Acrylic emulsion of novel transfer adhesive and preparation method of acrylic emulsion

A technology of acrylic emulsion and transfer adhesive, which is applied in adhesive types, ester copolymer adhesives, etc. It can solve problems such as poor adhesion, environmental hazards, and aluminum layer peeling off, so as to ensure conversion rate and environmental protection , Improve the bonding strength and reduce the effect of film forming temperature

Active Publication Date: 2014-12-10
ETABONG QINGDAO INDAL
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing aluminized transfer adhesives have certain defects in product performance and coating process. Some of them have poor adhesion, and the aluminum foil and paper are peeled off during use, or an aluminum layer appears during the next process. Falling off; some transferred paper has poor folding resistance and is easy to break; some coating process is complicated, inconvenient to use, easy to cause waste, or poor adaptability to the coating compound machine, and sticking rolls occur during sizing phenomenon
In addition, the traditional product alkylphenol polyoxyethylene ether compound (APEO) emulsifier has certain harm to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Add 4.0 parts of styrene, 11 parts of methyl methacrylate, 2.5 parts of butyl acrylate, 0.8 parts of acrylic acid and 1.0 part of N-methylol acrylamide into the container, mix well to make a solution of inner core monomer, and set aside ; Add 3 parts of styrene, 8.5 parts of methyl methacrylate, 23 parts of butyl acrylate, 1 part of acrylic acid and 1.0 part of N-methylol acrylamide into another container and mix evenly to make a shell monomer solution, which is set aside;

[0023] (2) Put 0.2 parts of alkyl alcohol polyether, 0.4 parts of sodium lauryl sulfate, and 0.16 parts of baking soda into the polymerization kettle, start stirring, set the stirring speed at 100 rpm, raise the temperature to 75°C, and add 0.1 parts Ammonium persulfate, start to add the inner core monomer solution dropwise, the dropping time is 2 hours, keep warm for 0.5 hours after dropping; add 0.08 parts of ammonium persulfate, then add the outer shell monomer dropwise, the dropping time is 3...

Embodiment 2

[0027] (1) Add 5 parts of styrene, 9 parts of methyl methacrylate, 2 parts of butyl acrylate, 1.2 parts of acrylic acid and 0.5 parts of N-methylol acrylamide into the container, mix well to make the inner core monomer solution, and set aside ; Add 5 parts of styrene, 5 parts of methyl methacrylate, 20 parts of butyl acrylate, 1.5 parts of acrylic acid and 0.5 parts of N-methylol acrylamide into another container and mix them uniformly to make a shell monomer solution for later use;

[0028] (2) Put 0.4 parts of alkyl alcohol polyether, 0.6 parts of sodium lauryl sulfate, and 0.2 parts of baking soda into the polymerization kettle, start stirring, set the stirring speed at 200 rpm, raise the temperature to 78°C, and add 0.1 parts Ammonium persulfate, start to add the inner core monomer solution dropwise, the dropping time is 2.5 hours, keep warm for 1 hour after dropping; add 0.1 part of ammonium persulfate, then add the shell monomer dropwise, the dropping time is 3.5 hours, d...

Embodiment 3

[0032] (1) Add 4.5 parts of styrene, 10 parts of methyl methacrylate, 2.25 parts of butyl acrylate, 1 part of acrylic acid and 0.8 parts of N-methylol acrylamide into the container, mix well to make the inner core monomer solution, and set aside ;Add 4 parts of styrene, 7 parts of methyl methacrylate, 22 parts of butyl acrylate, 1.25 parts of acrylic acid and 0.8 parts of N-methylol acrylamide into another container and mix evenly to make a shell monomer solution, which is set aside;

[0033] (2) Put 0.3 parts of alkyl alcohol polyether, 0.5 parts of sodium lauryl sulfate, and 0.18 parts of baking soda into the polymerization kettle, start stirring, set the stirring speed at 150 rpm, raise the temperature to 70°C, and add 0.1 parts Ammonium persulfate, start to drop the inner core monomer solution, the dropping time is 2 hours, keep warm for 0.5 hours after dropping; add 0.1 part of ammonium persulfate, then add the outer shell monomer dropwise, the dropping time is 3 hours, dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an acrylic emulsion of a novel transfer adhesive. The acrylic emulsion comprises the following raw materials: alkyl alcohol polyether, lauryl sodium sulfate, a pH regulator, ammonium persulfate, tert-butyl hydroperoxide, sodium hydrogen sulfite, ammonia water and isothiazolinone; inner-core monomers comprise styrene, methyl methacrylate, butyl acrylate, acrylic acid and N-hydroxymethyl acrylamide; and outer-shell monomers comprise styrene, methyl methacrylate, butyl acrylate, acrylic acid and N-hydroxymethyl acrylamide. The acrylic emulsion has the beneficial effect that the solid content is not less than 50%, and the characteristics such as adhesion, transfer and folding resistance are excellent; the acrylic emulsion can be widely applied to transferring to paper products from aluminum-coated layers on polymer base materials such as BOPP (biaxially-oriented Polypropylene) and PET (polyethylene terephthalate), is safe and environmentally friendly, low in VOC (volatile organic compounds) and capable of satisfying the industries with safety and sanitation requirements such as cigarette packaging.

Description

technical field [0001] The invention relates to the field of adhesive preparation, in particular to a novel acrylic emulsion of transfer adhesive and a preparation method. Background technique [0002] At present, most of the gold and silver cardboard used for packaging of cigarettes, food, cosmetics and gifts are made of aluminum foil or aluminized plastic film and cardboard directly. The aluminum foil or plastic film on the surface of the cardboard cannot be recycled directly. brought environmental pressure. In recent years, aluminized transfer paper has been widely used as a new type of environmentally friendly packaging material. The main uses of aluminized transfer paper include aluminized transfer beer label paper, aluminized transfer cigarette lining paper, aluminized transfer packaging cardboard, aluminized transfer food packaging paper, etc. It uses the peelability of the aluminum-plated transfer layer to transfer the aluminum layer with various aesthetic effects ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F220/14C08F212/08C08F220/58C08F2/30C08F2/26C09J133/08
Inventor 张凯琳董全江孙勇刘新建刘金亭关明李英会张华峰
Owner ETABONG QINGDAO INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap