Ferrovanadium slag-high aluminium blast furnace slag EPC (expendable pattern casting) coating and preparation method thereof

A technology of lost foam casting and blast furnace slag, which is applied to casting molding equipment, coatings, casting molds, etc., can solve problems such as environmental hazards, improve fire resistance limit, reduce manufacturing costs, and improve cohesiveness and dispersion. Effect

Inactive Publication Date: 2015-12-02
张燕
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the traditional production process of vanadium products, a large amount of waste slag is produced, such as vanadium extractio...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A vanadium-iron slag-high alumina blast furnace slag lost foam casting coating is characterized in that the lost foam casting coating is composed of the following raw materials in parts by weight:

[0046] 28 parts of ferrovanadium slag

[0047] 21 parts of high alumina blast furnace slag

[0048] 7 parts of quartz tailings

[0049] 5 parts of pyrite tailings

[0050] 4 parts diatomaceous earth

[0051] Silicon carbide 3 parts

[0052] 2 parts calcium peridot

[0053] 2 parts graphite powder

[0054] 2 parts cordierite

[0055] 2 parts talcum powder

[0056] 2 parts aluminum borate

[0057] 4 parts of γ-methacryloxypropyltrimethoxysilane

[0058] Monoalkoxy tris (dioctylphosphoryloxy) titanate 6 parts

[0059] Trimethylol melamine formaldehyde resin 2 parts

[0060] Dicumyl peroxide 0.3 parts

[0061] 0.4 parts of tristyrylphenol polyoxyethylene ether

[0062] 0.3 parts of polyvinyl acetate emulsion

[0063] Boron carbide fiber 2 parts

[0064] 1 part water...

Embodiment 2

[0074] A vanadium-iron slag-high alumina blast furnace slag lost foam casting coating is characterized in that the lost foam casting coating is composed of the following raw materials in parts by weight:

[0075] 34 parts of ferrovanadium slag

[0076] 27 parts of high alumina blast furnace slag

[0077] Quartz tailings 13 parts

[0078] 11 parts of pyrite tailings

[0079] 8 parts diatomaceous earth

[0080] Silicon carbide 7 parts

[0081] Calcium peridot 5 parts

[0082] 5 parts graphite powder

[0083] 6 parts cordierite

[0084] 4 parts talcum powder

[0085] 4 parts aluminum borate

[0086] 7 parts of γ-methacryloxypropyltrimethoxysilane

[0087] 10 parts of monoalkoxy tris(dioctylphosphoryloxy) titanate

[0088] 4 parts trimethylol melamine formaldehyde resin

[0089] 0.6 parts of dicumyl peroxide

[0090] 0.6 parts of tristyrylphenol polyoxyethylene ether

[0091] 0.6 parts of polyvinyl acetate emulsion

[0092] Boron carbide fiber 3 parts

[0093] 3 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a ferrovanadium slag-high aluminium blast furnace slag EPC (expendable pattern casting) coating and a preparation method thereof. According to the preparation method, ferrovanadium slag, high aluminium blast furnace slag, pyrite tailings, quartz tailings, kieselguhr, silicon carbide, monticellite, cordierite, graphite powder, talcum powder, aluminium borate, gamma-methacryloxy propyl trimethoxyl silane, mono-alkoxy tri (dioctylphosphate) titanate, trihydroxy methyl melamine formaldehyde resin, dicumyl peroxide, triphenyl ethyl phenol polyoxyethylene ether, polyvinyl acetate emulsion, boron carbide fiber, water glass, sodium borate, n-octyl alcohol, ethyl alcohol and water are adopted as the raw materials to prepare the EPC coating with an excellent use property and low production cost, and the purposes of comprehensively recycling ferrovanadium slag and high aluminium blast furnace slag and reducing the production cost are achieved.

Description

technical field [0001] The invention belongs to the field of lost foam casting coatings, in particular to a vanadium iron slag-high alumina blast furnace slag lost foam casting coating and a preparation method thereof. Background technique [0002] Lost foam casting technology is a new casting process in the foundry industry. The lost foam casting process refers to making foam plastic (EPS, ETMMA or EPMMA) into the shape, structure and size of the required castings. After the refractory coating is dried, it is embedded in a special sand box with dry sand (usually quartz sand) for molding, and then poured under a certain negative pressure. Lost foam casting is mainly called dry sand solid mold casting and negative pressure solid mold casting in China, and it is referred to as EPC casting abroad. [0003] At present, the most mature lost foam casting process is used in the mass production of automotive castings. The products produced include aluminum alloy castings (such as i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C3/00
Inventor 张燕
Owner 张燕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap