Environmental-protection type multi-element collaborative marine anti-fouling coating

A marine anti-fouling and anti-fouling coating technology, which is applied in the direction of anti-fouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problems of single anti-fouling methods and harmful environment, and achieve enhanced anti-fouling effect , long-lasting antifouling effect, environmentally friendly effect

Active Publication Date: 2015-07-08
LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the shortcomings of the existing antifouling coatings with single antifouling methods and harmful to the environment, and provide a multi-component synergistic marine antifouling coating with environmental friendliness, low surface energy, stable self-polishing, and long-lasting antifouling effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental-protection type multi-element collaborative marine anti-fouling coating
  • Environmental-protection type multi-element collaborative marine anti-fouling coating
  • Environmental-protection type multi-element collaborative marine anti-fouling coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Mix 30 parts of antifouling coating matrix resin containing antifouling active groups, 1 part of wetting and dispersing agent BYK163 and 26 parts of mixed organic solvent (dimethyl sulfoxide: ethylene glycol monomethyl ether: butyl acetate = 1:1 :1) Add to the dispersion tank, fully disperse and add 10 parts of copper pyrithione, 30 parts of pigments and fillers (6 parts of polytetrafluoroethylene, 8 parts of iron oxide red, 8 parts of zinc oxide, 8 parts of barium sulfate), 0.3 1 part of leveling agent BYK300, 0.3 part of defoamer BYK052, 2.4 parts of anti-settling agent (among them, 0.4 part of BYK410, 1 part of organic bentonite, 1 part of talcum powder), high-speed dispersion and grinding until the coating fineness is less than 50 μm, to obtain an environmentally friendly Multivariate synergistic marine antifouling coatings. Final packaging. In this example, the environment-friendly multi-component synergistic marine antifouling coating, the general performance of ...

Embodiment 2

[0036] Add 30 parts of antifouling coating matrix resin containing antifouling active groups, 1 part of wetting and dispersing agent BYK163 and 26 parts of mixed organic solvent into the dispersion tank, fully disperse and add 5 parts of copper pyrithione and 5 parts of pyridine sulfide in sequence Zinc ketone, 30 parts of pigments and fillers (5 parts of polytetrafluoroethylene, 8 parts of red iron oxide, 8 parts of zinc oxide, 9 parts of barium sulfate), 0.3 parts of leveling agent Levaslip435, 0.3 parts of defoamer BYK052, 2.4 parts of anti-settling (among them, 0.4 parts of BYK410, 1 part of organic bentonite, and 1 part of talcum powder), high-speed dispersion and grinding until the coating fineness is less than 50 μm, to obtain an environmentally friendly multi-component synergistic marine antifouling coating. Final packaging. In this example, the environment-friendly multi-component synergistic marine antifouling coating, the general performance of spraying on the tinpl...

Embodiment 3

[0038] Add 40 parts of antifouling coating base resin containing antifouling active groups, 0.8 parts of wetting and dispersing agent BYK163 and 22 parts of mixed organic solvent into the dispersion tank, fully disperse and add 4 parts of copper pyrithione and 3.5 parts of pyrithione in sequence Zinc ketone, 27 parts of pigments and fillers (5 parts of polytetrafluoroethylene, 8 parts of red iron oxide, 7 parts of zinc oxide, 7 parts of barium sulfate), 0.3 parts of leveling agent Levaslip435, 0.3 parts of defoamer BYK052, 2.1 parts of anti-settling (among them, 0.3 parts of BYK410, 0.9 parts of organic bentonite, and 0.9 parts of talcum powder), high-speed dispersion and grinding until the coating fineness is less than 50 μm, to obtain an environmentally friendly multi-component synergistic marine antifouling coating. Final packaging. In this example, the environment-friendly multi-component synergistic marine antifouling coating, the general performance of spraying on the ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface energyaaaaaaaaaa
surface energyaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environmental-protection type multi-element collaborative marine anti-fouling coating. The coating is composed of anti-fouling coating matrix resin containing an anti-fouling active group, a wetting and dispersing agent, a mixed organic solvent, a non-toxic anti-fouling agent, a pigment filler, a levelling agent, a defoaming agent and an anti-settling agent. The coating is non-toxic, does not pollute the environment, and is mainly applied in ship fouling resistance.

Description

technical field [0001] The invention relates to an environment-friendly marine antifouling paint, in particular to a non-toxic, long-acting, broad-spectrum environment-friendly multi-component synergistic marine antifouling paint, which is used for the antifouling of ocean-going ships. Background technique [0002] my country is vigorously developing the marine industry. Marine biofouling has a great negative impact on the life and service performance of marine equipment. Sea organisms adhere to increase the frictional resistance of ships, which affects the speed of ships and increases energy consumption. At the same time, marine biofouling can accelerate the aging of the paint film and aggravate the corrosion of the hull, which is extremely harmful. The most effective way to prevent biofouling is to apply antifouling coatings, so various antifouling coatings for ships have emerged as the times require. Self-polishing antifouling coatings containing organotins (TBTs) have...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D133/08C09D5/16C09D7/12C08F220/14C08F220/18C08F220/38C08F220/06C08F8/44
Inventor 周峰裴小维于波胡海媛刘维民
Owner LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap