Circulating water corrosion and scale inhibitor and preparation method thereof

A technology of corrosion and scale inhibitors and circulating water, which is applied in chemical instruments and methods, descaling and water softening, water/sludge/sewage treatment, etc. Reduced scale efficiency, large consumption of chemicals, etc., to achieve the effect of inhibiting corrosion reaction, inhibiting oxygen corrosion, and reducing deposition

Active Publication Date: 2016-06-08
内蒙古润嘉节能环保科技有限公司
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, urban sewage contains a large amount of inorganic ions (such as Ca 2+ , Mg 2+ , SO 4 2- ) and a small amount of organic matter, especially Ca 2+ , Mg 2+ , SO 4 2- Under the conditions of several times of concentration and high temperature, it is easy to cause mineral scale to form on the surface of the circulating cooling water system equipment, and the high salinity under the concentration condition will make the corrosion problem of the system more serious
At the same time, scaling and corrosion are the key problems in the circulating cooling water system. People often add scale and corrosion inhibitors to the circulating water system to alleviate and control the scaling and corrosion of the system. Since sewage has a stronger The original corrosion and scale inhibitor formulations are no longer applicable, and the development of new corrosion and scale inhibitors based on the quality of urban sewage biochemical effluent water is a key technology to solve the problem of urban sewage reuse as circulating cooling water
[0004] In the invention whose application number is CN200610127172.0, an environment-friendly corrosion and scale inhibitor is disclosed for the treatment of circulating cooling water, which is characterized in t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] A method for preparing a circulating water corrosion and scale inhibitor, which includes the steps:

[0032] In S100, the respective components of the corresponding mass percentages are stirred for 30 minutes at room temperature and pressure, and mixed evenly to obtain a mixture; and

[0033] In S200, the mixture is placed in a reactor equipped with ultrasonic waves and processed under the action of ultrasonic waves to prepare the circulating water corrosion and scale inhibitor.

[0034] Wherein, the power of the ultrasonic wave in the step S200 is 100w˜500w, and the processing time of the ultrasonic wave is 2h˜5h.

[0035] Preferably, the power of the ultrasound is 300w, and the processing time of the ultrasound is 3h.

[0036] The circulating cooling water corrosion and scale inhibitor has a wide range of raw material sources, low production costs, and can achieve excellent corrosion and scale inhibition effects at a relatively low concentration during use, further saving treat...

Example Embodiment

[0040] Example one

[0041] The mass percentage of the raw materials of the circulating water corrosion and scale inhibitor is: 20% polyacrylamide, 15% 2-hydroxyphosphonic acid, 5% polyepoxysuccinic acid, 10% anthocyanin, 20% tea Phenol, 10% melamine, 20% isophorone diamine, and the rest is a mixed solution of ethylene glycol and water. After mixing the above-mentioned components uniformly, and treating for 3 hours under the action of 300w ultrasonic wave, the measured corrosion inhibition rate is 85.2%, and the scale inhibition rate is 82.3%.

Example Embodiment

[0042] Example two

[0043] The mass percentage of the raw materials of the circulating water corrosion and scale inhibitor is: 25% polyacrylamide, 20% 2-hydroxyphosphonic acid, 5% polyepoxysuccinic acid, 10% anthocyanin, 20% tea Phenol, 5% melamine, 15% isophorone diamine, the rest is a mixed solution of ethylene glycol and water. After mixing the above-mentioned components uniformly, and treating for 3 hours under the action of 300w ultrasonic wave, the measured corrosion inhibition rate is 83.1%, and the scale inhibition rate is 81.6%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a circulating water corrosion and scale inhibitor and a preparation method thereof. The circulating water corrosion and scale inhibitor mainly comprises polyacrylamide, 2-hydroxyphosphonoacetic acid, polyepoxysuccinic acid, anthocyanidins, tea polyphenol, melamine, isophorondiamine, ethylene glycol and water. The circulating water corrosion and scale inhibitor is suitable for industrial circulating cooling water systems to realize pre-film corrosion, scale prevention and corrosion inhibition of high-salinity wastewater in the circulating cooling water.

Description

technical field [0001] The invention relates to the field of water treatment, in particular to a corrosion and scale inhibitor suitable for circulating cooling water and a preparation method thereof. Background technique [0002] At present, more than 70% of cities in my country are facing the crisis of water shortage, while industrial water accounts for about 80% of urban water supply, and circulating cooling water accounts for more than 70% of industrial water consumption. Although saving water, improving technology, increasing water prices and remote water transfer have all alleviated the water shortage problem to varying degrees, all countries in the world are currently using urban sewage for industrial circulating water systems as the first choice to solve the water shortage problem. Utilizing urban sewage for industrial circulating cooling water, on the one hand, the discharge of a large amount of urban sewage pollutes the environment and wastes resources; on the other...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F5/14
CPCC02F5/14C02F2303/08C02F2303/22
Inventor 魏亮翁挺
Owner 内蒙古润嘉节能环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap