Long-acting broad-spectrum bacterium resisting and corrosion preventing nano spraying foam agent as well as preparation method and application thereof

An antibacterial and anti-corrosion, broad-spectrum technology, applied in anti-corrosion coatings, fire-proof coatings, anti-fouling/underwater coatings, etc., can solve the problem of nano-long-acting broad-spectrum anti-bacterial and anti-corrosion spray foaming agent, no similar products have been found, and achieve light transmittance strong effect

Inactive Publication Date: 2017-01-04
江苏微特克纳米科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] At present, no similar products have been found at home and abroad for nano long-acting broad-spectrum antibacterial and anti-corrosion spray foam agents. After 2 years of research, we have achieved satisfactory results.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long-acting broad-spectrum bacterium resisting and corrosion preventing nano spraying foam agent as well as preparation method and application thereof
  • Long-acting broad-spectrum bacterium resisting and corrosion preventing nano spraying foam agent as well as preparation method and application thereof
  • Long-acting broad-spectrum bacterium resisting and corrosion preventing nano spraying foam agent as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1 Preparation of long-acting broad-spectrum antibacterial and antiseptic nano-spray foaming agent

[0025] The preparation method of long-acting broad-spectrum antibacterial and antiseptic nano-spray foam agent comprises the steps of: antibacterial drug aminoglycoside 0.2%, organic silane ethyl triethyl silane resin 2%, dispersant methyl amyl alcohol 1%, preservative Propyl hydroxybenzoate 1%, stabilizer magnesium stearate 0.1%, solvent ethanol 93.2%, disinfectant chlorhexidine 2.5%, solid and liquid mixed, stirred at 50 degrees for 2 hours.

Embodiment 2

[0026] Embodiment 2 Preparation of long-acting broad-spectrum antibacterial and antiseptic nano-spray foaming agent

[0027] The preparation method of long-acting broad-spectrum antibacterial and antiseptic nano-spray foam agent comprises the following steps: antibacterial drug aminoglycoside 0.2%, organosilylmethyltriethylsilane resin 2%, dispersant methyl amyl alcohol 1%, preservative sodium lactate 1%, stabilizer magnesium stearate 0.1%, solvent chloroform 93.2%, disinfectant chloramine T 2.5%, solid and liquid mixed, stirred at 50 degrees for 2 hours.

Embodiment 3

[0028] Embodiment 3 Preparation of long-acting broad-spectrum antibacterial and antiseptic nano-spray foaming agent

[0029] The preparation method of the long-acting broad-spectrum antibacterial and antiseptic nano-spray foam agent comprises the following steps: antibacterial drug Taineng 0.2%, organosilane ethyl triethyl silane resin 2%, dispersant methyl amyl alcohol 1%, preservative lactic acid chain ball Mectin 1%, stabilizer magnesium stearate 0.1%, solvent dichloroethane 93.2%, disinfectant chlorhexidine 2.5%, solid and liquid mixed, stirred at 50 degrees for 2 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a long-acting broad-spectrum bacterium resisting and corrosion preventing nano spraying foam agent. The nano spraying foam agent contains the following components by weight percent: 0.1-5% of bacterium resisting drugs, 2-25% of organosilane resin, 1-5% of dispersing agent, 1-8% of preservatives, 0.1-4% of stabilizing agents, 10-95% of solvents and 0.5-5% of disinfectants. The nano spraying foam agent has the characteristics and advantages that the use thickness of the long-acting broad-spectrum bacterium resisting and corrosion preventing nano spraying foam agent product is 10-50mu m; the product has the advantages of friction resistance, heat resistance, aging resistance, radiation resistance, no embrittlement at low temperature, hydrophobicity, moisture resistance, no toxicity, strong light transmittance, capability of resisting bacteria and preventing corrosion for 0.5-6 years, and the like and is widely applied to bacterium resistance, corrosion prevention and disinfection in the fields of medical equipment, household appliances, hospitals, schools, automobiles, families, etc.

Description

technical field [0001] The invention relates to an antibacterial and antiseptic nano-spray coating soaked product, in particular to a long-acting broad-spectrum anti-bacterial and anti-corrosion nano-spray foam agent and a preparation method and application thereof. Background technique [0002] Nanoscience is the study of the movement and changes of atoms and molecules in the range of one millionth of a meter to one billionth of a meter. The technology of manipulating and processing atoms and molecules within this scale is called nanotechnology. The purpose of developing nanotechnology is to produce computers smaller than human cells and ultra-efficient micro-machines, which can prevent and treat diseases at the molecular level. disease etc. [0003] Nanomaterials have very important application prospects in the field of environmental protection because of their unique particle size and surface properties, antibacterial, deodorizing, and disinfection properties. With the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/14C09D5/08C09D7/12
CPCC08K5/00C08K5/05C08K5/098C08K5/1345C09D4/00C09D5/08C09D5/14C09D5/18C09D183/04
Inventor 王天桃刘成龙王平斯航
Owner 江苏微特克纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap