Machine-spraying quick-demulsifying solidification film formation creep waterproof coating and preparation method thereof

A waterproof coating and rapid technology, applied in asphalt coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as difficulty in finding the source of leakage, difficulty in repair work, leakage, etc., to overcome deformation and cracking, shorten the construction period , the stable effect of the mixed system

Active Publication Date: 2014-01-22
浙江鲁班建筑防水有限公司
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But another problem has arisen from this, that is, once the waterproof layer produces small holes or cracks in a certain part and leaks water, there will be water channeling under the waterproof layer, resulting in multiple leaks in the room, and it is difficult to find the leak. The source of the leakage brings great difficulty to the repair work

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Embodiment 1 The weight ratio of each component of the raw materials of the fast demulsification and solidification film-forming creep type waterproof coating that can be machine sprayed is as follows:

[0036] Component A:

[0037] Styrene-butadiene-styrene block copolymer (TPO) 5%

[0038] Bitumen 35%

[0039] Fatty acid ester polypeptide condensate 2%

[0040] Neoprene Latex 17%

[0041] Activated Calcium Carbonate 3%

[0042] Water 38%.

[0043] Component B:

[0044] 1:1 mixture of magnesium chloride and calcium bromide by weight 30%

[0045] water 70%

[0046] The fatty acid ester polypeptide condensate described therein is obtained by condensation of fatty acid chlorides with amino groups of protein hydrolysates, and has the structural formula RCONH (polypeptide) COOH, wherein R is (C 17 -C 19 ).

[0047] Above-mentioned waterproof coating preparation method is as follows:

[0048] Preparation of component A:

[0049] 1) According to the above dos...

Embodiment 2

[0062] The weight ratio of each component of the raw material of the fast demulsification, solidification, film-forming and creeping waterproof coating that can be sprayed by machine is as follows:

[0063] Component A:

[0064] Polyolefin thermoplastic elastomer 5%

[0065] Bitumen 32%

[0066] Imidazoline emulsifier (2-alkyl-N carboxymethyl-N-hydroxyethyl imidazoline products) 5%

[0067] Neoprene Latex 11%

[0068] Natural rubber latex 8%

[0069] Bentonite 1%

[0070] water 38%

[0071] Component B:

[0072] Polyamidoamine dendrimers (PAMAM) 30%

[0073] Polyamine Condensate Demulsifier 3% (condensate of mixture of epihalohydrin and ammonia with amine)

[0074] water 67%

[0075] The above-mentioned waterproof coating preparation method is the same as that of Example 1, wherein the stirring time is 120 minutes.

[0076] The test data of the above waterproof coating are as follows:

[0077] Physical properties: 100% cohesive failure of adhesive propert...

Embodiment 3

[0082] The weight ratio of each component of the raw material of the fast demulsification, solidification, film-forming and creeping waterproof coating that can be sprayed by machine is as follows:

[0083] Thermoplastic Polyurethane (TPU) 7%

[0084] Bitumen 30%

[0085] Sodium Dialkyl Petroleum Sulfonate 2%

[0086] Butyl Rubber Latex 12%

[0087] Styrene Butadiene Rubber Latex 4%

[0088] Wollastonite powder 1%

[0089] Water 44%.

[0090] Component B:

[0091] Polyamide-amine dendrimers 40%

[0092] water 60%

[0093] The preparation method of the above-mentioned polymer waterproof coating is the same as in Example 1, wherein the stirring time is 90 minutes.

[0094] The test data of the above-mentioned polymer waterproof coating are as follows:

[0095] Physical properties: 100% cohesive failure of adhesive properties

[0096] Heat resistance 75℃

[0097] Low temperature flexibility -20℃

[0098] Creep performance under shear state 0.1 N / mm. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a machine-spraying quick-demulsifying solidification film formation creep waterproof coating and a preparation method thereof, belonging to the technical field of waterproof coating. The waterproof coating is formed from the components A and B by atomization mixing in air and dehydration curing, wherein the component A comprises the following components in percentage by weight: 5-20% of thermoplastic elastomer polymer, 20-50% of asphalt, 30-50% of water, 1-5% of emulsifier, 5-20% of rubber latex and 0-20% of filler; the component B consists of the following components in percentage by weight: 30-40% of demulsifier and 60-70% of water. The waterproof coating overcomes the shortcomings of a common elastomer, such as quick aging in a high-stress state for a long time, stretching fatigue and the like, and always keeps good viscosity and re-bonding ability; the problem of internal stress of a waterproof layer is thoroughly solved, so that the waterproof layer has the characteristics of strong sustained bonding ability, high elongation and low-temperature flexibility; the material has good adhesive property, good heat resistance and good low-temperature flexibility, and the creep property in a shear state can exceed 0.1N / mm.

Description

technical field [0001] The invention belongs to the technical field of waterproof coatings, and in particular relates to a non-curing waterproof coating capable of rapid demulsification, solidification, and film formation that can be sprayed by a machine and a preparation method thereof. Background technique [0002] Modified asphalt membranes, such as SBS and APP membranes, which are more popular in the waterproof material market at present, require flame spray guns to carry out on-site surface melting, require open flames, have high technical requirements, and easily cause the surface hot melt adhesive to coke. The width of the coil is only one meter, and there are many overlaps during laying. Due to the shape requirements of the base layer, it needs to be cut, and the amount of overlap is increased, which is likely to cause hidden dangers of joint waterproofing; Its water resistance is poor, and it is easy to cause waterproof failure due to degumming, so the bonding of po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D153/02C09D123/00C09D175/04C09D7/12
Inventor 项晓睿
Owner 浙江鲁班建筑防水有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap