Durable grouting material

A grouting material and a durable technology, applied in the field of material science, can solve problems such as poor durability, limited research, and pollution prices, and achieve the effects of improving compactness, enhancing waterproof performance and flame retardancy, and expanding the scope of application

Inactive Publication Date: 2016-01-27
王璐
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although chemical grouting materials have the advantages of good stability, strong injectability, low viscosity, and easy control of gel time, etc., and can be injected into relatively small cracks or pores in rock and soil, their disadvantages are: relatively low strength. Low, poor durability, certain toxicity, pollution to the environment and expensive
Although some achievements have been made in the research of grouting materials, the research on the dual mixing of polymer and mineral admixtures in grouting materials is still very limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] In this example, the SiO of silica sol 2 The content is 40%, the particle size range is 50nm; the fineness of the mineral admixture is 250 mesh; the modulus of sodium silicate is 1.7;

[0031] A durable grouting material, made of the following raw materials in proportion by weight: 60 parts of Portland cement, 20 parts of aluminate cement, 1.5 parts of polyvinyl alcohol, 1.5 parts of polyvinyl acetate, 1.5 parts of styrene-butadiene emulsion 1.5 parts of silica sol, 4 parts of silica fume powder, 15 parts of fly ash, 11 parts of steel slag, 0.2 parts of dimethyl silicone oil, 2.5 parts of sodium silicate, 2.5 parts of slaked lime, 2.5 parts of anhydrous gypsum, carboxymethyl fiber 0.2 parts of plain, 0.4 parts of sodium dodecyl sulfonate, 3 parts of bentonite, 0.5 parts of fine sand, 0.4 parts of sodium carbonate, 0.05 parts of ceramic fiber, 0.02 parts of latex powder, 0.03 parts of dolomite, 0.02 parts of pyrophyllite, methyl silicon 4 parts sodium bicarbonate.

[0...

Embodiment 2

[0034] In this example, the SiO of silica sol 2 The content is 30%, the particle size range is 20nm; the fineness of the mineral admixture is 200 mesh; the modulus of sodium silicate is 1.5;

[0035] A durable grouting material, made of the following raw materials in proportion by weight: 50 parts of Portland cement, 15 parts of aluminate cement, 1 part of polyvinyl alcohol, 1 part of polyvinyl acetate, 1 part of styrene-butadiene emulsion 1 part, 1 part of silica sol, 2 parts of silica fume powder, 10 parts of fly ash, 8 parts of steel slag, 0.1 part of dimethyl silicone oil, 2 parts of sodium silicate, 2 parts of slaked lime, 2 parts of anhydrous gypsum, carboxymethyl fiber 0.1 part of plain element, 0.3 part of sodium dodecyl sulfonate, 1 part of bentonite, 0.3 part of fine sand, 0.2 part of sodium carbonate, 0.03 part of ceramic fiber, 0.01 part of latex powder, 0.02 part of dolomite, 0.01 part of pyrophyllite, methyl silicon 2 parts sodium bicarbonate.

[0036] Grouting m...

Embodiment 3

[0038] In this example, the SiO of silica sol 2 The content is 50%, the particle size range is 80nm; the fineness of the mineral admixture is 300 mesh; the modulus of sodium silicate is 1.9;

[0039] A durable grouting material, made of the following raw materials in proportion by weight: 70 parts of Portland cement, 25 parts of aluminate cement, 2 parts of polyvinyl alcohol, 2 parts of polyvinyl acetate, 2 parts of styrene-butadiene emulsion 2 parts of silica sol, 6 parts of silica fume powder, 20 parts of fly ash, 14 parts of steel slag, 0.3 parts of dimethyl silicone oil, 3 parts of sodium silicate, 3 parts of slaked lime, 3 parts of anhydrous gypsum, carboxymethyl fiber 0.3 parts of plain, 0.5 parts of sodium dodecylsulfonate, 5 parts of bentonite, 0.7 parts of fine sand, 0.6 parts of sodium carbonate, 0.07 parts of ceramic fiber, 0.03 parts of latex powder, 0.04 parts of dolomite, 0.03 parts of pyrophyllite, methyl silicon 6 parts sodium bicarbonate.

[0040] Grouting m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Coagulation timeaaaaaaaaaa
Login to View More

Abstract

The invention discloses durable grouting material. The grouting material is prepared from the following raw materials in parts by weight: 50 to 70 parts of portland cement, 15 to 25 parts of aluminate cement, 4 to 8 parts of polymer emulsion, 20 to 40 parts of mineral additives, 0.1 to 0.3 parts of defoaming stabilizer, 6 to 9 parts of stimulator, 0.1 to 0.3 parts of water retaining agent, 0.3 to 0.5 parts of surfactant, 1 to 5 parts of bentonite, 0.3 to 0.7 parts of fine sand, 0.2 to 0.6 parts of sodium carbonate, 0.03 to 0.07 parts of ceramic fiber, 0.01 to 0.03 parts of emulsion powder, 0.02 to 0.04 parts of dolomite, 0.01 to 0.03 parts of pyrophyllite and 2 to 6 parts of methyl sodium silicate. According to the durable grouting material, a polymer and the mineral additives are modified together by utilizing the flexibility of the polymer and the rigidity of the mineral additives, so that the grouting material with good performance is obtained, and an application range of the grouting material is enlarged.

Description

technical field [0001] The invention relates to a durable grouting material, belonging to the technical field of material science. Background technique [0002] With the rapid development of my country's economy, the scale of transportation construction (such as high-speed rail, subway, highway) is getting larger and larger, and underground engineering and water conservancy projects are also receiving more and more attention. This is due to the increasing number of high-speed railways and subways, and the increasingly complex conditions of underground transportation projects, which have gradually revealed problems such as collapse, water inrush, and mud gushing; in addition, the traffic flow and axle load have increased rapidly, and roads have gradually experienced subsidence, muddying, Structural defects such as cracks. In order to solve these problems, people adopt grouting technology to reinforce and seal underground works and water conservancy projects. [0003] The gr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine