Cast iron evanescent mode paint and preparation method thereof
A technology of lost foam and coating, applied in casting molding equipment, coating, mold and other directions, can solve the problems of low cost performance of coatings, high scrap rate, many defects, etc., and achieve convenient construction, good thixotropy, and excellent performance. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0015] Example 1:
[0016] The cast iron lost foam coating is composed of the following raw materials: activated alumina 2kg, iron oxide 0.5 kg, silica 13 kg, bauxite 12 kg, quartz sand 20 kg, zircon powder 4 kg, silicon carbide 1.5 kg, potassium feldspar 1.5 kg, silica sol 3 kg, bentonite 1.5 kg, attapulgite 1.5 kg, sub-nano lithium magnesium silicate 0.25 kg, sodium pyrophosphate 0.03 kg, talc 1 kg, white latex 4 kg, xanthan gum 0.5 kg, BY Binder 1 kg, CMC 1.5 kg, sodium benzoate 0.02 kg, water 33.46 kg.
[0017] It is prepared according to the following steps: ①Bentonite, attapulgite, xanthan gum and CMC are hydrolyzed separately; ②Mixed xanthan gum and CMC after hydration, and sodium benzoate is added; ③Sub-nano lithium magnesium silicate and sodium pyrophosphate are mixed Then, add water to make a saturated solution; ④Mix the bentonite, attapulgite, the materials in ② and the rest of the water that have been made in the water, add BY binder, white latex and silica sol, and mi...
Example Embodiment
[0018] Example 2:
[0019] Cast iron lost foam coating is composed of the following raw materials: activated alumina 1.5 kg, iron oxide 1 kg, silica 5 kg, bauxite 3 kg, quartz sand 30 kg, zircon powder 5 kg, silicon carbide 1 kg, potassium feldspar 1 kg, Silica sol 2kg, bentonite 1kg, attapulgite 1kg, sub-nanolithium magnesium silicate 0.2kg, sodium pyrophosphate 0.02kg, talc 2kg, white latex 3kg, xanthan gum 0.3kg, BY binder 1.5kg, CMC1kg, Sodium benzoate 0.02kg, water 40.46kg.
[0020] The preparation method is the same as in Example 1.
Example Embodiment
[0021] Example 3:
[0022] Cast iron lost foam coating is composed of the following raw materials: activated alumina 5kg, iron oxide 3kg, silica 15kg, bauxite 2kg, quartz sand 10kg, zircon powder 8kg, silicon carbide 5kg, potassium feldspar 2kg, silica sol 0.1kg , Bentonite 1kg, attapulgite 1kg, sub-nanolithium magnesium silicate 2kg, sodium pyrophosphate 0.4kg, talc 3kg, white latex 1.5kg, xanthan gum 3kg, BY binder 0.1kg, CMC 0.1kg, sodium benzoate 0.06kg, 37.74kg of water.
[0023] The preparation method is the same as in Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap