High-performance adhesive for shoemaking

A technology for adhesives and shoes, applied in the direction of adhesives, adhesive additives, polymer adhesive additives, etc., can solve the problems of poor storage stability, poor water resistance, poor heat resistance, etc., and achieve low cost and environmental protection The effect of good resistance and excellent heat resistance

Inactive Publication Date: 2014-04-30
ANHUI MINGZHU PIGMENT TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the characteristics of chloroprene adhesive are: large initial adhesion, high bonding strength, good durability, flexible adhesive layer, good elasticity, impact and vibration resistance, good oil resistance, water resistance, alkali resistance, acid resistance, and solvent resistance. Performance, good adhesion to a variety of materials, easy to use, low price, but its heat resistance is poor, water resistance is not good, and storage stability is poor
In order to overcome the shortcomings of traditional neoprene adhesives such as poor heat resistance, poor water resistance, poor storage stability, and high toxicity, a high-performance adhesive for shoemaking is produced by improving the formula.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance adhesive for shoemaking

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0015] A high-performance adhesive for shoemaking, made from the following parts by weight of raw materials: 120 parts of styrene, 135 parts of ethyl acetate, 25 parts of chloroprene CR121, 16 parts of xylene, 4,4'-diphenyl 1.6 parts of methyl methane diisocyanate, 10 parts of polyisobutylene, 2 parts of 3-aminopropyltrimethoxysilane, 2.5 parts of polytetrahydrofuran ether glycol, 4 parts of SG-2 PVC resin, 1.8 parts of ferrocene, chlorohydrin rubber H45 8 parts, epoxy resin modified polyamide hot melt adhesive 6 parts, zinc oxide 3 parts, nano wollastonite powder 18 parts, anti-aging agent RD 1.5 parts, 2-thiol benzimidazole 2 parts, stearic acid 3 Parts, accelerator DM 1.5 parts, accelerator TMTD 1.5 parts, glycerol triglyceride 6 parts, N-(β-aminoethyl)-γ-aminopropyl trimethyl(eth)oxysilane 1 part, 2 parts of dicumyl oxide, 1.8 parts of silane coupling agent KH550, 1.5 parts of antioxidant DLTP, 15 parts of carbon black N339, 10 parts of N660 carbon black, 2 parts of zin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water contentaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-performance adhesive for shoemaking. The high-performance adhesive is prepared from the raw materials in parts by weight: 100-120 parts of styrene, 100-150 parts of ethyl acetate, 20-25 parts of neoprene CR121, 15-20 parts of dimethylbenzene, 1-2 parts of 4,4'-diphenylmethane diisocyanate, 8-12 parts of polyisobutylene, 2-3 parts of 3-aminopropyl trimethoxysilane, 2-3 parts of polytetrahydrofuran ether glycol, 3-5 parts of SG-2 PVC (Polyvinyl Chloride) resin, 1-2 parts of ferrocene, 8-10 parts of epichlorohydrin rubber H45, 5-8 parts of epoxy resin modified polyamide hot-melt adhesive and the like. The adhesive disclosed by the invention has excellent heat resistance and water resistance, is high in adhesive strength, good in storage stability, good in environmental protection performance, good in use effect and convenient to use and is water-resistant and dampproof.

Description

Technical field [0001] The invention relates to an adhesive, in particular to a high-performance adhesive for shoemaking. Background technique [0002] With the development of the shoe industry, adhesives for shoes have also developed correspondingly, and there are many varieties, but the largest amount of them is neoprene adhesive and polyurethane adhesive. Among them, the characteristics of neoprene adhesive are: large initial adhesion, high bonding strength, good durability, flexible adhesive layer, good elasticity, impact and vibration resistance, good oil resistance, water resistance, alkali resistance, acid resistance, and solvent resistance Performance, good adhesion to a variety of materials, easy to use, low price, but its heat resistance is poor, water resistance is poor, and storage stability is poor. In order to overcome the disadvantages of traditional neoprene adhesives such as poor heat resistance, poor water resistance, poor storage stability, and high toxicity, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J4/00C09J4/06C09J11/08C09J11/04C08B31/00
Inventor 徐冉阳
Owner ANHUI MINGZHU PIGMENT TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products