A treatment method and application of waste incineration fly ash

A treatment method, a technology for incinerating fly ash, applied in the application, household appliances, other household appliances, etc., can solve the problems of insufficient hardness, complicated construction, easy damage, etc., to prevent the seepage of heavy metals, avoid damage to dams, and good water permeability Effect

Active Publication Date: 2018-07-13
乐尔环境科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the complex construction existing in the reprocessing of garbage fly ash in the prior art, and the problems of insufficient hardness and easy damage of the building materials made of it due to the existence of pores, the present invention provides a treatment method of garbage incineration fly ash and Application, the incinerated garbage fly ash is used to build dams, pedestrian crossings, etc. after treatment. The dam is more stable, the invention is energy-saving and environment-friendly, makes the use of waste and garbage fly ash reasonably and efficiently, and effectively reduces the environmental pressure caused by garbage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A processing method for incineration fly ash, the steps of which are:

[0032] A Take calcium sulfate, sodium sulfate, calcium lignosulfonate and clay according to the mass ratio of 3:2.5:1:13, mix and stir them to obtain coagulant; the stirring time is 5-10 min;

[0033] B Select 40 parts by mass of water to be placed in the reaction vessel, then add 17 parts by mass of sodium silicate, 15 parts by mass of diatomaceous earth, 5 parts by mass of pyrrole and 5 parts by mass of ethylenediaminetetraacetic acid to the water Disodium is stirred while adding to obtain the first mixed solution; the stirring time in step B is 8-20min;

[0034] C Select 10 parts by mass of the coagulant obtained in step A and add it to the first mixed solution, and then add 5-15 parts by mass of activated carbon (activated carbon is the activated carbon described in Example 1 of the application text of Patent No. 201310221064X) , 18 parts of disodium methylene dinaphthalene sulfonate, 1 part of...

Embodiment 2

[0040] A processing method for incineration fly ash, the steps of which are:

[0041]A Take calcium sulfate, sodium sulfate, calcium lignosulfonate and clay according to the mass ratio of 2:3:1:10, mix and stir them to obtain coagulant; the stirring time is 5-10 min;

[0042] B Select 53 parts by mass of water to be placed in the reaction vessel, then add 10 parts by mass of sodium silicate, 20 parts by mass of diatomaceous earth, 2 parts by mass of pyrrole and 15 parts by mass of ethylenediaminetetraacetic acid to the water Disodium is stirred while adding to obtain the first mixed solution; the stirring time in step B is 8-20min;

[0043] C Select 8 parts by mass of the coagulant obtained in step A and add it to the first mixed solution, and then add 15 parts by mass of activated carbon ((activated carbon is the activated carbon described in Example 2 of the application text with patent number 201310221064X)) , 13 parts of disodium methylene dinaphthalene sulfonate, 4 parts...

Embodiment 3

[0050] A processing method for incineration fly ash, the steps of which are:

[0051] A Take calcium sulfate, sodium sulfate, calcium lignosulfonate and clay according to the mass ratio of 4:2:1:15, mix and stir them, and the stirring time is 5-10 min; obtain coagulant;

[0052] B Select 48 parts by mass of water to be placed in the reaction vessel, then add 15 parts by mass of sodium silicate, 18 parts by mass of diatomaceous earth, 3 parts by mass of pyrrole and 10 parts by mass of ethylenediaminetetraacetic acid to the water Disodium, stirring while adding, the stirring time is 8-20min; obtain the first mixed solution;

[0053] C Select 9 parts by mass of the coagulant obtained in step A and add it to the first mixed solution, then add 11 parts by mass of activated carbon, 15 parts of disodium methylene dinaphthalenesulfonate, 3 parts of borax and 2 parts of gelatin , stirring to obtain the second mixed solution, the stirring time is 10-25min;

[0054] D Stirring while he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a treatment method and an application of municipal solid waste incineration fly ash, and belongs to the field of municipal solid waste incineration fly ash. The treatment method comprises the following steps: A. calcium sulfate, sodium sulfate, calcium lignosulfonate and clay are mixed with stirring, and a coagulant is obtained; B. sodium silicate, diatomite, pyrrole and Ethylene diamine tetraacetic acid disodium salt are added into water with stirring, and a first mixed solution is obtained; C. the coagulant is added into the first mixed solution, active carbon, disodium methylene dinaphthalenesulfonate, borax and gelatin are added into the first mixed solution in order with stirring, and a second mixed solution is obtained; D. the second mixed solution is heated to 50-70 DEG C and cooled to normal temperature, and the curing agent is obtained. E. the municipal solid waste incineration fly ash, the portland cement, cobblestones, sand, a curing agent and water are mixed with stirring, and fly ash concrete is obtained; F. the fly ash concrete is laid in concrete pouring, wherein the concrete does not require hardness, but require good water permeability. The fly ash concrete has the advantages of good water permeability, energy saving and environmental protection, and low cost; the obtained fly ash concrete can be used for repairing dams and paving cross walk, and the like, so that utilization of waste materials is effectively realized, and the problem for treating the fly ash from municipal solid waste incineration is solved.

Description

technical field [0001] The invention belongs to the field of garbage fly ash treatment, and in particular relates to a treatment method and application of garbage incineration fly ash. Background technique [0002] At present, more and more methods of urban waste disposal are incineration. The advantage of incineration is that it greatly reduces the volume of waste and reduces the pollution of waste to the environment. However, the biggest problem is how to deal with the fly ash after incineration. The existing method of processing by cement curing often results in the need for a large amount of land occupied by the cured cement. In my country, incineration ash is divided into slag and fly ash. Slag refers to the product remaining on the hearth after combustion, while fly ash refers to the residue collected in the air pollution control system (APC). Internationally, ash is generally divided into three categories according to its collection source: bottom ash, flue gas puri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/20C04B28/04C04B38/00
CPCC04B28/04C04B40/0039C04B2111/00284C04B22/143C04B22/147C04B24/18C04B14/10C04B22/08C04B14/08C04B24/123C04B24/128C04B14/022C04B24/20C04B22/0013C04B24/14C04B18/105C04B14/02C04B38/00
Inventor 王明明其他发明人请求不公开姓名
Owner 乐尔环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap