Special treating agent for galvanizing surface chemical conversion and treating technique thereof

A technology of surface chemistry and chemical conversion, which is applied in the coating process of metal materials, etc., can solve the problems of unstable conversion liquid solution, inability to achieve long-term anti-corrosion, difficulty in large-scale construction, etc., and achieve broad industrial application value and low cost , The effect of convenient construction

Active Publication Date: 2015-04-08
STATE GRID CORP OF CHINA +1
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods have their own shortcomings, such as poor corrosion resistance of molybdate passivation film, better corrosion resistance of titanium salt and silicate conversion film, but the conversion solution solution is unstable, and can not achieve the purpose of long-term anticorrosion
Generally, this kind of process often faces problems such as high cost and difficulty in large-scale construction. Therefore, it is urgent to find a new chemical conversion treatment technology with low protection cost, convenient construction and good protection effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Below in conjunction with embodiment, the present invention is described in further detail:

[0037] In this embodiment, the galvanized Q235 steel is used as the substrate, and chemical transformation is carried out on its surface, including the following steps:

[0038] Step 1: prepare pretreatment agent, its composition is as follows:

[0039] Na 2 CO 3 3g / L, NaH 2 PO 4 8g / L, NaHPO 4 8g / L, sodium pyrophosphate 2.6g / L, copper sulfate 0.8g / L, copper nitrate 0.7g / L, nickel chloride 0.7g / L, nickel nitrate 0.8g / L, titanium oxysulfate 2g / L, titanium fluoride Potassium acid potassium 2g / L, after the solution is prepared, adjust the pH to 8.5 with NaOH solution.

[0040] Step 2: Pretreat the surface of the alloy with a pretreatment agent: soak the alloy in the pretreatment agent for 5 minutes at room temperature, then take it out and wash the residual solution on the surface with tap water at room temperature;

[0041] Step 3: Prepare chemical conversion treatment ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special treating agent for galvanizing surface chemical conversion and a treating technique thereof, belonging to the field of surface protection of transmission and transformer equipment components. The conversion treating method mainly comprises the steps of pretreatment, water washing, chemical conversion, water washing, natural drying and the like. The pretreatment agent is composed of Na2CO3, NaH2PO4, NaHPO4, sodium pyrophosphate, copper salt, nickel salt and titanium salt. In the treatment process, the conversion agent is composed of H3PO4 and ZnO, the corrosion inhibitor is one or both of thiocarbamide and hexamethylenetetramine, the complexing agent is composed of one or more of citric acid, tartaric acid and monobutyric acid, the surfactant is composed of one or more of OS-15, OP-10 and sodium dodecyl benzene sulfonate, and the accelerator is composed of one or more of sodium nitrate, sodium nitrate, hydrogen peroxide, potassium permanganate and potassium chlorate. The galvanizing substrate surface treated by the technique is a compact corrosion-resistant film with insulation resistance. The treating agent and treating technique can effectively enhance the corrosion resistance of the material and enhance the corrosion resistance and service life of the transmission and transformer equipment metal components.

Description

technical field [0001] The invention belongs to the technical field of corrosion protection, and in particular relates to a chemical conversion treatment agent for galvanized components of power transmission and transformation equipment and a treatment process thereof, in particular to a special treatment agent for chemical conversion of galvanized surfaces and a treatment process thereof. Background technique [0002] Steel is the most widely used metal in industry and daily life. However, steel is a metal that is easily corroded, and people generally use galvanizing to improve the ability to resist atmospheric corrosion. This kind of galvanized steel is the most widely used in industry and daily life. With the rapid development of my country's economy, the demand for electricity continues to increase, especially the continuous application of UHV technology, and the long-distance transmission of electricity plays an increasingly important role. function, using a large amoun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/07
CPCC23C22/17C23C22/80
Inventor 朱义东于博宇郑福民杨延格迟丹一张春艳李斌于宝兴张涛胡大伟王福会
Owner STATE GRID CORP OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products