Anti-corrosion anti-rust wear-resistant paint

A wear-resistant coating, anti-corrosion and anti-rust technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve problems such as not being able to meet the needs

Inactive Publication Date: 2016-10-12
WUHU SHUANGBAO BUILDING MATERIAL
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Anti-corrosion and wear-resistant coatings are an indispensable coating in paints and coatings. The annual economic loss caused by corrosion in the world is about 1 trillion US dollars, which is the sum of the losses caused by earthquakes, fires, and wind disasters. Anti-corrosion and wear-resistant coatings are the most effective. , the most economical and most commonly used anti-corrosion method has received widespread attention at home and abroad. Under normal conditions, anti-corrosion and wear-resistant coatings can prevent corrosion of metals and prolong the service life of non-ferrous metals. The anti-corrosion function lies in the coating The shielding effect, resistance effect, wet adhesion, chemical passivation and cathodic protection. Although many kinds of anti-corrosion and wear-resistant coatings have been developed at home and abroad, they still cannot meet the needs. How to prepare a kind of anti-corrosion and anti-rust performance, Coatings with good wear resistance and long service life have become a technical problem to be solved at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of anticorrosion antirust wear-resisting paint that the present invention proposes, its raw material comprises by weight: 100 parts of modified fluorosilicone acrylic emulsion, 45 parts of polyvinyl acetal modified phenolic resin, 20 parts of methyltrimethoxysilane, 35 parts of calcium naphthenate, 10 parts of silica sol, 5 parts of crystalline silica, 6 parts of polyvinyl acrylate emulsion, 6 parts of lead chromate, 5 parts of methyl cellulose, 4 parts of cellulose hydroxypropyl methyl ether 3 parts, 3 parts of m-xylene, 6 parts of calcium carbonate, 4 parts of talcum powder, 3 parts of precipitated barium sulfate, 6 parts of nano-aluminum powder, 6 parts of aluminum hydroxide, 4 parts of nano-calcium oxide, 3 parts of zinc oxide, 4 parts of dispersant 6 parts, 6 parts of defoamer, 3 parts of film-forming aid.

[0016] The modified fluorosilicone acrylic emulsion is prepared according to the following process: mix 5 parts of tetraethyl orthosilicate and 10 parts...

Embodiment 2

[0018] A kind of anticorrosion antirust wear-resisting paint that the present invention proposes, its raw material comprises by weight: 80 parts of modified fluorosilicone acrylic emulsion, 60 parts of polyvinyl acetal modified phenolic resin, 10 parts of methyltrimethoxysilane, 50 parts of calcium naphthenate, 5 parts of silica sol, 8 parts of crystalline silica, 3 parts of polyvinyl acrylate emulsion, 8 parts of lead chromate, 1 part of methyl cellulose, 6 parts of cellulose hydroxypropyl methyl ether 1 part of m-xylene, 8 parts of calcium carbonate, 2 parts of talcum powder, 5 parts of precipitated barium sulfate, 3 parts of nano-aluminum powder, 8 parts of aluminum hydroxide, 2 parts of nano-calcium oxide, 5 parts of zinc oxide, 3 parts of dispersant 8 parts, 8 parts of defoamer, 1 part of film-forming aid.

[0019] The modified fluorosilicone acrylic emulsion is prepared according to the following process: mix 2 parts of tetraethyl orthosilicate and 15 parts of water unif...

Embodiment 3

[0021] A kind of anticorrosion antirust wear-resisting paint that the present invention proposes, its raw material comprises by weight: 120 parts of modified fluorosilicone acrylic emulsion, 30 parts of polyvinyl acetal modified phenolic resin, 30 parts of methyltrimethoxysilane, 20 parts of calcium naphthenate, 15 parts of silica sol, 2 parts of crystalline silica, 9 parts of polyvinyl acrylate emulsion, 4 parts of lead chromate, 9 parts of methyl cellulose, 2 parts of cellulose hydroxypropyl methyl ether 5 parts of m-xylene, 4 parts of calcium carbonate, 6 parts of talcum powder, 1 part of precipitated barium sulfate, 9 parts of nano-aluminum powder, 4 parts of aluminum hydroxide, 6 parts of nano-calcium oxide, 1 part of zinc oxide, 5 parts of dispersant 4 parts, 4 parts of defoamer, 5 parts of film-forming aid.

[0022] The modified fluorosilicone-acrylic emulsion is prepared according to the following process: mix 8 parts of tetraethyl orthosilicate and 5 parts of water un...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses anti-corrosion anti-rust wear-resistant paint. The paint is prepared from a modified fluorine silicone-acrylic emulsion, polyvinyl acetal modified phenolic resin, methyltrimethoxysilane, calcium naphthenate, silica sol, crystalline silicon oxide, a polyacrylic acid vinyl ester emulsion, lead chromate, methylcellulose, hydroxypropyl methyl cellulose, m-xylene, calcium carbonate, talcum powder, precipitated barium sulfate, nano aluminum powder, aluminum hydroxide, nano calcium oxide, zinc oxide, a dispersing agent, a defoaming agent and a coalescing agent. The anti-corrosion anti-rust wear-resistant paint has excellent anti-corrosion, anti-rust and wear-resistant properties.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an anti-corrosion, anti-rust and wear-resistant coating. Background technique [0002] Anti-corrosion and wear-resistant coatings are an indispensable coating in paints and coatings. The annual economic loss caused by corrosion in the world is about 1 trillion US dollars, which is the sum of the losses caused by earthquakes, fires, and wind disasters. Anti-corrosion and wear-resistant coatings are the most effective. , the most economical and most commonly used anti-corrosion method has received widespread attention at home and abroad. Under normal conditions, anti-corrosion and wear-resistant coatings can prevent corrosion of metals and prolong the service life of non-ferrous metals. The anti-corrosion function lies in the coating The shielding effect, resistance effect, wet adhesion, chemical passivation and cathodic protection. Although many kinds of anti-corrosion and wear-resistant c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D143/04C09D7/12C09D5/10C08F220/14C08F220/04C08F220/34C08F220/28C08F230/08
CPCC08F220/04C08F220/14C08F220/28C08F220/281C08K2201/011C08K2201/014C08L2205/035C09D5/103C09D7/61C09D7/63C09D7/65C09D143/04C08L61/14C08K13/02C08K2003/2296C08K2003/0812C08K3/36C08K3/34C08F220/34C08F230/08
Inventor 胡昌悌
Owner WUHU SHUANGBAO BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap