Heatproof 105 DEG C polyvinyl chloride cable material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of polyvinyl chloride cable and polyvinyl chloride resin, applied in plastic/resin/wax insulators, organic insulators and other directions, can solve the problems of economic loss, easy failure, etc., achieve less smoke, good flame retardant effect, improve The effect of service life
Inactive Publication Date: 2014-10-22
ANHUI RONGJIU OPTICAL FIBER COMM
View PDF4 Cites 11 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the existing polyvinyl chloride cable materials are difficult to use for a long time at high temperature, and are prone to failure, causing great economic losses
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0013] A heat-resistant 105℃ polyvinyl chloride cable material, made of the following weight (kg) raw materials: SG-3 polyvinyl chloride resin 100, bisphenol A polycarbonate 15, chlorinated polyethylene 10, trimellitene Trioctyl acid 30, diisodecyl phthalate 15, pentaerythritol stearate 7, barium sulfate 15, nano wollastonite 8, composite filler 6, aniline methyl triethoxy silane 1.5, calcium zinc composite Stabilizer 6, barium stearate 1.5, ethylene bis stearamide 2, zinc borate 15, decabromodiphenyl ether 6, antioxidant 10350.6;
[0014] The preparation method of the composite filler is as follows: a. Take the following weight (kg) of raw materials: kaolinite 10, pyrophyllite 10, zeolite powder 6, fly ash 4, stearic acid 2, isopropyl distearyl oxide Base aluminate 1.5, calcium lignosulfonate 4, epoxy linseed oil 10, nano zirconia 3, nano jade powder 6, cerium isooctanoate 1.5, neodymium isooctanoate 0.5; b. Put kaolinite and pyrophyllite at 540℃ Calcined for 3h, cooled to room...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a heatproof 105 DEG C polyvinyl chloride cable material and a preparation method thereof, the cable material comprises the following raw materials by weight: 100 parts of SG-3 pvc resins, 15-20 parts of bisphenol A polycarbonate, 8-12 parts of chlorinated polyethylene, 25-35 parts of tricapryl trimellitate, 10-15 parts of diisodecyl phthalate, 5-10 parts of pentaerythritol stearate, 10-15 parts of barium sulfate, 5-10 parts of nano wollastonite, 4-8 parts of composite filling material, 1-2 parts of AMTEOS, 5-8 parts of calcium zinc composite stabilizing agent, 1-2 parts of barium stearate, 1-2 parts of ethylene bis stearamide, 10-15 parts of zinc borate, 5-10 parts of decabromodiphenyl oxide and 0.5-1 part of anti-oxidant. The cable material has excellent mechanical strength, heat stability, weather resistance and ageing resistance, and good flame retardation effect, flare quenching can be rapidly carried out after flame disappears, other material can not be combusted, the smoke amount is little while the cable material is combusted, can be used under 105 DEG C for long-term, and the usage life of the cable can be increased.
Description
Technical field [0001] The invention relates to a cable material and a preparation method thereof, in particular to a heat-resistant 105°C cable material and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is widely used as a sheath material for wires and cables because of its flame-retardant, oil-resistant, corona-resistant, chemical resistance, and good water resistance and processing properties. However, the existing polyvinyl chloride cable materials are difficult to use for a long time under high temperature and are prone to failure, causing great economic losses. Summary of the invention [0003] The purpose of the present invention is to provide a heat-resistant 105°C cable material and a preparation method thereof in view of the shortcomings of the prior art. [0004] The technical scheme adopted by the present invention is as follows: [0005] A heat-resistant 105℃ polyvinyl chloride cable material, made of the following parts by weight:...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.