A rare earth-containing thermos preform material

A thermos bottle and preform technology, applied in the field of glass materials, can solve the problems of being unable to adapt to the boiling water environment for a long time, low mechanical strength, and damage to personal safety, etc., and achieve the effect of promoting clarification, improving the bubble environment, and reducing the sintering temperature

Active Publication Date: 2017-01-11
山东誉滕医疗器械有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional thermos bottle preform is made of silicon dioxide as the main material and mixed with several oxides. The mechanical strength is not high, which makes it easier to break during use and transportation, resulting in waste of resources. Some thermal stability Not strong, unable to adapt to boiling water environment for a long time, not only easy to break, but also may damage personal safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A thermos bottle preform material containing rare earth, it is made up of the raw material of following parts by weight (kg):

[0028] Silica powder 80, dolomite 30, potassium feldspar 15, magnesia 6, calcium oxide 3, zirconia 4, alumina 2, lanthanum carbonate 0.1, boron oxide 0.5, premix 20, compound clarification aid 1;

[0029] Described premix is ​​made up of the raw material of following weight portion:

[0030] Marble 70, lepidolite 15, talcum powder 2, boric acid 6, sodium oxide 10;

[0031] The preparation method of described premix comprises the following steps:

[0032] Mix the above-mentioned raw material components into a glass melting furnace, melt at a high temperature of 1680°C for 2 hours, and then lower it to 1450°C for clarification for 1 hour to obtain a premix;

[0033] Described composite clarification aid is made up of the following raw materials of weight part:

[0034] Fly ash 30, sodium carbonate 14, bone char 1, barium nitrate 4, 60% sulfuri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a rare-earth-contained thermos flask blank material composed of the following raw materials in parts by weight: 70-80 parts of silicon powder, 20-30 parts of dolomite, 10-15 parts of potash feldspar, 4-6 parts of magnesium oxide, 2-3 parts of calcium oxide, 3-4 parts of zirconium dioxide, 1-2 parts of aluminum oxide, 0.08-0.1 part of lanthanum carbonate, 0.5-1 part of boric oxide, 10-20 parts of premix and 1-2 parts of composite clarification aid. The premix added in the rare-earth-contained thermos flask blank material is added into main molten glass after being clarified in advance, so that the air bubble environment in the molten glass is improved, and the clarification effect is effectively promoted; the premix is also favorable in shock resistance and fusion assistance performance and capable of reducing the product sintering temperature, shortening the sintering time and improving the flowability and adhesive force.

Description

technical field [0001] The invention mainly relates to a thermos bottle preform material containing rare earth, which belongs to the field of glass materials. Background technique [0002] The traditional thermos bottle preform is made of silicon dioxide as the main material and mixed with several oxides. The mechanical strength is not high, which makes it easier to break during use and transportation, resulting in waste of resources. Some thermal stability Not strong, unable to adapt to the boiling water environment for a long time, not only easy to break, but also may damage personal safety. Contents of the invention [0003] The purpose of the present invention is to provide a thermos bottle preform material containing rare earth. [0004] The present invention is achieved through the following technical solutions: [0005] A rare earth-containing thermos bottle preform material, which is composed of the following raw materials in parts by weight: [0006] Silica pow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C6/00C03C1/00
Inventor 金艳萍
Owner 山东誉滕医疗器械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com