A technology of ABS material and ABS resin, applied in the field of antibacterial and flame retardant ABS material and its preparation, can solve the problems such as the decrease of toughness of ABS resin, and achieve the effects of preventing discoloration, reducing energy consumption and increasing fluidity

Inactive Publication Date: 2015-07-01
ORINKO NEW MATERIAL CO LTD
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the increasing amount of flame retardant added, the toughness of ABS resin decreased significantly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] (2) Mix 70 parts of ABS resin, 1.0 part of antibacterial masterbatch, 1.0 part of antioxidant 2,6-tertiary butyl-4-methylphenol, and 1.2 parts of lubricant pentaerythritol stearate, and then add it to In the twin-screw extruder, extrude after melting, cool, air-dry, and pelletize to obtain antibacterial ABS masterbatch;

[0042] (3) Add 19 parts of antibacterial ABS masterbatch and flame retardant decabromodiphenylethane, 5.0 parts of coordinated flame retardant hydrotalcite, 0.2 parts of auxiliary flame retardant polytetrafluoroethylene, and 0.2 parts of heat stabilizer zinc stearate Add 1.0 parts of compatibilizer maleic anhydride to the twin-screw extruder again, extrude after melting, cool, air-dry, and pelletize to obtain antibacterial and flame-retardant ABS materials;

[0043] (4) Put the antibacterial and flame retardant ABS particles into the injection molding machine, and perform injection molding at 200-210°C to obtain injection molding grade antibacterial an...

Embodiment 2

[0047] Flame retardant bromotriazine 10 parts

[0048] Brominated polystyrene 5 parts

[0049] Coordinating flame retardant hydrotalcite 3.0 parts

[0050] Auxiliary flame retardant polytetrafluoroethylene 0.3 parts

[0051] Heat stabilizer calcium stearate 0.4 parts

[0052] Antibacterial masterbatch 0.7 parts

[0053] 0.5 part of compatibilizer maleic anhydride

[0054] ABS grafted maleic anhydride 0.5 parts

[0055] Antioxidant 0.8 parts

[0056] Lubricant N, N- already extended bis stearamide 1 part

[0057] The preparation method is the same as in Example 1.

[0058] Example 3:

Embodiment 3

[0060] Flame retardant Tetrabromobisphenol A 12 parts

[0061] Coordinating flame retardant hydrotalcite 2.0 parts

[0062] Auxiliary flame retardant polytetrafluoroethylene 0.3 parts

[0063] Heat stabilizer magnesium stearate 0.2 parts

[0064] Antibacterial masterbatch 0.5 parts

[0065] Compatibilizer ABS grafted maleic anhydride 0.7 parts

[0066] Antioxidant 1.0 parts

[0067] Lubricant oxidized polyethylene wax 0.4 parts

[0068] Amide wax 0.5

[0069] The preparation method is the same as in Example 1.

[0070] Example 4:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial flame-retardant ABS material and a preparation method thereof. The antibacterial flame-retardant ABS material is prepared from ABS resin, a flame-retarding agent, a coordinative flame-retarding agent, an auxiliary flame-retarding agent, a thermal stabilizer, an antibacterial master batch, a compatilizer, an antioxidant and a lubricating agent in parts by weight, wherein the antibacterial master batch is prepared from ABS and at least one of a silver ion type antibacterial agent, zinc oxide and copper oxide by a mass ratio of 10 to 1. According to the ABS material disclosed by the invention, the silver ion type antibacterial agent or the zinc oxide or the copper oxide and the ABS are used for preparing the antibacterial master batch by the mass ratio of 10 to 1, so that the silver ion type antibacterial agent or the zinc oxide or the copper oxide is effectively uniformly dispersed in the ABS resin in order to improve the antibacterial efficiency and achieve a better antibacterial effect than an antibacterial agent which is used independently; and color changes of antibacterial ABS plastic can be effectively prevented, and the antibacterial properties of the antibacterial ABS plastic can be improved.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an antibacterial and flame-retardant ABS material and a preparation method thereof. Background technique [0002] Acrylonitrile-butadiene-styrene resin (abbreviated as ABS) is an important general-purpose synthetic resin. As a joint between general-purpose synthetic resin and engineering plastics, it has special importance. ABS resin is composed of more than 50% styrene and variable amounts of butadiene and acrylonitrile. Among them, styrene provides hardness and ease of processing, acrylonitrile provides chemical resistance and thermal stability, and butadiene provides toughness and impact strength. Therefore, ABS resin has the characteristics of high impact strength, good heat resistance and low temperature resistance, and is easy to process. It is widely used in the fields of electronic appliances, auto parts, stationery, daily necessities and industrial parts. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08K13/02C08K3/22C08K5/3492C08K3/26C08K5/098C08K5/20C08J3/22
Inventor 文听雷李荣群任东方杨亚娣黄骎
Owner ORINKO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap