Anti-ultraviolet coating
An anti-ultraviolet and coating technology, applied in the field of coatings, can solve the problems of high brittleness of epoxy resin coatings, affecting the development of epoxy resin coatings, and prone to chalking, etc., to improve toughness and impact resistance, good anti-ultraviolet performance, The effect of increasing compatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] An anti-ultraviolet paint, the raw materials of which by weight include: 80 parts of modified epoxy resin emulsion, 25 parts of water, 3 parts of propylene glycol methyl ether acetate, 12 parts of light calcium carbonate, 20 parts of kaolin, and ethyl lauryl 3 parts of oxysulfobetaine, 1 part of sodium lauryl sulfonate, 0.05 parts of simethicone, 0.05 parts of defoamer TegoFoamex843, wetting agent Wet2650.4 parts, wetting agent Wet5000.1 part, 0.5 part of leveling agent, 0.3 part of polyacrylamide, 0.2 part of methyl cellulose, 0.02 part of 1,2-benzisothiazolin-3-one, 0.3 part of ultraviolet absorber UV-P;
[0022] In the preparation process of the modified epoxy resin emulsion, mix butyl titanate and ethanol, adjust the temperature to 20°C, add dropwise a 9.2wt% hydrochloric acid solution, and complete the dropwise addition within 15 minutes, keep warm and stir for 0.6 hours, Add γ-glycidoxypropyltrimethoxysilane, continue to heat and stir for 24h, heat to 70°C, heat and ...
Embodiment 2
[0024] An anti-ultraviolet coating, the raw materials of which by weight include: 100 parts of modified epoxy resin emulsion, 15 parts of water, 5 parts of propylene glycol methyl ether acetate, 8 parts of 200 mesh light calcium carbonate, 25 parts of 300 mesh kaolin, 10 parts 2 parts of dialkylethoxy sulfobetaine, 2 parts of sodium lauryl sulfonate, 0.03 parts of simethicone, defoamer TegoFoamex8430.07 parts, wetting agent Wet2650.2 parts, wetting agent Wet5000 .2 parts, 0.4 part of leveling agent, 0.5 part of polyacrylamide, 0.1 part of methyl cellulose, 0.04 part of 1,2-benzisothiazolin-3-one, 0.1 part of ultraviolet absorber UV-P;
[0025] In the preparation process of modified epoxy resin emulsion, mix butyl titanate and ethanol, adjust the temperature to 30℃, add dropwise hydrochloric acid solution with a mass fraction of 8.8wt%, add dropwise within 15min, keep stirring for 1h, add γ-Glycidyloxypropyltrimethoxysilane, continue to heat and stir for 20h, heat to 80°C, heat an...
Embodiment 3
[0027] An anti-ultraviolet paint, the raw materials of which by weight include: 85 parts of modified epoxy resin emulsion, 22 parts of water, 3.5 parts of propylene glycol methyl ether acetate, 11 parts of 300 mesh light calcium carbonate, 21 parts of 200 mesh kaolin, 10 parts Dialkylethoxysulfobetaine 2.7 parts, sodium lauryl sulfonate 1.2 parts, simethicone 0.045 parts, defoamer TegoFoamex8430.055 parts, wetting agent Wet2650.35 parts, wetting agent Wet5000 .13 parts, 0.48 parts of leveling agent, 0.35 parts of polyacrylamide, 0.18 parts of methyl cellulose, 0.025 parts of 1,2-benzisothiazolin-3-one, 0.25 parts of ultraviolet absorber UV-P;
[0028] In the preparation process of the modified epoxy resin emulsion, mix butyl titanate and ethanol, adjust the temperature to 22°C, add dropwise a 9.1wt% hydrochloric acid solution, and complete the dropwise addition within 15 minutes, keep the temperature and stir for 0.7h, Add γ-glycidoxypropyltrimethoxysilane, continue to heat and s...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com