Preparation method of collagen diaphragm material
A collagen film and collagen technology, applied in the preparation method of peptides, chemical instruments and methods, organic chemistry, etc., can solve the problems of low biological activity and biological safety, achieve high strength, low salt content, and flexible texture Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0035] Example 1
[0036] (1) Preparation of raw materials
[0037] Wash the cowhide and put it into a drum, and add 1% Na with more than double the weight of animal skin 2 CO 3 Stir for 2h and wash with clean water, then put the cowhide in 1 to 5 times the quality of the cowhide with 1% Na 2 S and 5% Ca(OH) 2 In the aqueous solution, dehairing the cowhide, and then use 5% NH 4 Cl adjust the pH of the solution to between 6-8, wash the cowhide, and then use a skinning machine to remove the lower layer of meat and the upper layer of skin on the cowhide to obtain a collagen fiber layer, and add acetone to the collagen fiber layer for multiple degreasing Then, air-dry to obtain raw materials;
[0038] (2) Fracture of collagen fibers
[0039] After the collagen fiber layer raw material obtained in step (1) is physically broken, it is added to 0.2mol / L volatile acid solution hydrochloric acid to soak to remove salt, and the mixture of collagen fiber layer and hydrochloric acid is placed in ...
Example Embodiment
[0046] Example 2
[0047] Example 2 is used to illustrate the preparation method of the collagen membrane provided by the present invention.
[0048] The collagen product was prepared by the same method as in Example 1, except that step (1) was carried out according to the following steps: the pig skin was washed and put into the drum, and 0.1% Na with more than double the weight of the pig skin was added. 2 CO 3 Stir for 2h and wash with clean water, then put the pigskin in 1 to 5 times the weight of pigskin containing 10% Na 2 S and 10%Ca(OH) 2 In the aqueous solution, the pig skin is dehaired, and then 1% NH is used 4 Cl adjust the pH of the solution to between 6-8, wash the pig skin, and then use a skin peeling machine to remove the lower and upper epidermis on the pig skin to obtain a collagen fiber layer. The collagen fiber layer is added with acetone for more After the second degreasing, air-dry to obtain raw materials.
Example Embodiment
[0049] Example 3
[0050] Example 3 is used to illustrate the preparation method of the collagen membrane provided by the present invention.
[0051] The collagen product was prepared by the same method as in Example 1, except that step (1) was carried out according to the following steps: Wash the cowhide and put it into a drum, and add 5% Na with more than double the quality of the cowhide. 2 CO 3 Stir for 2h and wash with clean water, then put the cowhide in 1 to 5 times the quality of the cowhide with 1% Na 2 S and 1%Ca(OH) 2 In the aqueous solution, dehairing the cowhide, and then use 10% NH 4 Cl adjust the pH of the solution to between 6-8, wash the cowhide, and then use a skinning machine to remove the lower layer of meat and the upper layer of skin on the cowhide to obtain a collagen fiber layer, and add acetone to the collagen fiber layer for multiple degreasing Then, air-dried to obtain raw materials.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap