Modified desulfurization gypsum foam brick and preparation method thereof

A technology of desulfurized gypsum and foam bricks, applied in the field of building materials, can solve problems such as environmental pollution, occupation of land resources, inconvenience in production and life, etc., and achieve the effects of high strength, clean indoor environment, and low cost

Inactive Publication Date: 2015-03-11
HEFEI KANGLING HEALTH TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The chemical properties of waste glass are stable, which not only brings inconvenience to people's production and life, but also pollutes the environment, and the placement of waste glass takes up a lot of land resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Non-limiting examples of the present invention are as follows:

[0022] A modified desulfurized gypsum foam brick, prepared from the following components by weight (kg):

[0023] Waste glass 55, fly ash 4, modified desulfurized gypsum 25, light calcium carbonate 8, sodium glutamate 0.8, sodium lauryl sulfate 0.8, sodium alginate 0.8, hydroxypropyl guar gum 0.8, dodecyl Sodium alkylbenzene sulfonate 0.3, glycine 0.8, organosilicon quaternary ammonium salt 3, castor oil 4, peanut oil 3, water 55;

[0024] Among them, the modified desulfurized gypsum is made of the following raw materials in weight (kg):

[0025] Desulfurization gypsum 250, nonylphenol polyoxyethylene ether 0.3, talc 4, sorbic acid 1.5, sodium hexametaphosphate 3, sodium chloride 4, calcium bicarbonate 3, alumina 1.5, borax 3, water 25;

[0026] The preparation method of modified desulfurized gypsum:

[0027] Mix desulfurized gypsum with talcum powder, sodium hexametaphosphate, sodium chloride, calcium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a modified desulfurization gypsum foam brick which is characterized in that the foam brick is prepared from the following raw materials, by weight: 50-60 parts of waste glass, 3-5 parts of fly ash, 20-30 parts of modified desulfurization gypsum, 5-10 parts of light calcium carbonate, 0.5-1 parts of sodium glutamate, 0.5-1 parts of sodium dodecyl sulfate, 0.5-1 parts of sodium alginate, 0.5-1 parts of hydroxypropyl guar gum, 0.2-0.4 parts of sodium dodecyl benzene sulfonate, 0.5-1 parts of glycine, 2-4 parts of organosilicon quaternary ammonium salt, 3-5 parts of castor oil, 2-4 parts of peanut oil, and 50-60 parts of water. According to the invention, through formula and process improvements, the foam brick has the advantages of high strength, good water resistance, good thermal insulation, good antibacterial performance, and good mildew resistance. The foam brick is energy-saving and emission-reducing. Raw material sources are rich, and cost is low. The foam brick and the preparation method provide high social and economic benefits.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a modified desulfurized gypsum foam brick and a preparation method thereof. Background technique [0002] Foam brick is a kind of aerated concrete block. After using a foaming agent to physically foam through a foaming machine, the air bubbles are added to the slurry for mixing, pouring, and finally a foam brick with internal pores is obtained. Foam bricks are mainly used for non-load-bearing walls. They have the characteristics of low cost, light weight, and good thermal insulation effects. They have been widely used in industrial and civil buildings and are a wall material with good performance. [0003] Glass materials are indispensable and indispensable materials for people's daily life. The extensive use of glass also leads to the inevitable generation of a large amount of waste glass waste in daily production and life. The chemical properties of waste glass are stable, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B41/49
Inventor 张百庆韩立平
Owner HEFEI KANGLING HEALTH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap