Nanometer fiber composite filament bundle capable of reducing content of phenol in smoke, and preparation method and application of nanometer fiber composite filament bundle

A nanofiber, composite tow technology, applied in the direction of cellulose/protein conjugated rayon, application, fiber processing, etc., can solve the problem that the specific surface area of ​​nanofibers cannot reflect the characteristics of fiber materials, reduce tar content, and low efficiency. The problem is that the preparation method is green and environmentally friendly, the phenol content is reduced, and the raw materials are cheap and easy to obtain.

Active Publication Date: 2015-12-16
CHINA TOBACCO ZHEJIANG IND
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention patent document with the publication number CN103625090A discloses a nanofiber membrane modified tow based on electrospinning. The tow is used in cigarette filters, which can effectively reduce the tar content, but has no effect on phenol reduction.
At the same time, the electrospinning technology of the traditional spinneret used in this patent document is easy to block holes and has low efficiency, and the maximum amount of nanofibers composited on the tow is only 0.8g / m 2 , unable to reflect the characteristics of fiber materials and the advantages of high specific surface area of ​​nanofibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nanometer fiber composite filament bundle capable of reducing content of phenol in smoke, and preparation method and application of nanometer fiber composite filament bundle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Dissolve 20g of cellulose diacetate and 5g of diphenylmethane diisocyanate in 200mL of dimethylformamide, and react at 50°C for 2.0h to obtain a reaction liquid; Tin was added to the reaction solution, and the reaction was continued at 90° C. for 1.5 h to obtain cyclodextrin-modified cellulose acetate.

[0042] Cyclodextrin-modified cellulose acetate, cellulose diacetate, glycerol triacetate and N,N-dimethylformamide with a mass ratio of 0.005:0.01:0.001:1 were prepared into a uniform spinning solution, and the spinning The liquid is placed in the liquid-carrying tank of the needleless electrospinning machine, and the electrospinning is carried out at a voltage of 30kV. The winding speed of the base material is 400m / min, and the nanofibers are deposited on the surface of the tobacco tow to obtain a nanofiber composite tow. The diameter of the nanofiber in the nanofiber composite tow is 500nm.

[0043]The obtained nanofiber composite tow was rolled into a filter rod on ...

Embodiment 2

[0045] Dissolve 10g of cellulose acetate and 10g of toluene diisocyanate in 200mL of dimethylformamide, and react at 25°C for 0.5h to obtain a reaction liquid; add 15g of α-cyclodextrin and 0.1g of potassium acetate to the reaction solution, and continue to react at 30°C for 0.5h to obtain cyclodextrin-modified cellulose acetate.

[0046] Cyclodextrin-modified cellulose acetate, cellulose triacetate, ethylene glycol and acetone with a mass ratio of 0.05:0.2:0.01:2 are prepared into a uniform spinning solution, and the spinning solution is placed in a needle-free electrospinning machine In the carrier liquid tank, electrospinning at a voltage of 5kV, the distance between the steel wire and the tobacco tow substrate is adjusted to 5cm, the winding speed of the tobacco tow substrate is 50m / min, and the nanofibers are deposited on the tobacco tow. The surface of the bundle is obtained to obtain a nanofiber composite tow, and the diameter of the nanofiber in the nanofiber composite...

Embodiment 3

[0049] Dissolve 15g of cellulose triacetate and 7.5g of hexamethylene diisocyanate in 200mL of dimethylformamide, and react at 50°C for 2.0h to obtain a reaction liquid; Tin acid was added to the reaction solution, and the reaction was continued at 70° C. for 1.5 h to obtain cyclodextrin-modified cellulose acetate.

[0050] Cyclodextrin-modified cellulose acetate, cellulose diacetate, glycerol triacetate and N,N-dimethylformamide with a mass ratio of 0.01:0.01:0.001:2 were prepared into a uniform spinning solution, and the spinning The liquid is placed in the liquid-carrying tank of the needleless electrospinning machine, and the electrospinning is carried out at a voltage of 30kV. The distance between the steel wire and the tobacco tow substrate is adjusted to 20cm, and the winding speed of the tobacco tow substrate is 150m. / min, the nanofibers are deposited on the surface of the tobacco tow to obtain the nanofiber composite tow, and the diameter of the nanofiber in the nano...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a nanometer fiber composite filament bundle capable of reducing the content of phenol in smoke, and a preparation method and an application of the nanometer fiber composite filament bundle. The nanometer fiber composite filament bundle comprises a filament bundle for a cigarette and nanometer fiber deposited on the surface of the filament bundle for the cigarette, wherein the diameter of the nanometer fiber is 20-500nm, and the nanometer fiber is prepared from cyclodextrin-modified cellulose acetate through electrostatic spinning. The preparation method of the nanometer fiber composite filament bundle comprises the following steps: (1) activating cellulose acetate with isocyanate, and performing graft copolymerization of activated cellulose acetate and cyclodextrin to obtain cyclodextrin-modified cellulose acetate; and (2) taking the filament bundle for the cigarette as a base material, and performing electrostatic spinning of a spinning solution containing cyclodextrin-modified cellulose acetate to obtain the nanometer fiber composite filament bundle. The preparation method is available in raw materials, and is green, environment-friendly, safe, and controllable, and the obtained nanometer fiber composite filament bundle has an excellent adsorption effect on phenol.

Description

technical field [0001] The invention relates to the technical field of cigarettes, in particular to a nanofiber composite tow for reducing the phenol content in smoke, a preparation method and application thereof. Background technique [0002] As people pay more and more attention to the health problems caused by smoking, the research on tar reduction and harm reduction technology of cigarette products has attracted great attention of the tobacco industry. Aiming at various harmful components in cigarette smoke, researchers have developed a variety of harm reduction technologies, such as tipping filters, applying filter ventilation and dilution technology, using cigarette tow with high air permeability and fast static burning rate, blending Methods such as expanded shredded tobacco and expanded cut stems are used. [0003] Among the existing harm reduction technologies, modifying cigarette filters is one of the most commonly used and most effective means of harm reduction. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F8/02D01F1/10D01D5/00A24D3/10
Inventor 徐志康储国海王辉安全福周国俊汤德芳万灵书杜芳琪李霞智锁红
Owner CHINA TOBACCO ZHEJIANG IND
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com