Preparation method and dry-wet spinning method of regenerated protein chitosan blended solution

A technology of dry and wet spinning, chitosan solution, applied in the field of regenerated eggs, to achieve the effect of improving uniformity and orientation, improving elongation and elasticity, and high protein content

Inactive Publication Date: 2013-05-22
河南鼎大生物科技有限公司
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the existing defects of using synthetic high polymers to prepare protein fibers, and to in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0042] In this embodiment, the blended solution of regenerated protein chitosan is used as a raw material to prepare composite fibers by a dry-wet spinning process;

[0043] The regenerated protein chitosan blend solution is made from silk, animal hair and chitosan, and its preparation steps are as follows:

[0044] (1) Boil the silk into 0.5% Na 2 CO 3 Degumming in the solution, the amount of silk is 1.5% of the solution weight, degumming 3 times, 15 minutes each time, rinse 3 times with hot water after degumming, then dry at 90 ° C, cut into pieces;

[0045] (2) The dried and shredded silk fiber and pig hair are blended according to the mass ratio of 1:0.2, and then pulverized into a protein fine powder with a diameter of about 25 microns by an airflow ultrafine pulverizer.

[0046] (3) Add protein fine powder into 1-butyl-3-methylimidazolium chloride salt solution, stir and dissolve vigorously at 80°C for 140 minutes, and filter to obtain a regenerated protein solution wi...

Embodiment example 2

[0073] In this embodiment, the blended solution of regenerated protein chitosan is used as a raw material to prepare composite fibers by a dry-wet spinning process;

[0074]The regenerated protein chitosan blend solution is made from silk, animal hair and chitosan, and its preparation steps are as follows:

[0075] (1) Put the Na concentration of 0.5 into the silk under the boiling condition 2 CO 3 Degumming in the solution, the amount of silk is 2.0% of the solution weight, degumming 3 times, 50 minutes each time, rinse with hot water 3 times after degumming, then dry at 60°C and cut into pieces.

[0076] (2) Blend the dried and shredded silk fibers and goat hair at a mass ratio of 1:5, and then pulverize them into protein fine powder with a diameter of about 5.0 microns through an airflow ultrafine pulverizer.

[0077] (3) Add protein fine powder to 1-butyl-3-methylimidazolium tetrafluoroborate aqueous solution, stir and dissolve vigorously at 100°C for 80 minutes, and fil...

Embodiment example 3

[0104] In this embodiment, the blended solution of regenerated protein chitosan is used as a raw material to prepare composite fibers by a dry-wet spinning process;

[0105] The regenerated protein chitosan blend solution is made from silk, animal hair and chitosan, and its preparation steps are as follows:

[0106] (1) Boil the silk into 0.5% Na 2 CO 3 Degumming in the solution, the amount of silk is 3.5% of the solution weight, degumming 3 times, 40 minutes each time, rinse with hot water 3 times after degumming, then dry at 70 ℃, cut into pieces.

[0107] (2) Blend the dried and shredded silk fiber and camel hair according to the mass ratio of 1:10, and then pulverize it into a protein fine powder with a diameter of about 2.0 microns through an airflow ultrafine pulverizer.

[0108] (3) Add protein fine powder into 1-ethyl-3-methylimidazole diethyl phosphate aqueous solution, stir and dissolve vigorously at 115°C for 100 minutes, and filter to obtain a regenerated protein...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Heightaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method and a dry-wet spinning method of a regenerated protein chitosan blended solution. The preparation method comprises the steps of: carrying out ultrafine grinding on raw materials of leftovers of reeling silks and leftovers of animal coarse hairs such as goat hairs, pig hairs, camel hairs and wools, dissolving the crushed raw materials in an ionic liquid to obtain a regenerated protein solution with high molecular weight, and blending the regenerated protein solution with a chitosan liquid to obtain a spinning solution. The spinning solution is molded by using a dry-wet spinning technology, the structure uniformity and the orientation degree of fibers are enhanced through solidification and drafting, and the elongation and the elasticity of the fibers are improved through oxidation crosslinking. The regenerated protein chitosan blended fiber has high protein content, and has functions of bacteria resistance, moisture prevention and promotion of blood coagulation and wound healing; and all compositions in the fiber are in biomass states, have good biodegradability and biocompatibility and can be applied to textile fibers and biomedical materials.

Description

Technical field [0001] The invention is the field of regeneration of biomass resources, involving a preparation method of recycled protein fiber containing chitosan, and specifically involves a regenerative egg with dry and wet spinning technology [0002] The method of preparation and wet wet spinning in white shell polycanic solution. Background technique [0003] Protein fiber has good hygroscopic absorption and anticidering performance, and has good affinity with human skin. In recent years, soybean protein, milk protein, and silkworm pupa protein fibers that have been processed by protein have been market -orientedEssenceHowever, the preparation of these protein fibers is co -concentrated or mixed by protein and synthetic polymers such as polyethylene glycols, polyacrylpines, etc., and the protein content in the fiber is very low.%, The main component is still a synthetic polymer, so the protein fiber is not a protein fiber in a complete sense, and it does not have the excel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F8/18D01F8/02D01F11/02D01F11/00D01D1/02D01D5/06D01D5/14D01D10/06
Inventor 赵振强
Owner 河南鼎大生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap