High-temperature tempered glass ink and preparation method thereof

A tempered glass ink and high temperature technology, applied in the field of ink, can solve the problems of poor water resistance, physical injury of printing workers, inconsistent use effects, etc., and achieve the effect of convenient operation and control, high production efficiency and rich colors

Inactive Publication Date: 2015-09-09
陈养生
View PDF2 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the existing ink, the ink has poor adhesion to the glass substrate, poor water resistance, coating peeling off after wet or muddy water contact, poor weather resistance, easy to change color, and cannot be used for a long time beautifully
Some inks used for printing have poor printing adaptability, and may have inconsistent results due to different conditions such as seasons, humidity, and temperature.
[0005] Some inks contain highly toxic organic solvents, such as benzene, ketone solvent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A high temperature tempered glass ink, comprising the following raw materials in parts by weight:

[0044] Glass base glaze 40 parts

[0045] Coloring agent 25 parts

[0046] 10 parts varnish

[0047] Additive 0.3 parts.

[0048] The glass-based glaze is composed of the following raw materials by weight percentage: 14% silicon oxide, 30% bismuth oxide, 15% boron oxide, 10% titanium oxide, 10% aluminum oxide, 8% zirconium oxide, 1% zinc oxide, and 1% sodium oxide , potassium oxide 1% and silicic acid 10%.

[0049] The coloring agent is a mixture composed of copper chromium oxide, zinc oxide, titanium dioxide and high temperature resistant pearl powder in a weight ratio of 3:1.5:1:2.

[0050] The varnish is composed of the following raw materials in percentage by weight: 20% turpentine, 30% terpineol, 10% terpineol, 20% rosin resin, 10% hydroxyethyl cellulose and 10% high-boiling organic solvent.

[0051] The high-boiling organic solvent is a mixture of ethylene glyc...

Embodiment 2

[0061] A high temperature tempered glass ink, comprising the following raw materials in parts by weight:

[0062] Glass base glaze 42 parts

[0063] Coloring agent 27 parts

[0064] 12 parts varnish

[0065] Additive 0.6 parts.

[0066] The glass-based glaze is composed of the following raw materials by weight percentage: 10% silicon oxide, 22% bismuth oxide, 17% boron oxide, 12% titanium oxide, 12% aluminum oxide, 9% zirconium oxide, 2% zinc oxide, and 2% sodium oxide , potassium oxide 2% and silicic acid 12%.

[0067] The coloring agent is a mixture composed of copper chromium oxide, zinc oxide, titanium dioxide and high temperature resistant pearl powder in a weight ratio of 3.5:1.7:1:2.5.

[0068] The varnish is composed of the following raw materials in weight percentage: 15% turpentine, 22% terpineol, 14% terpineol, 18% rosin resin, 16% hydroxyethyl cellulose and 15% high-boiling organic solvent.

[0069] The high-boiling organic solvent is a mixture of ethylene gly...

Embodiment 3

[0079] A high temperature tempered glass ink, comprising the following raw materials in parts by weight:

[0080] Glass-based glaze 45 parts

[0081] Coloring agent 30 parts

[0082] 14 parts varnish

[0083] Additive 0.9 parts.

[0084] The glass-based glaze is composed of the following raw materials by weight percentage: 10% silicon oxide, 20% bismuth oxide, 15% boron oxide, 15% titanium oxide, 15% aluminum oxide, 10% zirconium oxide, 3% zinc oxide, and 3% sodium oxide , potassium oxide 3% and silicic acid 15%.

[0085] The coloring agent is a mixture composed of copper chromium oxide, zinc oxide, titanium dioxide and high temperature resistant pearl powder in a weight ratio of 4:2:1:3.

[0086] The varnish is composed of the following raw materials in percentage by weight: 20% turpentine, 25% terpineol, 15% terpineol, 15% rosin resin, 15% hydroxyethyl cellulose and 10% high-boiling organic solvent.

[0087] The high-boiling organic solvent is a mixture of ethylene glyc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of ink, and particularly relates to high-temperature tempered glass ink and a preparation method thereof. The high-temperature tempered glass ink comprises the following raw materials in parts by weight: 40 to 50 parts of glass glaze, 25 to 35 parts of coloring agent, 10 to 18 parts of varnish and 0.3 to 1.5 parts of additive. The high-temperature tempered glass ink is not only efficient, environment-friendly and rich in color, but also has excellent characteristics such as high temperature resistance, high hardness, high weather resistance, ultrahigh wear resistance, acid-alkali resistance and the like.

Description

technical field [0001] The invention relates to the technical field of inks, in particular to a high-temperature tempered glass ink and a preparation method thereof. Background technique [0002] With the development of construction, automobile, decoration, furniture, information industry technology and other industries and the improvement of people's requirements for living space environment, functional processed products such as safety glass and energy-saving insulating glass have been widely used. The supply and demand pattern and consumption structure of flat glass are changing. [0003] On safety glass products, the application of printing process is becoming more and more extensive. In our daily life, there are many safety glass products such as sliding doors, tea sets, disinfection cabinets, ovens, furniture, car windshields, etc. These glass products have become beautiful and colorful after being decorated by printing technology. colorful. It not only increases th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/08C09D11/14C09D11/03C09D11/037
CPCC09D11/08C09D11/03C09D11/037C09D11/14
Inventor 陈养生
Owner 陈养生
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap