Single-component oxime-removed silicone sealant for sealing solar cell module and preparation method thereof
A solar cell and silicone sealant technology, which is applied to chemical instruments and methods, adhesives, and other chemical processes, can solve the problems of inconvenient operation, no mention of glue flame retardancy, no mention of water vapor transmission rate, etc. question
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0034] Example 1
[0035] Set the specific surface area to 130 cm 3 / g fumed silica is dried and dehydrated at 110°C for 2 hours; 100 parts of α,ω-dihydroxy polydimethylsiloxane with a viscosity of 20000cPa.s and polydimethylsiloxane with a methyl group at the molecular end 10 parts methyl silicone oil with 1000cPa.s alkane viscosity, 5 parts polyisobutylene resin, 30 parts activated calcium carbonate, 25 parts aluminum hydroxide, 5 parts basic zinc carbonate, 2 parts ammonium polyphosphate, particle size 0.08 micron Add 3 parts of titanium dioxide into a vacuum kneader, blend and dehydrate for 150 minutes at a temperature of 110°C and a vacuum degree of 0.07 MPa, and cool to obtain a base material. At room temperature, the specific surface area is 130m 2 / g fumed white carbon black 5 parts, methyl triisobutyl ketoxime silane 8 parts, vinyl triisobutyl ketoxime silane 5 parts, tetraisobutyl ketoxime silane 0.5 parts, vinyl tris (β-methyl 3 parts of oxyethoxy) silane, 1 part of b...
Example Embodiment
[0037] Example 2
[0038] Set the specific surface area to 200cm 3 / g fumed white carbon black is dried and dehydrated at 110°C for 3 hours; 100 parts of α,ω-dihydroxy polydimethylsiloxane with a viscosity of 50000cPa.s and polydimethylsiloxane whose molecular end is methyl 10 parts methyl silicone oil with 1000cPa.s alkane viscosity, 1 part polyisobutylene resin, 30 parts activated calcium carbonate, 25 parts aluminum hydroxide, 5 parts basic zinc carbonate, 2 parts ammonium polyphosphate, particle size 0.08 micron Add 3 parts of titanium dioxide into a vacuum kneader, blend and dehydrate for 150 minutes at a temperature of 110°C and a vacuum degree of 0.07 MPa, and cool to obtain a base material. At room temperature, the specific surface area is 200cm 3 / g 5 parts of fumed silica, 12 parts of methyl triisobutyl ketoxime silane, 2 parts of vinyl triisobutyl ketoxime silane, 3 parts of vinyl tris (β-methoxyethoxy) silane, 1 part of bis(γ-trimethoxysilylpropyl)amine, 1.1 parts o...
Example Embodiment
[0040] Example 3
[0041] Set the specific surface area to 130cm 3 / g fumed white carbon black is dried and dehydrated at 110°C for 2 hours; 100 parts of α,ω-dihydroxy polydimethylsiloxane with a viscosity of 80,000 cPa.s and polydimethylsiloxane whose molecular end is methyl 15 parts of methyl silicone oil with 1000cPa.s alkane viscosity, 5 parts of polyisobutylene resin, 40 parts of active calcium carbonate, 20 parts of aluminum hydroxide, 15 parts of basic zinc carbonate, 3 parts of titanium dioxide with a particle size of 0.08 microns, add to vacuum In the kneader, at a temperature of 110°C and a degree of vacuum of 0.07 MPa, blend and dehydrate for 150 minutes, and cool to obtain the base material. At room temperature, the specific surface area is 130cm 3 / g 3 parts of fumed silica, 8 parts of methyl triisobutyl ketoxime silane, 5 parts of vinyl triisobutyl ketoxime silane, 0.5 part of tetraisobutyl ketoxime silane, γ-aminopropyl triethyl 1.5 parts of oxysilane, 1.0 part o...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap