Lubricating agent for superfine copper wire drawing

A lubricant and copper wire technology, which is applied in the direction of lubricating compositions, additives, petroleum industry, etc., can solve the problems that lubricant cannot pass through with copper wire, lubrication failure, copper wire oxidation, etc., so as to inhibit the production of copper soap, Guaranteed lubricating performance and moderate cost effect

Inactive Publication Date: 2015-09-09
TIANJIN UNIVERSITY OF TECHNOLOGY
View PDF3 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The copper wire drawing production process is used in the wire and cable industry. In order to make it efficiently produced, lubricants must be used. However, in actual production, some problems often occur: during the drawing process of copper ultra-fine wire, the copper wire is prone to oxidation; Copper ions in the lubricant react with anions to form copper soaps, and these copper soaps precipitate and block the die holes of the wire drawing die, causing the lubricant to fail to pass through the die holes with the copper wires and fail to adhere to the surface of the copper wires, resulting in lubrication failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The base oil is prepared by mixing paraffinic base oil and naphthenic oil at a ratio of 2:1, and the number of parts by mass is 5-30 parts; the emulsifier is prepared by mixing triethanolamine oleate and sodium petroleum sulfonate at a ratio of 3:1, and the number of parts by mass is 10-40 parts; long-chain isomeric alcohol as coupling agent, 1 part by mass; distilled tall oil DTO30, diethanolamine DEA, boric acid and diethylene glycol as 5:3:1:1 surfactant Mixed preparation, the number of parts by mass is 1 part; the anti-corrosion and anti-rust agent is benzotriazole, the number of parts by mass is 2 parts; -20 parts; the defoamer is dimethyl silicone oil, the mass part is 0.1 part; the fungicide is mixed with triazine and benzoisothiazolinone in 4:1, and the mass part is 1 part; The grinding agent is an alkyl phosphite, and the mass fraction is 1 part, and the mass fraction of water is 30-50 parts.

[0020] Add base oil, emulsifier, surfactant, couplant, alkali reta...

Embodiment 2

[0022] The base oil is prepared by mixing paraffinic base oil and naphthenic oil at a ratio of 2:1, and the number of parts by mass is 10-25 parts; the emulsifier is prepared by mixing triethanolamine oleate and sodium petroleum sulfonate at a ratio of 3:1, and the number of parts by mass is 15-30 parts; long-chain isomeric alcohols as coupling agent, 2 parts by mass; distilled tall oil DTO30, diethanolamine DEA, boric acid and diethylene glycol as 5:3:1:1 surfactant Mixed preparation, the number of parts by mass is 2 parts; the anti-corrosion and anti-rust agent is benzotriazole, the number of parts by mass is 4 parts; -25 parts; The defoamer is dimethyl silicone oil, and the mass parts are 0.1 parts; the fungicide is mixed with triazine and benzoisothiazolinone in 4:1, and the mass parts are 2 parts; The grinding agent is an alkyl phosphite, with 2 parts by mass and 30-50 parts by mass of water.

[0023] Add base oil, emulsifier, surfactant, couplant, alkali retaining agent...

Embodiment 3

[0025] The base oil is prepared by mixing paraffinic base oil and naphthenic oil at a ratio of 2:1, and the number of parts by mass is 5-20 parts; the emulsifier is prepared by mixing triethanolamine oleate and sodium petroleum sulfonate at a ratio of 3:1, and the number of parts by mass is 10-25 parts; long-chain isomeric alcohol as coupling agent, 3 parts by mass; distilled tall oil DTO30, diethanolamine DEA, boric acid and diethylene glycol for surfactant according to 5:3:1:1 Mixed preparation, the number of parts by mass is 3 parts; the anti-corrosion and antirust agent is benzotriazole, the number of parts by mass is 6 parts; -25 parts; the defoamer is dimethyl silicone oil, and the mass parts are 0.1 parts; the fungicide is mixed with triazine and benzoisothiazolinone in 4:1, and the mass parts are 3 parts; The grinding agent is an alkyl phosphite, with 3 parts by mass and 30-50 parts by mass of water.

[0026] Add base oil, emulsifier, surfactant, couplant, alkali reta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a lubricating agent for superfine copper wire drawing. The lubricating agent comprises the following components in parts by mass: 5-25 parts of lubrication base oil, 10-30 parts of an emulsifying agent, 1-5 parts of a surface active agent, 1-10 parts of an antirust agent, 1-5 parts of an extreme pressure antiwear additive, 1-5 parts of a thickening agent, 5-25 parts of an alkali retention agent, 1-5 parts of a bactericide, 0.1 part of a defoaming agent and 30-50 parts of water. The lubricating agent for superfine copper wire drawing has good oxidation resisting, cooling, cleaning, lubricating, rust preventing, hard water resisting and copper soap dispersing properties, and is particularly suitable for superfine copper wire drawing.

Description

technical field [0001] The invention relates to a lubricant for ultrafine copper wire drawing, which belongs to the technical field of molds. Background technique [0002] The copper wire drawing production process is used in the wire and cable industry. In order to make it efficiently produced, lubricants must be used. However, in actual production, some problems often occur: during the drawing process of copper ultra-fine wire, the copper wire is prone to oxidation; Copper ions in the lubricant react with anions to form copper soaps, and these copper soaps precipitate and block the die holes of the wire drawing die, causing the lubricant to fail to pass through the die holes with the copper wires and fail to adhere to the surface of the copper wires, resulting in lubrication failure. [0003] The high-speed wire drawing production line developed in recent years puts forward higher requirements for lubricants, such as requiring suitable lubricity to reduce wear and improve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/00C10M133/16C10N30/04C10N30/06C10N30/12C10N30/18C10N40/24
Inventor 马叙王悦阳丁燕红
Owner TIANJIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap