Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Process method for making building material from straw fiber and pulp

A technology of straw fiber and process method, which is applied in the field of straw fiber pulp to make building materials, can solve problems such as pollution, and achieve the effects of high strength, green environmental protection and low cost

Active Publication Date: 2015-12-09
北京秸大环保科技有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a process method for making building materials from straw fiber pulp to solve the problem of pollution caused by the presence of formaldehyde in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0020] A process for making building materials from straw fiber pulp. The building material formula includes straw fibers, talcum powder, magnesium oxide and a modifier, wherein the mass proportions of each component are straw fiber 70%; talc powder 10%; magnesium oxide 10% % and modifier 10%, the modifier is made up of sodium dodecylbenzenesulfonate, powdered activated carbon, pulping black liquor, sodium silicate and liquid paraffin, wherein the mass proportion of each component is dodecane Sodium phenyl sulfonate 10%; powdery activated carbon 30%; pulping black liquor 40%; sodium silicate 10% and liquid paraffin 10%, the Baume degree of pulping black liquor is 28°, the specific process steps are as follows:

[0021] (1) Modifier preparation: first put the pulping black liquor into a stirring container, then add sodium dodecylbenzenesulfonate, stir for ten minutes, then add sodium silicate and powdered activated carbon, and stir for fifteen minutes ,spare;

[0022] (2) Put ...

example 2

[0025] A process for making building materials from straw fiber pulp. The building material formula includes pulp, talcum powder, magnesium oxide and a modifier, wherein the mass proportions of each component are 70% of pulp; 10% of talc powder; 10% of magnesium oxide and Modifier 10%, the modifier is composed of sodium dodecylbenzenesulfonate, powdered activated carbon, pulping black liquor, sodium silicate and liquid paraffin, wherein the mass proportion of each component is dodecylbenzene Sodium sulfonate 10%; powdered activated carbon 30%; pulping black liquor 40%; sodium silicate 10% and liquid paraffin 10%, the Baume degree of pulping black liquor is 28°, the specific process steps are as follows:

[0026] (1) Modifier preparation: first put the pulping black liquor into a stirring container, then add sodium dodecylbenzenesulfonate, stir for ten minutes, then add sodium silicate and powdered activated carbon, and stir for fifteen minutes ,spare;

[0027] (2) Put the pla...

example 3

[0030] A process for making building materials from straw fiber pulp. The building material formula includes wheat straw fiber, talcum powder, magnesium oxide and a modifier, wherein the weight ratio of each component is 60% of wheat straw fiber; 15% of talc powder; 10% of magnesium oxide % and modifier 15%, the modifier is made up of sodium dodecylbenzenesulfonate, powdered activated carbon, pulping black liquor, sodium silicate and liquid paraffin, wherein the mass proportion of each component is dodecane Sodium phenyl sulfonate 10%; powdery activated carbon 30%; pulping black liquor 40%; sodium silicate 10% and liquid paraffin 10%, the Baume degree of pulping black liquor is 28°, the specific process steps are as follows:

[0031] (1) Modifier preparation: first put the pulping black liquor into a stirring container, then add sodium dodecylbenzenesulfonate, stir for ten minutes, then add sodium silicate and powdered activated carbon, and stir for fifteen minutes ,spare;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process method for making a building material from straw fiber and pulp. A formula of the building material comprises the following components in percentage by mass: 60 to 80 percent of plant fiber, 5 to 15 percent of talcum powder, 5 to 15 percent of magnesium oxide and 5 to 15 percent of a modifying agent, wherein the modifying agent is composed of the following components in percentage by mass: 10 percent of sodium dodecyl benzene sulfonate, 30 percent of powdered activated carbon, 40 percent of pulping black liquor, 10 percent of sodium silicate and 10 percent of liquid paraffin. The straw fiber or the pulp serves as raw materials, and by utilizing the reduction characteristic of lignin, a produced building material product does not contain formaldehyde and any colloid, is non-toxic, tasteless, radiation-free, water-proof, damp-proof, fire-proof, sound-proof, thermally insulated, acid-base-resistant, ageing-resistant and moth-proof, and has the advantages of light weight, high strength, low cost and environmental protection.

Description

technical field [0001] The invention relates to the technical field of building material production and processing, in particular to a process for making building materials from straw fiber pulp. Background technique [0002] my country is a large agricultural country with extremely rich biomass resources. The annual output of crop straw alone reaches 700 million tons per year, of which nearly 200 million tons of rice straw accounts for about 30% of the straw resources. Most of these straws are discarded in the fields, or directly burned as living energy, resulting in waste of resources and environmental pollution. With the implementation of the national policy of prohibiting the logging of natural forests, the panel and building material production industries are facing great challenges. How to find new alternatives to natural wood to make building materials has become the only way for the industry to seek new raw materials to replace natural wood and develop new building m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L91/06C08K13/06C08K9/04C08K3/04C08K3/34C08K3/22
Inventor 刘秀平沈晓东
Owner 北京秸大环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com