EPDM (Ethylene-Propylene-Diene Monomer) acrylic resin rubber sealing gasket material and preparation method thereof

A technology of EPDM rubber and rubber gasket, applied in the field of rubber composite material processing, can solve the problems of low strength, unsatisfactory sealing effect, poor wear resistance, etc., achieve low cost, good sealing and aging resistance, The effect of improving process performance

Inactive Publication Date: 2014-03-26
蚌埠市方园电子应用研究所有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance, and low strength, which are far from meeting the actual requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • EPDM (Ethylene-Propylene-Diene Monomer) acrylic resin rubber sealing gasket material and preparation method thereof
  • EPDM (Ethylene-Propylene-Diene Monomer) acrylic resin rubber sealing gasket material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The present invention will be described in detail below through specific examples.

[0010] An EPDM acrylic resin rubber gasket material, made of the following raw materials in parts by weight (kg): EPDM rubber (LANXESS 2470) 60, acrylate rubber 10, phthalate 12 , Zinc Oxide 3, Stearic Acid 2, Carbon Black 30, N-Phenyl-α-Naphthylamine 1, Tributyltin Chloride 1, Dioctadecyl Dimethyl Ammonium Chloride 1, Antiaging Agent ODA1, Accelerator DM3, sulfur 2, modified attapulgite 10;

[0011] The modified attapulgite is made of the following raw materials in parts by weight (kg): attapulgite 20, clay 12, 1,6-hexamethylene diisocyanate 3, tripropylene glycol diacrylate 2, nano titanium dioxide 3, nano Silicon dioxide 1, zinc oxide 1, accelerator TMTD1, actinolite powder 8, pepper seed oil 1; the preparation method is to mix attapulgite and clay into a calciner and calcinate at 700-720°C for 3-4 hours, Cool, soak in 10-12% hydrochloric acid solution for 1-2 hours, filter and tak...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an EPDM (Ethylene-Propylene-Diene Monomer) acrylic resin rubber sealing gasket material, which is characterized by comprising the following raw materials in parts by weight: 60-65 parts of EPDM (Lanxee 2470), 10-12 parts of acrylate rubber, 12-15 parts of phthalate esters, 3-4 parts of zinc oxide, 2-3 parts of stearic acid, 30-34 parts of carbon black, 1-2 parts of N-phenyl-1-naphthylamine, 1-2 parts of chlorotributyltin, 1-2 parts of dioctadecyl dimethyl ammonium chloride, 1-2 parts of anti-aging agent ODA, 3-4 parts of accelerator DM, 2-3 parts of sulfur, and 10-12 parts of modified attapulgite. According to the EPDM acrylic resin rubber sealing gasket material, the technological property of rubber can be improved due to the addition of the modified attapulgite, and the toxic and side effects and environmental pollution can be reduced due to the use of an environment-friendly compounding ingredient; the material has the advantages of reasonable formula, excellent mechanical property, high strength, good sealing and anti-aging properties, as well as simpleness in technology and low cost and is safe and non-toxic.

Description

technical field [0001] The invention relates to the field of processing rubber composite materials, in particular to a EPDM acrylic resin rubber sealing gasket material and a preparation method thereof. Background technique [0002] Gasket is a material used for sealing inside machinery, equipment, pipelines, etc. The gaskets currently used are mostly rubber gaskets, which are characterized by high temperature resistance, ozone resistance, natural aging resistance, vacuum resistance, fuel oil resistance, lubricating oil resistance, strong oxidant resistance, chemical resistance and good electrical insulation performance. Widely used in defense industry and civilian industry. However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance and low strength, which are far from meeting the actual requirements. Therefore researching and developing a kind of high-performance rubber gasket has become the task of top priority. Conten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L33/04C08K13/06C08K9/00C08K9/02C08K3/34C08K5/103C08K3/22C08K3/36C08K5/12
CPCC08L23/16C08L2201/08C08L33/04C08K13/06C08K9/00C08K9/02C08K3/34C08K3/346C08K5/12C08K2003/2296C08K3/04
Inventor 夏云夏建生
Owner 蚌埠市方园电子应用研究所有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap