Preparation method for rubber for automobile exhaust pipe lifting ring

An automobile exhaust and rubber technology, which is applied in the field of rubber preparation for automobile exhaust pipe suspension rings, can solve the problems of poor high temperature resistance of automobile exhaust pipe suspension rings, etc., and achieve the effects of improving aging resistance and heat resistance

Inactive Publication Date: 2015-03-04
LIUZHOU YINGHANG AUTO PARTS
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem solved by the present invention is to provide a method for preparing rubber for automobile exhaust pipe suspension rings, which can be used to prepare automobile exhaust pipe suspension rings to solve the problem of poor high temperature resistance of automobile exhaust pipe suspension rings produced in the prior art. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The preparation method of the rubber used for the suspension ring of the automobile exhaust pipe adopts the following preparation raw materials: EPDM rubber 6.0kg; chlorosulfonated polyethylene rubber 4.0kg; Zhongchao carbon black N200 1.0kg; general furnace black N660 2.5kg; indirect method oxidation Zinc 0.5kg; tetramethylthiuram disulfide 0.3kg; tetraethylthiuram disulfide 0.1kg; 2-mercaptobenzimidazole 0.2kg; zinc stearate 0.1kg; Thiodibenzothiazole 0.5kg; Trimeric thiocyanate 0.05kg; Paraffin oil 1.5kg; Magnesium strong powder 0.5kg; Sulfur 0.02kg;

[0015] A. Put EPDM rubber and chlorosulfonated polyethylene rubber into an internal mixer, and masticate at 80°C for 25 minutes;

[0016] B. After the mastication in step A is completed, add China Super Carbon Black N200, General Furnace Black N660, indirect method zinc oxide, 2-mercaptobenzimidazole, 2,2'-dithiobis Benzothiazole, paraffin oil and magnesium powder, banburying at 75°C for 10 minutes, after banburying, ...

Embodiment 2

[0020] The preparation method of the rubber used for the automobile exhaust pipe suspension ring adopts the following preparation raw materials: EPDM rubber 6.0kg; chlorosulfonated polyethylene rubber 4.0kg; Zhongchao carbon black N200 1.5kg; general furnace black N660 2.0kg; indirect method oxidation Zinc 1.0kg; tetramethylthiuram disulfide 0.2kg; tetraethylthiuram disulfide 0.2kg; 2-mercaptobenzimidazole 0.1kg; zinc stearate 0.03kg; Thiodibenzothiazole 0.3kg; Trimeric thiocyanate 0.08kg; Paraffin oil 1.0kg; Magnesium strong powder 1.0kg; Sulfur 0.01kg;

[0021] A. Put EPDM rubber and chlorosulfonated polyethylene rubber into an internal mixer, and masticate at 90°C for 10 minutes;

[0022] B. After the mastication in step A is completed, add China Super Carbon Black N200, General Furnace Black N660, indirect method zinc oxide, 2-mercaptobenzimidazole, 2,2'-dithiobis Benzothiazole, paraffin oil and magnesium powder, banburying at 85°C for 5 minutes, after banburying, control...

Embodiment 3

[0026] The preparation method of the rubber used for the automobile exhaust pipe suspension ring adopts the following preparation raw materials: EPDM rubber 6.0kg; chlorosulfonated polyethylene rubber 4.0kg; Zhongchao carbon black N200 1.2kg; general furnace black N660 2.2kg; indirect method oxidation Zinc 0.8kg; Tetramethylthiuram disulfide 0.25kg; Tetraethylthiuram disulfide 0.15kg; 2-thiol benzimidazole 0.15kg; Zinc stearate 0.2kg; Thiodibenzothiazole 0.4kg; Trimeric thiocyanate 0.06kg; Paraffin oil 1.4kg; Magnesium strong powder 0.7kg; Sulfur 0.015kg;

[0027] A. Put EPDM rubber and chlorosulfonated polyethylene rubber into an internal mixer, and masticate at 85°C for 20 minutes;

[0028] B. After the mastication in step A is completed, add China Super Carbon Black N200, General Furnace Black N660, indirect method zinc oxide, 2-mercaptobenzimidazole, 2,2'-dithiobis Benzothiazole, paraffin oil and magnesium powder, banburying at 80°C for 8 minutes, after banburying, contro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for rubber for an automobile exhaust pipe lifting ring and belongs to the technical field of rubber pipe products for an automobile. The preparation method comprises the following steps: EPDM and chlorosulfonated polyethylene rubber are put into an internal mixer for plastication, intermediate super carbon black N200, general furnace black N660, indirect zinc oxide, 2-thiol group benzimidazole, 2,2'-dithio-dibenzo thiazole, paraffin oil and strong magnesium powder are added, and mixing is performed to obtain a mixed material; the mixed material is put into vulcanization equipment, zinc diethyl dithiocarbamaate, zinc stearate, trithiocyanuric acid and sulphur are added, vulcanization is performed sequentially at four temperature intervals. Compared with the preparation method for rubber for the automobile exhaust pipe lifting ring in the prior art, the preparation method disclosed by the invention has the advantage that by using the synergistic effect of all raw materials, the heat resistance of the automobile exhaust pipe lifting ring is improved effectively and meanwhile the ageing resistance of the automobile exhaust pipe lifting ring is also improved when the raw materials are used for preparing the automobile exhaust pipe lifting ring.

Description

technical field [0001] The invention relates to the technical field of rubber hose products for automobiles, in particular to a method for preparing rubber for suspension rings of automobile exhaust pipes. Background technique [0002] In terms of the role of the automobile exhaust pipe on the automobile body, it plays the role of shock absorption and noise reduction, and prolongs the life of the exhaust muffler system. The main material of the exhaust pipe is stainless steel. For ordinary cars, because the exhaust gas of the car is under great pressure when it leaves the engine, the noise it produces may make people feel crazy. At this time, the main role of noise reduction is the exhaust pipe of the car. The device greatly reduces the noise of the car. The main function of the automobile exhaust pipe suspension ring is to fix the exhaust pipe to reduce the vibration generated by the exhaust pipe during movement and prevent the collision between the exhaust pipe and the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/34C08K13/02C08K3/04C08K3/22C08K5/40C08K5/37C08K5/098C08K5/47B29C35/02
CPCB29C35/02C08K2201/014C08L23/16C08L2201/08C08L2205/02C08L2205/03C08L23/34C08L91/06C08K13/02C08K3/04C08K2003/2296C08K5/098
Inventor 陈永亮
Owner LIUZHOU YINGHANG AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com