Environment-friendly casting molding sand and preparation method thereof

A casting mold and environmental protection technology, which is applied in the direction of casting molding equipment, casting molds, mold cores, etc., can solve the problems of rough surface of aluminum sand parts, poor air permeability of sand molds, toxic gas pollution, etc., and achieve good bonding effect and no collapse Good performance, the effect of solving shrinkage cavity

Active Publication Date: 2014-09-24
中合基铭实业江苏有限公司
View PDF7 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Molding sand is generally made by mixing molding materials such as raw sand for casting, molding sand binder and auxiliary additives in a certain proportion. Natural silica sand containing clay can also be used. In the usual molding sand formula for aluminum casting, the particle size of the molding sand is too large or If it is too small, the diameter of the sand material is too large. Although the air permeability is good, the surface of the aluminum sand parts is rough and the finish is not good. The diameter of the sand material is too small, resulting in poor air permeability of the sand mold and air holes in the aluminum casting
Coal powder clay green sand, which is widely used at home and abroad, is generally made of raw sand, binders, coal powder additives, etc. and water. It has a certain anti-sticking sand effect, low material cost, and high production efficiency. However, its consumption is large, the emission is serious, and the coal powder is burned and decomposed in the casting process to produce toxic gas pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] An environmentally friendly foundry sand made from the following raw materials in parts by weight (kg): quartz sand 220, sodium bentonite 55, red clay 25, talcum powder 35, zinc oxide 25, traditional Chinese medicine slag 22, straw powder 43, carboxymethyl fiber Vegetable 2.5, Brown Sugar 7, Fatty Alcohol Polyoxyethylene Ether 1.6, Brick Slag Powder 44, Boric Acid 2.5, Perlite 43, Polyvinyl Alcohol 2.5, Tung Oil 1.5, Bamboo Charcoal 33, Appropriate amount of water.

[0012] The preparation method of the environment-friendly foundry sand is characterized in that it comprises the following steps: putting sodium bentonite, red clay, brick slag powder, and perlite in a calcination furnace at 560°C for 3.6 hours, and then taking them out and crushing them into 250-mesh powder, Then add traditional Chinese medicine residue, straw powder, appropriate amount of water, stir and disperse, knead the mud, send it to a calcination furnace at 1430°C for 4 hours, take it out and pulver...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly casting molding sand which is made of the following raw materials in parts by weight: 200-230 parts of quartz sand, 50-60 parts of sodium bentonite, 20-30 parts of red soil, 30-40 parts of talcum powder, 20-30 parts of zinc oxide, 20-24 parts of Chinese medicine residue, 40-45 parts of straw powder, 2-3 parts of carboxymethyl cellulose, 5-8 parts of brown sugar, 1-2 parts of fatty alcohol polyoxyethylene ether, 40-50 parts of brick trash powder, 2-3 parts of boric acid, 40-45 parts of perlite, 2-3 parts of polyving alcohol, 1-2 parts of tung oil, 30-35 parts of bamboo charcoal and a proper amount of water. According to the invention, the brick trash powder is adopted, the Chinese medicine residue, the straw powder and the like are sintered at high temperate, the sand is loosened, breathable and good in collapsibility and is environmental-friendly and energy-saving, and with the combination of talcum powder, the dispersity and the plasticity are improved; due to adoption of brown sugar, tung oil and carboxymethyl cellulose as binding agents, the sand is not only good in binding effect, but also not affected in collapsibility at high temperature; the pass percent of cast pieces is improved, and the casting cost is lowered.

Description

technical field [0001] The invention relates to the field of casting, in particular to an environment-friendly foundry sand and a preparation method thereof. Background technique [0002] Molding sand is a material used for molding in casting. Molding sand is generally made by mixing molding materials such as raw sand for casting, molding sand binder and auxiliary additives in a certain proportion. Natural silica sand containing clay can also be used. In the usual molding sand formula for aluminum casting, the particle size of the molding sand is too large or If it is too small, the diameter of the molding sand is too large. Although the air permeability is good, the surface of the aluminum sand parts is rough and the finish is not good. If the diameter of the molding sand is too small, the air permeability of the sand mold is not good, and the aluminum castings have pores. Coal powder clay green sand, which is widely used at home and abroad, is generally made of raw sand, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C1/00B22C1/20
Inventor 朱安会马洪章
Owner 中合基铭实业江苏有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products