Nano calcium carbonate /wood composite material production method

A nano-calcium carbonate, production method technology, applied in the fields of botanical equipment and methods, wood treatment, impregnating wood, etc., can solve problems such as easy combustion, poor dimensional stability, cracking, etc., and achieve anti-corrosion, flame-retardant improvement, and anti-loss stability. , the effect of simple processing technology

Inactive Publication Date: 2015-08-26
王玉燕
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to long-term contact with oxygen, light, and moisture, wood is prone to shrinkage and swelling, poor dimensional stability, and easy to change color, crack, wear and bruise, and is also easy to burn and be eaten by insects and bacteria.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The technical solutions of the present invention will be further described below in combination with specific preferred embodiments.

[0015] A production method for preparing nano calcium carbonate / wood composite material, comprising the following steps:

[0016] (1) Wood pretreatment: After peeling and sawing the log into required size specifications, dry it at 50°C-80°C for 8-24 hours, and control the moisture content of the wood to 8%-25%. Then microwave treatment for 10-30 minutes; wherein, the log is suitable for any wood, including poplar, birch, nanmu, eucalyptus, fir, pine and the like.

[0017] (2) Preparation of wood modifier: Add 20-40 parts by mass of nano-calcium carbonate and 0.5-2 parts by mass of surfactant into the mixer, then add 300-400 parts by mass of water, at a temperature of 60°C-85°C , Stir at a high speed of not less than 6000r / min for 20-50min, then ultrasonically disperse at 60°C-75°C for 10-20min, then add 10-15 parts by mass of sodium oct...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nano calcium carbonate /wood composite material production method including the five steps of pretreatment of wood, preparation of a wood modifying agent, preparation of a wood modifying liquid, dipping treatment, and post drying treatment, and the wood modifying agent includes nano calcium carbonate, a surface active agent, water, sodium octoborate, diammonium phosphate, boric acid, ammonium molybdate, carbendazim, dodecyl dimethyl benzyl ammonium chloride, imidacloprid, and sodium dodecyl sulfate, and the surface active agent is one of fatty alcohol polyoxyethylene ether, polyoxyethylene amide, and sodium dodecyl benzene sulfonate. The beneficial effect is that the nano calcium carbonate /wood composite material production method has simple process, high efficiency, environmental friendliness and low cost and other advantages, and by use of the nano calcium carbonate for modification, the nano calcium carbonate /wood composite material has good enhancement, weighting, anti-erosion, stability improvement and the like.

Description

technical field [0001] The invention relates to the technical field of wood production, in particular to a production method for preparing nanometer calcium carbonate / wood composite material. Background technique [0002] As a natural and renewable resource, wood has the advantages of beautiful texture, natural color, comfortable texture, good plasticity, and easy processing, so it is used as an ideal material for building decoration and furniture manufacturing. However, due to long-term contact with oxygen, light, and moisture, wood is prone to shrinkage and swelling, poor dimensional stability, and easy to change color, crack, wear and bruise, and is also easy to burn and be eaten by insects. Therefore, the modification of wood has been widely concerned for a long time. Nano-calcium carbonate has a good impact-reinforcing effect, and has high chemical stability, thermal stability and non-migration, and is cheap. A nano-calcium carbonate / wood composite material prepared b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/08B27K3/52B27K5/04A01N59/26A01P1/00A01P3/00A01N51/00
CPCB27K3/08A01N51/00A01N59/26B27K3/52B27K5/04B27K2240/00B27K2240/30
Inventor 不公告发明人
Owner 王玉燕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap