Stretch-proof wear-resistant oil-resistant modified cable material and preparation method thereof

A stretch-resistant, cable material technology, applied to rubber insulators, organic insulators, etc., can solve the problem that cable materials cannot meet the demand, and achieve the effects of improving heat resistance, increasing cross-linking degree, and reducing cross-linking reaction time

Inactive Publication Date: 2014-12-24
ANHUI LAND GRP
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the wear resistance, stretch resistance and oil resistance of rubber materials, people add various compounding components in the process of making rubber products from raw rubber. and oil resistance are greatly affected, but the current cable materials still cannot meet the demand. How to prepare a rubber material with excellent wear resistance, tensile resistance and oil resistance has become a technical problem that needs to be solved at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017]The present invention proposes a stretch-resistant, abrasion-resistant and oil-resistant modified cable material, whose raw materials include, by weight, 8 parts of chloroprene rubber, 28 parts of hydrogenated nitrile rubber, 70 parts of EPDM rubber, and 20 parts of melamine-formaldehyde resin. , 13 parts of pretreated plant powder, 11 parts of aluminum borate whiskers, 2 parts of titanium nitride, 8 parts of alumina, 27 parts of calcite, 27 parts of furnace carbon black, 18 parts of quartz powder, diethyl phthalate DEP8 3 parts, 3 parts of cresyl diphenyl phosphate CDPP, 5.3 parts of antimony trioxide, 5.3 parts of red phosphorus capsule, 8 parts of peroxide curing system, 0.4 parts of anti-aging agent D-500, 1.8 parts of anti-aging agent SP; The ethylene-propylene ratio of the rubber is 63:37, and the peroxide vulcanization system includes: 80wt% di-tert-butyl peroxide, 10wt% N, N'-m-phenylene bismaleimide, 3wt% butyl Sodium acetylenic acid, 7wt% sulfur powder; wherein...

Embodiment 2

[0020] The present invention proposes a stretch-resistant, abrasion-resistant and oil-resistant modified cable material, the raw materials of which include by weight: 12 parts of chloroprene rubber, 25 parts of hydrogenated nitrile rubber, 73 parts of EPDM rubber, and 17 parts of melamine formaldehyde resin , 16 parts of pretreated plant powder, 8 parts of aluminum borate whiskers, 5 parts of titanium nitride, 4 parts of alumina, 30 parts of calcite, 24 parts of furnace carbon black, 21 parts of quartz powder, diethyl phthalate DEP6 4 parts, 4 parts of cresyl diphenyl phosphate CDPP, 3.4 parts of antimony trioxide, 6.2 parts of red phosphorus capsule, 6 parts of peroxide vulcanization system, 0.8 parts of anti-aging agent D-50, 1.2 parts of anti-aging agent SP; The ethylene-propylene ratio of the rubber is 70:30, and the peroxide vulcanization system includes by weight percentage: 84wt% di-tert-butyl peroxide, 5wt% N, N'-m-phenylene bismaleimide, 5wt% butyl Sodium acetylenic a...

Embodiment 3

[0023] The present invention proposes a kind of stretch-resistant, abrasion-resistant and oil-resistant modified cable material. The raw materials include by weight: 9 parts of chloroprene rubber, 27 parts of hydrogenated nitrile rubber, 71 parts of EPDM rubber, and 19 parts of melamine formaldehyde resin , 14 parts of pretreated plant powder, 10 parts of aluminum borate whiskers, 3 parts of titanium nitride, 7 parts of alumina, 28 parts of calcite, 26 parts of furnace carbon black, 19 parts of quartz powder, diethyl phthalate DEP7 .1 part, 3.2 parts of cresyl diphenyl phosphate CDPP, 4.8 parts of antimony trioxide, 5.8 parts of red phosphorus capsule, 7.5 parts of peroxide curing system, 0.5 parts of anti-aging agent D-500, 1.6 parts of anti-aging agent SP; The ethylene-propylene ratio of EPDM rubber is 65:35, and the peroxide curing system includes by weight percentage: 80wt% di-tert-butyl peroxide, 10wt% N, N'-m-phenylene bismaleimide , 5wt% sodium butynedate, 5wt% sulfur p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stretch-proof wear-resistant oil-resistant modified cable material which is prepared from the following raw materials in parts by weight: 8-12 parts of chloroprene rubber, 25-28 parts of hydrogenated butadiene-acrylonitrile rubber, 70-73 parts of an ethylene propylene diene monomer, 17-20 parts of melamine formaldehyde resin, 13-16 parts of pre-treated plant powder, 8-11 parts of aluminum borate crystal whiskers, 2-5 parts of titanium nitride, 4-8 parts of aluminum oxide, 27-30 parts of calcite, 24-27 parts of furnace black, 18-21 parts of quartz powder, 6-8 parts of diethyl phthalate DEP, 3-4 parts of cresyl diphenyl phosphate CDPP, 3.4-5.3 parts of antimonous oxide, 5.3-6.2 parts of red phosphorus capsules, 6-8 parts of a peroxide vulcanization system, 0.4-0.8 part of an antiager D-50 and 1.2-1.8 parts of an antiager SP. The invention further discloses a preparation method of the stretch-proof wear-resistant modified cable material.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a stretch-resistant, wear-resistant, oil-resistant modified cable material and a preparation method thereof. Background technique [0002] In recent years, with the growth of the national economy and the development of the cable industry, the use of cables in my country is increasing, and cables are often subject to friction during use, which puts forward requirements for improved wear resistance of cable materials for protecting cables. Cable materials for protecting cables are generally made of rubber materials, which are non-polar substances. According to the principle of similar compatibility, cable materials are often easily dissolved in oil, which is not conducive to the use of cable materials in oil-filled environments. The cable needs to be erected in the sky. At this time, the cable material is required to be able to overcome the gravity of itself and the cable c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L15/00C08L11/00C08L61/28C08L97/02C08K13/04C08K7/08C08K3/28C08K3/22C08K3/26C08K3/04C08K3/36C08K5/12C08K5/526C08K3/02H01B3/28
CPCC08L23/16C08L2201/02C08L2201/08C08L2203/202C08L2205/035H01B3/28C08L15/00C08L11/00C08L61/28C08L97/02C08K13/04C08K7/08C08K3/28C08K2003/2227C08K3/346C08K3/04C08K3/36C08K5/12C08K5/523C08K3/2279C08K2003/026
Inventor 李正祥刁宏明王赵兰刘琴
Owner ANHUI LAND GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products