Heat-resistant stable plastic plate and preparation method thereof

A kind of plastic sheet and stable technology, applied in the field of plastic sheet, can solve the problems of affecting the service life of the sheet, small linear expansion coefficient, poor heat resistance stability, etc. Effect

Inactive Publication Date: 2016-05-11
宁波远欣石化有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The elasticity of soft PVC is 1.5-15MPa, but the elongation at break is as high as 200%-450%. It can be used in chemical industry, electroplating, lining of electrolyzer, insulating cushion, train, automobile interior and auxiliary materials, etc. The heat resistance stability of PVC is very poor. It begins to decompose at 140°C, and the melting temperature is 160°C. The linear expansion coefficient of PVC is small, and it is flame retardant. Poor resistance, poor heat and humidity resistance and other shortcomings, seriously affecting the service life of the plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] A heat-resistant and stable plastic plate, which is composed of the following raw materials in parts by weight:

[0020] Calcium propionate 1, polyoxymethylene 2, stabilizing agent 2, sodium carboxymethyl cellulose 1, diethylene glycol dibenzoate 2, titanate coupling agent 2010.1, dimethyl isophthalate 4, poly Vinyl chloride 100, oleic acid diethanolamide 0.7, 2-mercaptobenzimidazole 0.6, ricinoleic acid 0.6, potassium dichromate 0.6, 96% sulfuric acid 30, sisal fiber 3, conch shell powder 2, diacetone acrylamide 0.4 , Expandable graphite 10.

[0021] Described stabilizing assistant is made up of the raw material of following weight part:

[0022] Zinc naphthenate 2.8, dibutyltin dilaurate 1, calcium palmitate 2, sodium myristate soap 0.1, 70% ethanol 3;

[0023] Mix the above-mentioned raw materials, keep stirring at 60°C for 20 minutes, and obtain the product.

[0024] A method for preparing the heat-resistant and stable plastic plate, comprising the following step...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elastic modulusaaaaaaaaaa
elasticityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a heat-resistant stable plastic plate. The heat-resistant stable plastic plate is prepared from, by weight, 1-2 parts of calcium propionate, 2-4 parts of polyformaldehyde, 2-3 parts of stabilizing auxiliary, 1-2 parts of sodium carboxymethylcellulose, 2-3 parts of diethylene glycol dibenzoate, 0.1-0.2 part of titanate coupling agent 201, 4-6 parts of dimethyl isophthalate, 100-130 parts of polyvinyl chloride, 0.7-2 parts of diglycolamide oleate, 0.6-2 parts of 2-mercapto benzimidazole, 0.6-1 part of ricinoleic acid, 0.6-1 part of potassium dichromate, 30-40 parts of 96-98% sulfuric acid, 3-5 parts of sisal fiber, 2-3 parts of conch shell powder, 0.4-2 parts of diacetone acrylamide and 10-14 parts of expansible graphite. Various stabilizing auxiliaries are added, the heat-resistant stability of the finished plate can be effectively improved, and the service life of the plate is prolonged.

Description

technical field [0001] The invention relates to the technical field of plastic plates, in particular to a heat-resistant and stable plastic plate and a preparation method thereof. Background technique [0002] The natural color of polyvinyl chloride (PVC) is light yellow translucent and shiny. Transparency is better than polyethylene and polypropylene, and worse than polystyrene. Depending on the amount of additives, it can be divided into soft and hard PVC. Soft products are soft and tough, and feel sticky. The hardness of hard products is higher than that of low-density polyethylene. And lower than polypropylene, there will be whitening at the inflection. Common products: plates, pipes, soles, toys, doors and windows, wire sheaths, stationery, etc. It is a polymer material that uses a chlorine atom to replace a hydrogen atom in polyethylene. PVC has high hardness and mechanical properties. And it increases with the increase of molecular weight, but decreases with the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L59/02C08L1/28C08L97/02C08K13/02C08K5/098C08K5/12C08K5/10C08K5/20C08K5/37C08K3/04
CPCC08L27/06C08L2201/08C08L2205/035
Inventor 施利群
Owner 宁波远欣石化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap