Production method of moisture-proof low-aldehyde urea-formaldehyde resin adhesive

A technology of low-aldehyde urea-formaldehyde resin and urea-formaldehyde resin, which is applied in the direction of adhesives, adhesive additives, aldehyde/ketone condensation polymer adhesives, etc., can solve the problems of poor water resistance of wood-based panels, warpage and deformation of wood-based panels, and achieve fine particle size, Effects of improving water resistance and enhancing adhesive strength

Active Publication Date: 2017-12-15
香河天亚木业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor water resistance of wood-based panels made of various straws, nut shells and other raw materials, the panels warp and deform due to differences in expansion force after moisture absorption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of moisture-proof low-aldehyde urea-formaldehyde resin adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The production of urea-formaldehyde resin comprises the steps:

[0024] Pre-polymerization stage: put the formaldehyde aqueous solution with a weight concentration of 37% into the reaction kettle, start the agitator, add formic acid to adjust the pH of the solution to 2-2.5 when the temperature is stable at 49-55°C, add the first batch of urea to react with formaldehyde, Make the molar ratio of formaldehyde and urea F / U =10; react at 55-60°C for 35 minutes;

[0025] Polymerization stage: after the reaction in the prepolymerization stage, immediately adjust the pH of the reaction solution to 8.1-8.5 with aqueous sodium hydroxide solution, raise the temperature to 81-85°C, and add the first batch of melamine. The amount of the first batch of melamine accounts for 10% of the total melamine weight. % ~ 30%, after stirring evenly, add the second batch of urea to make formaldehyde and urea F / U = 3, and react for 35 minutes;

[0026] Post-polymerization stage: After the react...

Embodiment 2

[0028] Take 60 parts of the modified urea-formaldehyde resin obtained in Example 1, take 10 parts of OPE moisture-proof agent, stir and mix evenly, add 15 parts of calcium carbonate, grind with a three-roller mill for 30 minutes, and obtain a moisture-proof and low-formaldehyde urea-formaldehyde resin glue.

Embodiment 3

[0030] Take 65 parts of the modified urea-formaldehyde resin obtained in Example 1, take 11 parts of OPE moisture-proof agent, stir and mix evenly, add 16 parts of kaolin, grind with a three-roll mill for 30 minutes, and obtain a moisture-proof and low-formaldehyde urea-formaldehyde resin glue.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a moisture-proof low-formaldehyde urea-formaldehyde resin adhesive. The raw materials and parts by weight include: 60-80 parts of modified urea-formaldehyde resin, 10-14 parts of OPE moisture-proof agent, and 15-20 parts of filler; the production method is as follows: First, prepare urea-formaldehyde resin, formaldehyde is one-time feeding, and urea is feeding in three times; the production of urea-formaldehyde resin is divided into three stages: pre-polymerization, polymerization and late polymerization. agent. After the late stage of polymerization, add OPE moisture-proof agent, mix and stir evenly, add filler, and grind with a three-roll mill for 30 minutes to obtain a moisture-proof low-formaldehyde urea-formaldehyde resin adhesive. The moisture-proof and low-formaldehyde urea-formaldehyde resin of the invention has excellent water resistance, good moisture-proof performance and low formaldehyde residual content, and solves a difficult problem in the particleboard and density board industry today.

Description

technical field [0001] The invention relates to a urea-formaldehyde resin adhesive, in particular to a production method of a urea-formaldehyde resin adhesive with good moisture-proof performance and low aldehyde. Background technique [0002] With the rapid development of China's economy and the improvement of people's living standards, the requirements for home decoration are also constantly increasing. Because of its natural and beautiful texture and good texture, wooden floor has become the first choice material for home floor decoration. In order to save wood and protect forests, the state encourages the use of the three residues in forestry production, sawdust, shavings, bark, sanding powder, and branch materials produced in wood processing, bamboo processing, and wood-based panel production, as well as those produced after harvesting crops. All kinds of straw, nut shells, etc. are used as raw materials to produce wood-based panels. The wood-based panels produced fro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J161/32C09J11/08C09J11/04C08G12/40
Inventor 马云周子茜周帆陈宏玲秦文雄
Owner 香河天亚木业有限公司