A technology for aerated bricks and tailings, applied in the field of aerated bricks, can solve problems such as poor water resistance, moisture resistance, thermal insulation, etc., residual biomass raw materials, and difficulty in raw material processing, etc., to improve the overall strength and stability. The effect of improving surface resistance and high surface resistance

Inactive Publication Date: 2015-10-21
合肥蓝科新材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the technical level of domestic aerated concrete has reached the international advanced level. In order to reduce the cost, the existing aerated bricks often result in a single variety, poor water resistance, moisture resistance, thermal insulation and other performances, and it is difficult to meet the development needs of the current society;
[0003] At present, many biomass raw materials such as bark and coconut shell are mostly used in fuel, feed and other fields, but there are still many remaining biomass raw materials, and these remaining raw materials also have problems such as processing difficulties, and aerated bricks are indispensable for social construction. Therefore, if the excessive surplus biomass raw materials are used for the production of aerated bricks, not only can the production cost be saved, but also the problem of excessive surplus resources can be solved, so as to make due contributions to the modernization construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A tailings aerated brick is characterized in that it is composed of the following raw materials in parts by weight:

[0022] Molybdenum oxide 0.8, titanium sulfate 0.2, sepiolite powder 6, tailings 20, potassium zirconium carbonate 2, dimethylethanolamine 0.1, bone char 3, high borate calcium borate 3, lapis lazuli powder 6, volcanic ash 3, aluminum sulfate 0.4, powder Coal ash 300, quicklime 46, aluminum powder 0.5, ordinary Portland cement 40, biomass resistance enhancer 10;

[0023] The biomass resistance enhancer is composed of the following raw materials in parts by weight:

[0024] Biomass raw powder 200, aluminum sulfate 3, fatty alcohol polyoxyethylene ether 2, dipotassium glycyrrhizinate 2, glycidyl methacrylate 30, divinylbenzene 0.7, polyvinyl alcohol 3, aminopropyl triethoxy Silane 0.6;

[0025] Mix fatty alcohol polyoxyethylene ether and dipotassium glycyrrhizinate, add it to 40 times of water, stir evenly, add raw biomass powder, raise the temperature to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a mill tailing air-entraining brick. The mill tailing air-entraining brick is composed of the following raw materials of, by weight, 0.8-2 parts of molybdenum oxide, 0.1-0.2 part of titanous sulfate, 4-6 parts of sea-foam stone powder, 10-20 parts of mill tailings, 1-2 parts of potassium zirconium carbonate, 0.1-0.4 part of dimethylethanolamine, 2-3 parts of bone charcoal, 2-3 parts of high-boron calcium borate, 4-6 parts of celestite powder, 2-3 parts of volcanic ash, 0.2-0.4 part of aluminum sulfate, 260-300 parts of pulverized coal, 42-46 parts of quick lime, 0.3-0.5 part of aluminum powder, 37-40 parts of ordinary portland cement and 5-10 parts of a biomass resistance enhancement agent. According to the mill tailing air-entraining brick, the biomass resistance enhancement agent is added, waste resource barks and coconut shells are adopted as biomass raw powder, after enzyme treatment and alkali treatment, fiber materials with good pliability can be obtained, the fiber materials are blended with methylacrylic acid glycidyl ester and subjected to modification, the surface resistance is improved, then the modified substance is mixed with saline solutions, polyving alcohol and the like and dried, so that the effective recycle of resources is achieved, and meanwhile the stability of promoters is also improved.

Description

technical field [0001] The invention mainly relates to the field of aerated bricks, in particular to a tailings aerated brick. Background technique [0002] Air-entrained concrete is a new type of wall building material. It is unique in that it is a very lightweight new type of building wall material for thermal insulation. The air-entrained concrete technology started a hundred years ago, and my country's technology started relatively late, 40 years behind foreign countries. However, the development of my country's air-entrained concrete industry is indeed very rapid. At present, the technical level of domestic aerated concrete has reached the international advanced level. In order to reduce the cost, the existing aerated bricks often result in a single variety, poor water resistance, moisture resistance, thermal insulation and other performances, and it is difficult to meet the development needs of the current society; [0003] At present, many biomass raw materials s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/12C04B18/08C04B22/04
CPCY02W30/91
Inventor 吴春云
Owner 合肥蓝科新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products