Polymer coating and preparation method thereof

A polymer and coating technology, applied in the field of coatings, can solve the problems of film-forming mechanical properties, poor water resistance and solvent resistance, etc., and achieve the effect of good coating film hardness and good surface effect

Inactive Publication Date: 2015-09-09
HEFEI JIKE NEW MATERIALS
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Water-based polyurethane emulsion has the advantages of adjustable hardness, excellent adhesion and flexibility, and is widely used in the fields of coatings, adhesives and inks. At present, the relatively mature anionic water-based polyurethane is synthesized mainly th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A polymer coating, characterized in that the coating is composed of component A and component B with a mass ratio of 1.7:1, and component A is composed of the following raw materials in parts by weight:

[0035] Isophorone diisocyanate 67, polyethyleneimine 4, maleic anhydride-acrylic acid copolymer 1, diphenylsilanediol 0.4, sodium fluorosilicate 2, barium stearate 3, sp-80 0.3, ethyl Cellulose 2, polycarbonate diol 93, polysilsesquioxane 1.6, azobisisobutyronitrile 0.9, butyl tin mercaptide 0.17, fluoroboric acid 0.13, castor oil 10, 1,4-butanediol 1.3 ;

[0036] Described B component is made up of the raw material of following parts by weight:

[0037] Acetyl triethyl citrate 4.6, dimethylaminopropylamine 0.2, dimethylthiotoluenediamine 3, casein 0.2, diethylaminoethanol 0.6, talc 5.

[0038] A preparation method of polymer coating, comprising the following steps:

[0039] Wherein the preparation method of component A comprises the following steps:

[0040] (1) A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polymer coating. Firstly, a castor oil crosslinking prepolymer is adopted, wherein a multifunctional group structure of castor oil can endow a polymer with certain crosslinking, accordingly, the crosslinking degree of the polymer is improved, the interaction force of molecular chains is increased, movement of the molecular chains is blocked, water molecules cannot easily enter the molecular chains to swell the polymer, and the water absorption of the coating is reduced; meanwhile, the castor oil is triglycerin of fatty acid, nonpolar fatty acid chains of medium-long chains in molecules of the castor oil enable the coating to have excellent hydrophobicity, and the water absorption is further reduced; besides, ester in the castor oil has higher cohesive energy and can improve the tensile strength of the coating; ethyl cellulose has better heat resistance and thermoplasticity and has good compatibility with polyurethane, and the comprehensive performance of the prepolymer can be improved; the polyurethane prepolymer and polysilsesquioxane are subjected to blending modification.

Description

technical field [0001] The invention relates to a paint, in particular to a polymer paint and a preparation method thereof. Background technique [0002] Water-based polyurethane emulsion has the advantages of adjustable hardness, excellent adhesion and flexibility, and is widely used in the fields of coatings, adhesives and inks. At present, the relatively mature anionic water-based polyurethane is synthesized mainly through the synthesis of polyurethane molecular chains. The hydrophilic group is introduced into the segment and internally emulsified. After film formation, it has certain hygroscopicity, and the mechanical properties, water resistance and solvent resistance of film formation are poor. Usually, cross-linking modification and compound modification can be used to improve the water resistance and mechanical properties of the film; [0003] In order to improve the mechanical properties, water resistance and other properties of polyurethane, while reducing product...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D7/12
Inventor 徐明
Owner HEFEI JIKE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap