Preparation method of hydrotreating catalyst

Abstract

The invention discloses a preparation method of a hydroprocessing catalyst. The catalyst is a bulk phase catalyst and comprises hydrogenation active metal components W, Ni and Mo, and aluminum oxide. The preparation method comprises the following preparation processes of preparing pulp containing nickel and aluminum precipitates by an ammonia distilling method, preparing pulp containing tungsten and aluminum precipitates by a parallel-flow method, uniformly mixing the pulp containing the nickel and aluminum precipitates with the pulp containing the tungsten and aluminum precipitates, then performing ageing, performing hydrothermal treatment with steam, adding urea, performing mixing with MoO3, then performing pulping, performing shaping and the like, so as to obtain the hydroprocessing catalyst. The catalyst is particularly suitable for being used for ultra-deep hydrodesulfurization and denitrification reactions of diesel fraction.

Description

technical field [0001] The invention relates to a preparation method of a hydrogenation treatment catalyst, in particular to a preparation method of a high-activity bulk phase hydrogenation treatment catalyst. Background technique [0002] At present, in the world, crude oil is becoming increasingly heavy and inferior, coupled with the continuous development of the world economy and increasingly stringent environmental protection regulations, it is necessary to produce a large amount of light clean fuel. The development and use of ultra-low sulfur or even sulfur-free gasoline and diesel is the trend of clean fuel development in the world today. The use of traditional hydrodesulfurization catalysts can also achieve deep desulfurization or even ultra-deep desulfurization of diesel oil by increasing the severity of the reaction, such as increasing the reaction temperature, hydrogen partial pressure or reducing the reaction space velocity, but the increase in the reaction temper...

AI Technical Summary

Problems solved by technology

[0010] The bulk phase hydrogenation catalyst disclosed by CN102049265A adds ammonium bicarbonate during the coprecipitation process, and the bulk phase hydrogenation catalyst disclosed by CN102451703A adds carbon dioxide during the coprecipitation process to generate carbonate or bicarbonate. It releases a certain amount of gas during the roasting process. Under the impact of the gas, the pore volume and specific surface area of ​​the catalyst are increased, so that more metal active sites are exposed on the surface of the catalyst, but this method will cause some pores to collapse. , the pore distribution is dispersed, the mechanical strength is reduced, and the active metal is locally aggregated, and the exposed metal active sites are limited

The co-precipitation method adopted above will make the distribution of different hydrogenation active metals difficult to control, thereby affecting the distribution of different hydrogenation active metals and reducing the interaction between active metals. At the same time, the content of surface active metals in the catalyst is relatively low. Small and low active center density, which ultimately affects the ultra-deep hydrodesulfurization performance of the catalyst