 40 parts of styrene-ethylene-styrene copolymer (SEBS), 10 parts of polypropylene (PP), 5 parts of polyethylene octene co-elastomer (POE), 5 parts of silicone, double 15 parts of pentaerythritol phosphate melamine salt, 3 parts of zinc borate, 40 parts of white oil, 0.1 part of antioxidant, 0.1 part of coloring agent. The above weighed raw materials are uniformly mixed in a high-speed mixer at 1150rpm / min for 8 minutes, and then 5 parts of ethylene-vinyl acetate copolymer grafted maleic anhydride (EVA-g-MAH) are added, and then mixed 2 minutes, then extrude on a twin screw extruder, pelletize, and cool. The extrusion processing temperature is between 180℃ and 220℃, and the temperature of the die and die is 220℃.
[0034] The invention adds white oil to improve the hardness of the material, and uses polypropylene material to adjust the tensile strength and scratch resistance. At the same time, to improve the shea...
Example Embodiment
[0035] Embodiment two:
[0036] According to the mass parts ratio, weigh 35 parts of styrene-butadiene-styrene block copolymer (SBS), 5 parts of polypropylene (PP), and 10 parts of polyethylene octene co-elastomer (POE). 15 parts of ammonium phosphate, 10 parts of melamine, 5 parts of silicone, 5 parts of zinc borate, 30 parts of white oil, 0.1 part of antioxidant, 0.1 part of coloring agent. The weighed raw materials are uniformly mixed in a high-speed mixing mixer for 10 minutes, and then 5 parts of styrene-ethylene-butadiene-styrene copolymer grafted maleic anhydride (SEBS-g-MAH) are added, and then mixed for 2 Minutes, then extrude on a twin screw extruder, pelletize, and cool. The extrusion processing temperature is between 180℃ and 220℃, and the temperature of the die and die is 220℃.
[0037] The invention adds white oil to improve the hardness of the material, and uses polypropylene material to adjust the tensile strength and scratch resistance. At the same time, to impro...
Example Embodiment
[0038] Embodiment three:
[0039] According to the mass parts ratio, weigh 40 parts of styrene-ethylene-styrene copolymer (SEBS), 10 parts of styrene-butadiene-styrene block copolymer (SBS), and 5 parts of polypropylene (PP). Polyethylene octene co-elastomer (POE) 10 parts, ammonium polyphosphate 15 parts, melamine 10 parts, silicone 5 parts, silicon dioxide 2 parts, white oil 50 parts, antioxidant 0.1 part, coloring agent 0.1 part , The weighed raw materials are uniformly mixed in a high-speed mixing mixer for 10 minutes, then 7.5 parts of ethylene-vinyl acetate copolymer grafted methyl methacrylate (EVA-g-MMA) are added, and then mixed for 2 minutes, then Extrude on a twin screw extruder, pelletize, and cool. The extrusion processing temperature is between 180℃ and 220℃, and the temperature of the die and die is 220℃.
[0040] The invention adds white oil to improve the hardness of the material, and uses polypropylene material to adjust the tensile strength and scratch resistan...
PUM
Property | Measurement | Unit |
---|---|---|
Melt index | aaaaa | aaaaa |
Melt index | aaaaa | aaaaa |
Melt index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap