A low-shrinkage medium-temperature curing high-efficiency flame-retardant unsaturated polyester glass steel plate and its preparation method

An unsaturated, low-shrinkage technology, applied in the field of low-shrinkage, medium-temperature curing, high-efficiency flame-retardant unsaturated polyester FRP sheet and its preparation, can solve the highest level of flame-retardant effect, flame-retardant performance limitations, and environmental protection Demand and other issues, to achieve the effect of ensuring life, health and safety, low curing shrinkage, and reducing smoke toxicity

Active Publication Date: 2016-08-17
扬州万盛实业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the wider application of FRP materials in aviation, transportation, electrical appliances and other fields, the current products basically cannot reach the highest level of flame retardant effect, and its flame retardant performance has become the key reason restricting its development.
Moreover, the use of traditional halogen-based flame retardants does not meet the needs of environmental protection. The market size and application fields of halogen-based flame retardants have long ranked first among all types of flame retardants. However, when halogen-based flame retardants burn, they generate more smoke, Corrosive gases and certain toxic products will cause products to be abandoned because they fail to meet the requirements of green environmental protection. With the development of the economy, the market urgently needs products with good appearance, good flame retardant effect, low pollution, and high performance-price ratio. FRP sheet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-shrinkage medium-temperature curing high-efficiency flame-retardant unsaturated polyester glass steel plate and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A low-shrinkage medium-temperature curing high-efficiency flame-retardant unsaturated polyester fiberglass plate, which is made of the following raw materials in weight ratio:

[0023] Bisphenol A type unsaturated polyester resin 50 parts

[0024] Polyvinyl acetate and polymethyl methacrylate block copolymer 20 parts

[0025] 1 part cobalt isooctanoate

[0026] Dibenzoyl peroxide 0.5 parts

[0027] 2 parts methyl ethyl ketone peroxide

[0028] 0.15 parts of light magnesium oxide

[0029] Dimethyl methylphosphonate flame retardant 8 parts

[0030] Aluminum hydroxide 100 parts

[0031] Zinc stearate 2 parts

[0032] 100 parts glass fiber

[0033] The preparation method is:

[0034] (1) First add bisphenol A type unsaturated polyester resin, polyvinyl acetate and polymethyl methacrylate block copolymer, and cobalt isooctanoate in the above ratio into the beater, and stir rapidly for 3 minutes;

[0035] (2) Add dibenzoyl peroxide, methyl ethyl ketone peroxide, and ...

Embodiment 2

[0038] A low-shrinkage medium-temperature curing high-efficiency flame-retardant unsaturated polyester fiberglass plate, which is made of the following raw materials in weight ratio:

[0039] Bisphenol A type unsaturated polyester resin 52 parts

[0040] Polyvinyl acetate and polymethyl methacrylate block copolymer 22 parts

[0041] 2 parts cobalt isooctanoate

[0042] Dibenzoyl peroxide 0.8 parts

[0043] 3 parts methyl ethyl ketone peroxide

[0044] 0.2 parts of light magnesium oxide

[0045] Dimethyl methylphosphonate flame retardant 10 parts

[0046] Aluminum hydroxide 110 parts

[0047] Zinc stearate 2 parts

[0048] Glass fiber 110 parts

[0049] Preparation:

[0050] (1) First add bisphenol A type unsaturated polyester resin, polyvinyl acetate and polymethyl methacrylate block copolymer, and cobalt isooctanoate in the above ratio into the beater, and stir rapidly for 3 minutes;

[0051] (2) Add dibenzoyl peroxide, methyl ethyl ketone peroxide, and light magnesi...

Embodiment 3

[0054] A low-shrinkage medium-temperature curing high-efficiency flame-retardant unsaturated polyester fiberglass plate, which is made of the following raw materials in weight ratio:

[0055] Bisphenol A type unsaturated polyester resin 54 parts

[0056] Polyvinyl acetate and polymethyl methacrylate block copolymer 24 parts

[0057] 2 parts cobalt isooctanoate

[0058] Dibenzoyl peroxide 1.1 parts

[0059] 4 parts methyl ethyl ketone peroxide

[0060] 0.3 parts of light magnesium oxide

[0061] Dimethyl methylphosphonate flame retardant 13 parts

[0062]Aluminum hydroxide 110 parts

[0063] 3 parts zinc stearate

[0064] 120 parts glass fiber

[0065] Preparation:

[0066] (1) First add bisphenol A type unsaturated polyester resin, polyvinyl acetate and polymethyl methacrylate block copolymer, and cobalt isooctanoate in the above ratio into the beater, and stir rapidly for 3 minutes;

[0067] (2) Add dibenzoyl peroxide, methyl ethyl ketone peroxide, and light magnesiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
cure shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-shrinkage medium-temperature curing high-efficiency flame-retardant unsaturated polyester glass steel plate and a preparation method thereof. It is prepared from the following components, which are calculated in parts by weight: unsaturated polyester 50-60 parts of resin, 20-30 parts of low shrinkage additive, 1-3 parts of accelerator, 0.5-2 parts of initiator, 2-5 parts of medium temperature curing agent, 0.1-0.5 parts of thickener, dimethyl phosphonate 8-15 parts of ester flame retardant, 100-130 parts of aluminum hydroxide, 2-3 parts of mold release agent, and 100-150 parts of glass fiber. The present invention improves the degree of curing of the product, enhances the bending strength, improves the flexibility, and simultaneously reduces the Sheet styrene residue.

Description

technical field [0001] This aspect relates to the technical field of polymer materials, in particular to a low-shrinkage medium-temperature curing high-efficiency flame-retardant unsaturated polyester glass steel plate and a preparation method thereof. Background technique [0002] Fiberglass reinforced plastic (FRP) is also known as SMC, that is, fiber reinforced plastics, generally refers to glass fiber reinforced unsaturated polyester, epoxy resin and phenolic resin matrix, FRP products have light weight, high strength, corrosion resistance, good electrical properties, good thermal properties , Good designability, good resistance to the atmosphere, water, and general concentrations of acids, alkalis, salts, and various oils and solvents, used in aviation, rockets, spacecraft, high-pressure vessels, and other needs In the application of products that reduce their own weight, they have excellent results. They can be used to replace aluminum alloy and stainless steel in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/06C08L53/00C08K13/04C08K7/14C08K5/5333
Inventor 高山俊朱祥楼王邦延
Owner 扬州万盛实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com