Modified environmental protection plastic with high ductility, impact resistance and oxidation resistance

An environmentally friendly plastic and ductility technology, applied in the field of plastics, can solve the problems of large consumption of agricultural products, low tensile strength, high brittleness, etc., to improve ductility, improve tensile performance and impact resistance, and improve wear resistance The effect of tear resistance

Active Publication Date: 2014-12-24
珠海市安迪尔生物科技有限公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, the research and development direction of degradable plastics has mainly focused on using starchy agricultural products such as corn and soybeans as the main raw materials to make completely biodegradable plastic materials with high agricultural product content. However, this material is brittle, not resistant to water, Low tensile strength and other disadvantages, and the consumption of agricultural products is also relatively large, and extensive production and use is by no means beneficial to the current food security problems of human society

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The present invention proposes a highly ductile, impact-resistant, oxidation-resistant, modified environmental-friendly plastic. Its raw materials include, by weight, 50 parts of polybutylene succinate PBS, 30 parts of poly-β-hydroxybutyrate PHB, peanuts 25 parts of protein powder, 2.5 parts of potassium titanate fiber, 13 parts of coconut fiber, 1.2 parts of silane coupling agent KH570, 3 parts of sodium sorbate, 1.1 parts of ethyl p-hydroxybenzoate, 1.4 parts of dioctyl phthalate DOP , 1.6 parts of zinc stearate, 5 parts of acetate starch, 15 parts of talc powder, 11 parts of wollastonite powder, 5 parts of calcite powder, 7 parts of sepiolite, 1.4 parts of tert-butyl hydroquinone TBHQ, 2,6 - 1.4 parts of di-tert-butyl-4-methylphenol BHT;

[0013] During the preparation process, the silane coupling agent KH570 was added to the potassium titanate fiber and stirred at a stirring speed of 27rpm for 8 minutes, then coconut fiber was added and stirred at a stirring speed o...

Embodiment 2

[0015] The present invention proposes a highly ductile, impact-resistant and oxidation-resistant modified environmentally-friendly plastic, whose raw materials include, by weight, 45 parts of polybutylene succinate PBS, 35 parts of poly-β-hydroxybutyrate PHB, peanut protein 20 parts of powder, 3 parts of potassium titanate fiber, 14 parts of coconut fiber, 1.7 parts of silane coupling agent KH570, 2 parts of sodium sorbate, 1.6 parts of ethyl p-hydroxybenzoate, 1.5 parts of dioctyl phthalate DOP, Zinc stearate 1.4 parts, acetate starch 3 parts, talc powder 18 parts, wollastonite powder 7 parts, calcite powder 9 parts, sepiolite 11 parts, tert-butylhydroquinone TBHQ 1 part, 2,6- 1 part of di-tert-butyl-4-methylphenol BHT;

[0016] During the preparation process, the silane coupling agent KH570 was added to the potassium titanate fiber and stirred at a stirring speed of 24rpm for 9min, then coconut fiber was added and stirred at a stirring speed of 25rpm for 11min, then peanut p...

Embodiment 3

[0018] The invention proposes a high ductility, impact resistance, oxidation resistance and modified environment-friendly plastics, the raw materials of which include by weight: polybutylene succinate PBS, poly-β-hydroxybutyrate PHB 31 parts, peanut protein powder 24 parts, potassium titanate fiber 2.7 parts, coconut fiber 15 parts, silane coupling agent KH570 1.3 parts, sodium sorbate 2.7 parts, ethyl p-hydroxybenzoate 1.2 parts, dioctyl phthalate DOP 1.45 parts, hard 1.5 parts of zinc fatty acid, 4.5 parts of acetate starch, 16 parts of talc powder, 10 parts of wollastonite powder, 6 parts of calcite powder, 8 parts of sepiolite, 1.3 parts of tert-butyl hydroquinone TBHQ, 2,6-di 1.1 parts of tert-butyl-4-methylphenol BHT.

[0019]During the preparation process, the silane coupling agent KH570 was added to the potassium titanate fiber and stirred at a stirring speed of 30 rpm for 5 minutes, then coconut fiber was added and stirred at a stirring speed of 32 rpm for 7 minutes, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses modified environmental protection plastic with high ductility, impact resistance and oxidation resistance. The modified environmental protection plastic comprises the following raw materials in parts by weight: 45-50 parts of poly butylenes succinate (PBS), 30-35 parts of poly-beta-hydroxybutyric acid (PHB), 20-25 parts of peanut protein powder, 2.5-3 parts of potassium titanate fiber, 12-15 parts of coconut fiber, 1.2-1.7 parts of a silane coupling agent KH570, 2-3 parts of sodium sorbate, 1.1-1.6 parts of ethyl p-hydroxybenzoate, 1.4-1.6 parts of dioctyl phthalate (DOP), 1,2-1.6 parts of zinc stearate, 3-5 parts of starch acetate, 15-18 parts of talcum powder, 7-11 parts of wollastonite powder, 5-9 parts of calcite powder, 7-11 parts of sepiolite,1-1.4 parts of tertiary butyl hydroquinone (TBHQ) and 1-1.4 parts of 2,6-di-tert-butyl-4-methylphenol (BHT). The modified environmental protection plastic disclosed by the invention can be decomposed by microorganisms and is high in ductility and good in impact resistance and oxidation resistance.

Description

technical field [0001] The invention relates to the technical field of plastics, in particular to a modified environmental protection plastic with high ductility, impact resistance and oxidation resistance. Background technique [0002] As a non-renewable resource, petroleum is increasingly consumed. At the same time, the non-degradability of petroleum-based plastics has also caused serious pollution to the environment. According to statistics, waste plastics account for 7-8% of the total waste in developed countries. The development of degradable plastics can reduce white pollution and have significant economic and social benefits. In recent years, the research and development direction of degradable plastics has mainly focused on using starchy agricultural products such as corn and soybeans as the main raw materials to make completely biodegradable plastic materials with high agricultural product content. However, this material is brittle, not resistant to water, Low tens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L67/04C08L89/00C08L97/02C08L3/06C08K13/06C08K9/06C08K7/08C08K5/12C08K5/098C08K3/34C08K3/26C08K5/101C08K5/13
Inventor 高忠青
Owner 珠海市安迪尔生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap