New material for electric heating parquet with built-in heating layer

A technology of solid wood composite flooring and built-in heating, which is applied in the field of new materials of solid wood composite flooring and electric heating solid wood composite flooring with built-in heating layer. Achieve the effect of increasing the storage period, improving the pot life and improving the preparation process

Active Publication Date: 2016-04-20
JIUSHENG WOOD
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the floor, especially the solid wood composite floor, is made of multiple pieces of wood boards bonded by adhesives, under long-term heating conditions, the adhesive force of the adhesives is likely to decrease, and the boards are degummed and warped.
On the other hand, due to the poor performance of the existing adhesives and waterproofing agents, the waterproof effect of the existing electric heating floor is not satisfactory, and the waterproof performance is a very important indicator for the electric heating floor. Water is extremely easy to cause safety accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • New material for electric heating parquet with built-in heating layer
  • New material for electric heating parquet with built-in heating layer
  • New material for electric heating parquet with built-in heating layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1: An electric heating solid wood composite floor with a built-in heating layer, as attached Figure 3-5 As shown, it includes a composite base material layer 1, a carbon fiber paper 2 is bonded on the top of the composite base material layer 1, copper sheet electrodes 3 are provided on both sides of the carbon fiber paper 2, and a decorative veneer 4 is provided above the carbon fiber paper 2; A back plate 5 is provided below the composite substrate layer 1 . The composite substrate 1 includes 8 layers of eucalyptus veneers 6 laminated together, and the wood grain direction of the 8 layers of eucalyptus veneers is vertically pressed and pasted, that is, the wood of the adjacent wood veneers Grain direction is vertical. The eucalyptus veneer is 1.5mm, and the beech veneer is 0.8mm. The eucalyptus veneer is 1.5mm, and the beech veneer is 0.8mm.

[0030] The preparation process of the electric heating solid wood composite floor with built-in heating laye...

Embodiment 2

[0041] Embodiment 2: the preparation method of melamine modified urea-formaldehyde resin glue comprises the following steps;

[0042] (1) Preparation of polyamide; add 30 parts of diethylenetriamine into an appropriate amount of water and stir, add 50 parts of adipic acid while stirring, and after stirring for 30 minutes, uniformly heat up to 160°C within 3 hours and keep it warm for 15 minutes, then cool down to 110°C, add an appropriate amount of water to cool, then heat to 100°C, and get polyamide after stirring evenly;

[0043] (2) Adjust 45 parts of formaldehyde solution to pH 9.5, then add 15 parts of urea, heat to 95°C for 60 minutes, then adjust the solution to pH 5, add 10 parts of polyamide and 30 parts of melamine after fully reacting, and then Add 5 parts of epichlorohydrin dropwise, react while stirring, and wait until the reaction is completed to obtain melamine-modified urea-formaldehyde resin glue.

Embodiment 3

[0044] Embodiment 3: the preparation method of waterproofing agent comprises the following steps;

[0045] (1) Take 80 parts of octamethylcyclotetrasiloxane, 3 parts of N-β-aminoethyl-γ-aminopropylmethyldimethoxysilane and 2 parts of tetramethylcyclotetrasiloxane, mix and stir evenly , heating up to 80°C, then adding 0.2 parts of tetramethylammonium hydroxide, heating up to 125°C for 3 hours, and then removing low boilers to obtain the primary product;

[0046] (2) Add the primary product and melamine at a mass ratio of 2:1, stir to 70-80°C while heating, and react for 1.5 hours to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a new material for electric heating parquet with a built-in heating layer. The new material contains melamine modified urea-formaldehyde resin adhesive bonded with carbon fiber paper. A preparing method for the melamine modified urea-formaldehyde resin adhesive includes the following steps that 1, polyamide is prepared, wherein an appropriate amount of water is added into 30-40 parts of diethylenetriamine, the mixture is stirred, 40-50 parts of hexanedioic acid are added in the stirring process, after stirring is conducted for 30 min, temperature is uniformly raised to 150 DEG C-170 DEG C within 1-5 h, kept for 15 min and then lowered to 80 DEG C-120 DEG C, an appropriate amount of water is added for cooling, and the mixture is heated to 80 DEG C-120 DEG C again and uniformly stirred to obtain polyamide; 2, the pH value of 40-60 parts of a formaldehyde solution is adjusted to 9.5, then 15-30 parts of urea are added, the mixed solution is heated to 85 DEG C-95 DEG C to react for 40-60 min, the pH value is adjusted to 5, after the sufficient reaction, 10-20 parts of polyamide and 20-30 parts of melamine are added, 5-10 parts of epoxy chloropropane are added dropwise, and all the substances react while stirred so that melamine modified urea-formaldehyde resin adhesive can be obtained after the reaction is finished.

Description

technical field [0001] The invention relates to a new material for a solid wood composite floor, in particular to a new material for an electric heating solid wood composite floor with a built-in heating layer, and belongs to the technical field of electric heating floors. Background technique [0002] As we all know, flooring has gradually become a necessity for home decoration and has entered most families due to its very practical functions such as moisture insulation, cold resistance, and comfort. With the continuous improvement of people's living standards, the use function of the floor is also continuously improved. In order to solve the problem of heating in winter, more and more families use electric heating floors that can generate heat for heating. However, since the floor, especially the solid wood composite floor, is made of multiple wood boards bonded by adhesives, in a long-term heating state, the adhesive force of the adhesives is likely to decrease, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02F24D13/02C09J161/32C08G12/40
CPCC08G12/40C09J161/32E04F15/041F24D13/024
Inventor 吴忠其王艳伟邵煜孙龙祥徐立
Owner JIUSHENG WOOD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap