Semiconductive silicon rubber shielding material for radiation-resistant cable, and preparation method thereof

A technology of shielding material and silicone rubber, applied in the field of semi-conductive silicone rubber shielding material for radiation-resistant cables and its preparation, can solve the problems of intolerant radiation, shielding materials are not resistant to light, etc. Radiation performance, the effect of good production and processing performance

Inactive Publication Date: 2013-03-13
SICHUAN MINGXING CABLE
View PDF4 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The present invention aims to solve the problems of shielding materials in the prior art that are not resistant to light and radiation, and provides a radiation-resistant semi-conductive silic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Semiconductive silicon rubber shielding material for radiation-resistant cable, and preparation method thereof
  • Semiconductive silicon rubber shielding material for radiation-resistant cable, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A radiation-resistant semi-conductive silicone rubber shielding material for cables, comprising the following raw material components in parts by weight:

[0062] Silicone rubber 100 parts

[0063] Conductive carbon black 20 parts

[0064] White carbon black 40 parts

[0065] Dicumyl peroxide 1.0 parts

[0066] Vulcanizing agent 2.0 parts

[0067] Diphenylsilanediol 5 parts

[0068] Stearic acid 1.0 parts

[0069] Zinc oxide 4 parts

[0070] 2 parts of ferric oxide;

[0071] The silicone rubber is phenylene ether silicone rubber or phenylene silicone rubber; the co-curing agent is triallyl cyanurate.

Embodiment 2

[0073] A radiation-resistant semi-conductive silicone rubber shielding material for cables, comprising the following raw material components in parts by weight:

[0074] Silicone rubber 100 parts

[0075] Conductive carbon black 40 parts

[0076] White carbon black 50 parts

[0077] Dicumyl peroxide 2.5 parts

[0078] Vulcanizing agent 3.0 parts

[0079] Diphenylsilanediol 15 parts

[0080] Stearic acid 2.0 parts

[0081] Zinc oxide 6 parts

[0082] 5 parts of ferric oxide;

[0083] The silicone rubber is phenylene ether silicone rubber or phenylene silicone rubber; the co-curing agent is triallyl cyanurate.

Embodiment 3

[0085] A radiation-resistant semi-conductive silicone rubber shielding material for cables, comprising the following raw material components in parts by weight:

[0086] Silicone rubber 100 parts

[0087] Conductive carbon black 30 parts

[0088] White carbon black 45 parts

[0089] Dicumyl peroxide 1.75 parts

[0090] Vulcanizing agent 2.5 parts

[0091] Diphenylsilanediol 10 parts

[0092] 1.5 parts of stearic acid

[0093] Zinc oxide 5 parts

[0094] 3.5 parts of ferric oxide;

[0095] The silicone rubber is phenylene ether silicone rubber or phenylene silicone rubber; the co-curing agent is triallyl cyanurate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific resistanceaaaaaaaaaa
Oil absorption valueaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a semiconductive silicon rubber shielding material for a radiation-resistant cable, and a preparation method of the material, belonging to the technical field of cable shielding material. The semiconductive silicon rubber shielding material comprises the raw material components in parts by weight: 100 parts of silicon rubber, 20-40 parts of conductive carbon black, 40-50 parts of white carbon black, 1.0-2.5 parts of dicumyl peroxide, 2.0-3.0 parts of auxiliary vulcanizing agent, 5-15 parts of diphenyl silanediol, 1.0-2.0 parts of stearic acid, 4-6 parts of zinc oxide and 2-5 parts of ferric oxide, wherein the silicon rubber is phenyl ether supporting silicone rubber or phenylene silicone rubber; and the auxiliary vulcanizing agent is triene propyl cyanurate. The silicon rubber shielding material is good in radiation-resistant performance, and can give play to the specified function for a long time on radiation occasion when being used as a shielding layer of an electric wire and the cable.

Description

technical field [0001] The invention relates to a cable shielding material. More specifically, the invention relates to a semiconductive silicon rubber shielding material for radiation-resistant cables and a preparation method thereof, belonging to the technical field of cable shielding materials. Background technique [0002] In the wire and cable industry, semi-conductive polymer materials are mainly used for conductor shielding and insulation shielding, that is, conductive fillers are added to the polymer matrix material, such as acetylene carbon black, conductive graphite powder, conductive carbon fiber, etc. These two shields are usually based on EVA in power cables. EVA is a thermoplastic elastomer, and its softness is not as good as that of rubber. It is often used in fixed-laying cables. For mobile cables, EVA is stretched due to the limitation of its VA content. The reason is: the higher the VA content, the better the elasticity and softness of EVA, but its price i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08K13/02C08K3/04C08K3/36C08K5/14C08K5/549C08K5/09C08K3/22C08K5/3492H01B7/17
Inventor 张圣博李广元沈卢东盛业武陈光高王娟陈超
Owner SICHUAN MINGXING CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap